Fireside corrosion degradation of ferritic alloys at 600°C in oxy-fired conditions
Source abstract
Abstract
Abstract This paper reports the results of a study carried out to investigate the effects of simulated coal/biomass combustion conditions on the fireside corrosion. The 1000 h deposit recoat exposure (5 × 200 h cycles) was carried out at 600 °C. In these tests ferritic alloys were used 15Mo3, T22, T23 and T91. Kinetics data were generated for the alloys exposed using both traditional weight change methods and metal loss measurements. The highest rate of corrosion based on EDX results occurred under D1 deposit where provoke mainly by the formation of alkali iron tri-sulphate phase.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Combustion and Detonation Processes · Fire dynamics and safety research · Thermochemical Biomass Conversion Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (26)
Show source-provided references
1. Advanced Power Plant Using High Efficiency Boiler/Turbine, Best Practice Brochure, Carbon Abatement Technologies Programme, 2006.
2. Corrosion of superheater steel materials under alkali salt deposits Part 1: The effect of salt deposit composition and temperature10.1016/j.corsci.2008.01.010 ↗
3. P. Dechamps, The EU Research Strategy Towards Zero Emission Fossil Fuel Power Plants, in: J. Lecomte-Beckers, M. Carton, F. Schubert, P.J. Ennis, Materials for Advanced Power Engineering (2006) 25–40.
4. M. Farley, Clean Coal Technologies for power generation, in: A. Strang, W.M. Banks, G.M. McColvin, J.E. Oakey, R.W. Vanstone, Parsons 2007: Power Generation in an Era of Climate Change, IOM, 2007, pp. 335–342.
5. Fireside issues in advanced power generation systems10.1179/174892408X373509 ↗
6. Thermodynamic modelling of the corrosive deposits in oxy-fuel fired boiler
7. Review of status of advanced materials for power generation
8. Degradation of heat exchanger materials under biomass co-firing conditions10.3184/096034007X281640 ↗
9. Current limitations of high-temperature alloys in practical applications10.1007/BF01046730 ↗
10. Laboratory studies of the effects of sulfates and chlorides on the oxidation of superheater alloys
11. Fundamental mechanisms of the attack of chlorine, HCl and chlorides on steel and high temperature alloys in the temperature range 400–900 °C
12. A pilot-plant study of the effect of alkali salts on the initial stages of the high temperature corrosion of alloy 304L10.4028/www.scientific.net/MSF.461-464.965 ↗
13. The implications of chlorine-associated corrosion on the operation of biomass-fired boilers10.1016/S0360-1285(00)00003-4 ↗
14. D.A. Vaughan, H.H. Krause, W.D. Boyd, Chloride corrosion and its inhibition in refuse firing, in: Proceedings of The International Conference on Ash Deposits and Corrosion from Impurities in Combustion Gases, Henniker, New Hampshire, USA, 1977.
15. The effects of chlorides, hydrogen chloride and sulphur dioxide in the oxidation of steels below deposits10.1016/0010-938X(95)00011-8 ↗
16. Iron steel corrosion in a system of O2, SO2 and alkali chloride. The formation of low melting point salt mixtures10.1016/0010-938X(90)90069-H ↗
17. Saunders · 1995
18. Fireside corrosion behaviour of HVOF & plasma sprayed coatings in advanced coal/biomass co-fired power plants10.1007/s11666-013-9887-x ↗
19. Fireside corrosion of super-heaters: effects of air and oxy-firing of coal and biomass10.1016/j.fuel.2011.03.010 ↗
20. Fireside issues in advanced power generation systems10.1179/174892408X373509 ↗
21. K. Natesan, A. Purohit, D.L. Rink, Coal-ash corrosion of alloys for combustion 628 power plants, in: Presented at Fossil Energy Conference, 2003.
22. L. Paul, G. Clark, Coal ash corrosion resistance of new chromium and chromium silicon alloys, in: Presented at NACE Presented at Corrosion 2005 Conference (Paper no. 05453).10.5006/C2005-05453 ↗
23. Corey · Trans. ASME · 1945 · 67 · 289
24. Rahmel · 1963
25. Cutler · 1981 · vol. 41
26. The effects of chloride, and sulphur dioxide in the oxidation of steels below deposits10.1016/0010-938X(95)00011-8 ↗