The effect of phosphates on the susceptibility of α-brass to stress corrosion cracking in sodium nitrite
Source abstract
Abstract
Di-sodiumhydrogenphosphate (DSHP) inhibits the stress corrosion cracking (SCC) of α-brass in 0.1 M NaNO 2 . It increases the maximum stress and the time to failure at failure in slow strain-rate tests. It also changes the mode of failure to ductile failure in the presence of moderate concentrations. The results are complemented by some electrochemical measurements. The inhibiting effect of DSHP is attributed to the formation of zinc phosphate on the surface of the alloy which inhibits dezincification and subsequently the SCC of the brass.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Metallurgy and Material Science · Nanoporous metals and alloys · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Effect of oxyanions and chloride ions on the stress corrosion cracking susceptibility of admiralty brass in nonammoniacal aqueous solutions
2. Cole · Corros. Sci. · 1988 · 28 · 10910.1016/0010-938X(88)90012-1 ↗
3. Yu · Fatigue Fract. Engng Mater. Struct. · 1989 · 12 · 48110.1111/j.1460-2695.1989.tb00558.x ↗
4. Alvarez · Corros. Sci. · 1984 · 24 · 76910.1016/0010-938X(84)90026-X ↗
5. Rebak · Corros. Sci. · 1988 · 28 · 108910.1016/0010-938X(88)90103-5 ↗
6. Yu · Corros. Sci. · 1987 · 27 · 14110.1016/0010-938X(87)90069-2 ↗
7. Yu · Corros. Sci. · 1987 · 27 · 15910.1016/0010-938X(87)90070-9 ↗
8. Gouda · 1984 · 1 · 153
9. Ashworth · Corrosion · 1979 · 35 · 1910.5006/0010-9312-35.4.190 ↗
10. Sircar · Corros. Sci. · 1983 · 23 · 77710.1016/0010-938X(83)90040-9 ↗
11. Sayed · Corros. Sci. · 1994 · 36 · 22110.1016/0010-938X(94)90154-6 ↗
12. Hancock · J. appl. Chem. · 1959 · 9 · 34510.1002/jctb.5010090701 ↗
13. El-Tantawy · J. electroanal. Chem. · 1981 · 125 · 32110.1016/S0022-0728(81)80351-8 ↗
14. Cohen · Corrosion · 1976 · 32 · 46110.5006/0010-9312-32.12.461 ↗
15. Laz · Electrochim. Acta · 1992 · 37 · 65510.1016/0013-4686(92)80068-W ↗
16. Drogowska · J. electrochem. Soc. · 1992 · 139 · 278710.1149/1.2068980 ↗
17. Rozenfeld · 1981 · 176
18. Rebak · Corros. Sci. · 1989 · 29 · 100310.1016/0010-938X(89)90090-5 ↗
19. Duffo · Corros. Sci. · 1993 · 34 · 7910.1016/0010-938X(93)90260-N ↗
20. Ateya · Corrosion · 1994 · 50 · 2010.5006/1.3293490 ↗
21. Kojima · J. electrochem. Soc. · 1973 · 120 · 102610.1149/1.2403621 ↗
22. Kojima · J. electrochem. Soc. · 1973 · 120 · 120210.1149/1.2403661 ↗
23. Pickering · Corros. Sci. · 1983 · 23 · 110710.1016/0010-938X(83)90092-6 ↗
24. Alloy Dissolution
25. Burstein · J. electrochem. Soc. · 1994 · 141 · 91210.1149/1.2054857 ↗
26. Stability Constants of Metal-Ion Complexes
27. Bertocci · Corrosion · 1984 · 40 · 43910.5006/1.3593952 ↗
28. Sieradzki · J. electrochem. Soc. · 1987 · 134 · 163510.1149/1.2100726 ↗
29. Pickering · Corrosion · 1973 · 29 · 32510.5006/0010-9312-29.8.325 ↗
30. Vetter · 1967 · 162
31. St-Pierre · J. electrochem. Soc. · 1990 · 137 · 249110.1149/1.2086974 ↗