Effect of TCP phase formation on the electrochemical corrosion behavior of the nickel-based superalloy UNS N26455
Source abstract
Abstract
Abstract The effect of topologically close-packed (TCP) phase formation on the electrochemical corrosion behavior of the UNS N26455 (Ni–16Cr–16Mo) superalloy was evaluated using different electrochemical techniques. We verified that this superalloy is resistant to highly corrosive environments but its corrosion potential decreases and the anodic current density increases as the TCP phase concentration increases in the microstructure. Its anodic behavior indicates that there is a selective dissolution process associated with this secondary phase, which is completely dissolved before repassivation occurs. Although the repassivation potential remains nearly unchanged, the degraded points configure defects that may negatively affect the material’s performance during service.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (48)
Show source-provided references
1. On the performance of commercially available corrosion-resistant nickel alloys: a review10.1515/corrrev-2016-0014 ↗
2. A Review on Superalloys and IN718 Nickel-Based INCONEL Superalloy10.21533/pen.v3i1.43 ↗
3. Ni based superalloy: casting technology, metallurgy, development, properties and applications
4. Corrosion-resistant nickel alloys: part 2
5. Role of alloyed molybdenum on corrosion resistance of austenitic Ni-Cr–Mo–Fe alloys in H2S–Cl− environments10.1016/j.corsci.2015.05.053 ↗
6. Crevice corrosion of nickel-based alloys considered as engineering barriers of geological repositories10.1038/s41529-017-0010-5 ↗
7. Effect of alloy composition on the crevice corrosion resistance of nickel alloys
8. Effect of alloying elements on crevice corrosion inhibition of nickel–chromium–molybdenum–tungsten alloys under aggressive conditions: an electrochemical study10.5006/1170 ↗
9. What does the pitting resistance equivalent really tell us?10.1016/1350-6307(95)00026-7 ↗
10. Modeling of Ni–Cr–Mo based alloys: part I – phase stability
11. Modeling of Ni–Cr–Mo based alloys: part II – kinetics, calphad comput10.1016/j.calphad.2006.12.006 ↗
12. GCP and TCP phases presented in nickel-base superalloys10.1016/j.matpr.2016.03.024 ↗
13. Formation and effect of topologically close-packed phases in nickel-base superalloys10.1080/02670836.2016.1187335 ↗
14. Corrosion resistance of the UNS N26455 superalloy in simulated environment containing chloride and CO210.20964/2020.10.56 ↗
15. The crystal structure of the P phase, Mo–Ni–Cr. II. Refinement of parameters and discussion of atomic coordination10.1107/S0365110X57000018 ↗
16. ASTM A494 A494M-18a: standard specification for castings, nickel and nickel alloy
17. ASTM E3-11: standard guide for preparation of metallographic specimens
18. ASTM G192-08: standard test method for determining the crevice repassivation potential of corrosion-resistant alloys using a potentiodynamic-galvanostatic-potentiostatic technique
19. ASTM G5-14e1: standard reference test method for making potentiodynamic anodic polarization measurements
20. ASTM G61-86: standard test method for conducting cyclic potentiodynamic polarization measurements for localized corrosion susceptibility of iron-, nickel-, or cobalt-based alloys
21. Influence of micro-structure on corrosion behavior of a Ni-based superalloy in 3.5% NaCl10.1016/j.electacta.2007.05.043 ↗
22. Influence of nanocrystallization on passive behavior of Ni-based superalloy in acidic solutions10.1016/j.electacta.2006.08.070 ↗
23. The impedance properties of the oxide film on the Ni–Cr–Mo Alloy-22 in neutral concentrated sodium chloride solution10.1016/j.electacta.2010.07.064 ↗
24. ASTM G48-11: standard test methods for pitting and crevice corrosion resistance of stainless steels and related alloys by use of ferric chloride solution
25. Passivation and depassivation of alloy 22 in acidic chloride solutions10.1149/1.3246790 ↗
26. An electrochemical impedance study of alloy 22 in NaCl brine at elevated temperature. I. Corrosion behavior10.1016/j.jelechem.2004.06.031 ↗
27. Using pit solution chemistry for evaluation of metastable pitting stability of austenitic stainless steel10.1002/maco.200403827 ↗
28. CPE analysis by local electrochemical impedance spectroscopy10.1016/j.electacta.2005.02.128 ↗
29. Determination of effective capacitance and film thickness from constant-phase-element parameters10.1016/j.electacta.2009.10.065 ↗
30. Analyzing simulated electrochemical impedance spectroscopy results by the systematic permutation of data points
31. Characterization of passive films on shape memory stainless steels10.1016/j.corsci.2011.12.022 ↗
32. Effect of surface treatment on electrochemical behavior of CP Ti, Ti–6Al–4V and Ti–13Nb–13Zr alloys in simulated human body fluid10.1016/j.corsci.2005.06.003 ↗
33. The analysis of electrode impedances complicated by the presence of a constant phase element10.1016/S0022-0728(84)80324-1 ↗
34. ASTM G102-189e1: standard practice for calculation of corrosion rates and related information from electrochemical measurements
35. Microstructure stability and mechanical properties of an age-hardenable Ni–Mo–Cr alloy subjected to long-term exposure to elevated temperature10.1016/j.matchar.2010.04.008 ↗
36. Crevice corrosion repassivation of Alloy 22 in aggressive environments10.5006/1.3279917 ↗
37. The effect of H2S concentration on the corrosion behavior of carbon steel at 90 °C10.1016/j.corsci.2010.02.004 ↗
38. The history of the point defect model for the passive state: a brief review of film growth aspects10.1016/j.electacta.2010.11.005 ↗
39. Pitting corrosion of metals: a review of the critical factors10.1149/1.1838615 ↗
40. Current transients caused by potential jumps applied to passivating films on nickel10.1016/0013-4686(90)87071-9 ↗
41. Effect of chloride ions on the corrosion behaviour of steel in 0.1 M citrate10.1016/j.electacta.2005.05.011 ↗
42. Repassivation kinetics in stress corrosion cracking-I. Type AISI 304 stainless steel in chloride solutions10.1016/0010-938X(88)90107-2 ↗
43. Localized corrosion (pitting): a model of passivity breakdown including the role of the oxide layer nanostructure10.1016/j.corsci.2008.06.047 ↗
44. Cr, Mo and W alloying additions in Ni and their effect on passivity10.1016/j.electacta.2004.01.061 ↗
45. Influence of chromium and molybdenum on the corrosion of nickel-based alloys10.5006/1.3279907 ↗
46. Using electrochemical methods to determine alloy 22’s crevice corrosion repassivation potential10.1007/s11837-005-0065-6 ↗
47. An electrochemical impedance study of Alloy-22 in NaCl brine at elevated temperature: II. Reaction mechanism analysis10.1016/j.jelechem.2004.05.032 ↗
48. Impedance studies of the passive film on aluminium10.1016/j.corsci.2005.05.058 ↗