Critique of the Ford–Andresen film rupture model for aqueous stress corrosion cracking

M.M. Hall

Corrosion Science· Volume 51· Issue 5
Publisher page

Abstract

Abstract The Ford–Andresen film rupture model for aqueous stress corrosion cracking has obtained a prominent position in the nuclear reactor industry. The model is said to have superior predictive capabilities because it is derived from a fundamental understanding of the film rupture-repassivation mechanism of crack advance. However, a critical review shows that there are conceptual and mathematical problems with the Ford–Andresen model development; there are inconsistencies among the stated and implied assumptions, the crack tip current density expression lacks the necessary dependence on crack tip strain rate and the fundamental proportionality that exists between crack tip strain rate and crack growth rate is overlooked and omitted from the model development. Consequently, the Ford–Andresen model must be considered neither phenomenologically nor fundamentally supported.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Fatigue and fracture mechanics · Hydrogen embrittlement and corrosion behaviors in metals · High Temperature Alloys and Creep

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (41)

Show source-provided references
1. R.B. Mears, R.H. Brown, E.H. Dix Jr., A generalized theory of stress corrosion cracking, in: Symposium on Stress-Corrosion Cracking of Metals, Am. Soc. Testing and Materials, Inst. Mining Engineers, 1944, pp. 329–323.10.1520/STP42581S ↗
2. Film-rupture mechanism of stress corrosion10.6028/jres.048.013 ↗
3. A theory for the propagation of stress corrosion cracks in metals10.1149/1.2404217 ↗
4. D.A. Vermilyea, A film rupture model for stress corrosion cracking, in: Proceedings of Conference on Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, Unieux-Firminy; France, 12–16 June 1973, 1977, pp. 208–217.
5. Predictive approaches to stress corrosion cracking failure10.1016/0010-938X(80)90128-6 ↗
6. Factors influencing stress corrosion kinetics10.5006/1.3583125 ↗
7. F.P. Ford, Mechanisms of environmental cracking peculiar to the power generation industry, Report NP2589, EPRI, Palo Alto, September, 1982.
8. Corrosion in nuclear systems: environmentally assisted cracking in light water reactors
9. Development and use of a predictive model of crack propagation in 304/316L, A533B/A508 and Inconel 600/182 alloys in 288°C water
10. The estimation of crack tip strain rate parameters characterizing environment assisted crack growth data
11. L.M. Young, P.L. Andresen, T.M. Angeliu, Crack tip strain rate: estimates based on continuum theory and experimental measurement, Corrosion 2001, NACE, 2001, paper #01131.
12. Crack tip strain rate equation with applications to hydrogen embrittlement and active path dissolution models of stress corrosion cracking
13. T. Shoji, Quantitative prediction of environmentally-assisted cracking based on crack tip strain rate, in: Proceedings of ASME-PVP Symposium, Predictive Capabilities in Environmentally-Assisted Cracking, Miami, 1985, pp.127–142.
14. T. Shoji, S. Suzuki, R.G. Ballinger, Theoretical prediction of SCC growth behavior – threshold and plateau growth rate, in: Proceedings of the Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Breckinridge, 1995, pp. 881–889.
15. Overview of current progress in application of advanced technology to EAC
16. Development of a fundamental crack tip strain rate equation and its application to quantitative prediction of stress corrosion cracking of stainless steel in high temperature oxygenated water10.1016/j.jnucmat.2003.09.008 ↗
17. An alternative to the Shoji crack tip strain rate equation10.1016/j.corsci.2008.07.011 ↗
18. P.L. Andresen and F.P. Ford, Fundamental quantification of crack advance for life prediction in energy systems, in: Proceedings of the CORROSION 96 Research Topical Symposia , Part I – Life Prediction of Structures Subject to Environmental Degradation: The Science and Its Control in Engineering Practice, NACE, 1996, pp. 51–99.
19. Electrochemical effects on environmentally-assisted cracking
20. On the modeling of stress corrosion cracking of iron and nickel base alloys in high temperature aqueous environments10.1016/0010-938X(96)00048-0 ↗
21. Response to “On the modeling of stress corrosion cracking of iron and nickel base alloys in high temperature aqueous environments”10.1016/0010-938X(96)00055-8 ↗
22. Clarification of issues raised by P.L. Andresen, F.P. Ford in their response to “On the modeling of stress corrosion cracking of iron and nickel base alloys in high temperature aqueous environments”10.1016/S0010-938X(97)00042-5 ↗
23. An inconsistency in “Film Rupture Model” of stress corrosion cracking10.1016/j.corsci.2006.10.023 ↗
24. Role of slip emergence in the early stages of stress corrosion cracking in face centered iron–nickel–chromium alloys10.5006/0010-9312-23.5.117 ↗
25. Stability, validity and sensitivity to input parameters of the slip-dissolution model for stress-corrosion cracking10.1016/j.corsci.2007.05.001 ↗
26. Film rupture model for aqueous stress corrosion cracking under constant and variable stress intensity factor10.1016/j.corsci.2008.08.052 ↗
27. Was · 2007
28. Fundamental modeling of environmental cracking for improved design and lifetime evaluation in BWRs10.1016/0308-0161(94)90142-2 ↗
29. P.L. Andresen, Conceptual similarities and common predictive approaches for SCC in high temperature water systems, Corrosion 96, NACE, 1996, paper #96258.
30. T.M. Angeliu, P.L. Andresen, F.P. Ford, Applying slip-oxidation to the SCC of austenitic materials in BWR/PWR environments, Corrosion 98, NACE, 1998, 262/1–262/24.
31. The crack-tip system and its relevance to the prediction of cracking in aqueous environments
32. Mechano-chemical anodic dissolution of austenitic stainless steel in hot chloride solution10.1098/rspa.1962.0142 ↗
33. Dependence of the velocity of the anodic dissolution of iron on its yield rate under tension10.1063/1.1712258 ↗
34. Mechanism of acceleration of the electrode dissolution of metals during yielding under stress10.1063/1.1670162 ↗
35. Mechano-electrochemical dissolution of copper at reversible electrode potential10.1016/0010-938X(73)90042-5 ↗
36. Stress corrosion crack propagation; a constant charge criterion10.1016/S0010-938X(75)80017-5 ↗
37. The mechanical and electrochemical behaviour of passive film and the film rupture – dissolution model
38. Modeling of anodic current transients resulting from oxide rupture of plastically strained beta plus alpha titanium10.1149/1.1838564 ↗
39. Continuum mechanics characterization of plastic deformation-induced oxide film rupture10.1080/01418619908214287 ↗
40. Landau · 1987
41. The asymptotic stress and strain field near the tip of a growing crack under creep conditions10.1007/BF00036192 ↗