A method for investigation of hot corrosion by gaseous Na2SO4
Source abstract
Abstract
A novel in situ exposure method for investigating hot corrosion of aluminde coatings in the absence of an alkali sulphate melt is presented. The samples are exposed to Na2SO4(g) at a temperature above the dew point of the gas. Results from 100 and 500 h exposures at 900 degrees C of Ni-based In792 covered with SIF232 aluminide coating are presented. Already after 100 h of testing, attack characteristic for Type I hot corrosion is observed. The reactions taking place during the testing are discussed and the results are compared with those from the well-known ex situ salt hot corrosion test.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Advanced ceramic materials synthesis · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Passage of trace metal contaminants through gas paths of gas turbines burning biomass and waste-fuels10.1016/j.fuel.2008.06.012 ↗
2. Chemistry and electrochemistry of the hot corrosion of metals10.5006/1.3583026 ↗
3. High-temperature corrosion of superalloys10.1080/02670836.1987.11782259 ↗
4. Vanadic and chloride attack of superalloys10.1080/02670836.1987.11782265 ↗
5. Kofstad · 1988
6. Current limitations of high-temperature alloys in practical applications10.1007/BF01046730 ↗
7. Hot corrosion in gas turbine components10.1016/S1350-6307(00)00035-2 ↗
8. Structure and 900°C hot corrosion behavior of chromium-modified platinum aluminide coatings10.1016/0257-8972(88)90132-6 ↗
9. A life prediction model for coatings based on the statistical analysis of hot salt corrosion performance10.1016/0010-938X(92)90138-S ↗
10. The hot corrosion of directionally solidified Ni–Cr–Nb–Al (γγ′−δ) eutectic alloys10.1007/BF00616101 ↗
11. Comparison of hot corrosion protection of coatings on IN-738LC10.1179/174329404X7144 ↗
12. Hot corrosion behaviour of CM 247 LC alloy in Na2SO4 and NaCl environments10.1023/A:1018831025272 ↗
13. Development of burner rig corrosion tests for gas turbine alloys: study of protective metallic coatings and inhibitors for hot salt corrosion10.4028/www.scientific.net/MSF.461-464.917 ↗
14. Comparison of hot-salt corrosion behavior of superalloys in high- and low-velocity burner rigs10.1080/02619180.1989.11753437 ↗
15. Advaced burner-rig test for oxidation-corrosion resitance evaluation of MCRALY/superalloys systems10.1016/j.surfcoat.2006.07.256 ↗
16. Development of a new test method of high temperature corrosion in gas turbines based on thermodynamic modeling10.4028/www.scientific.net/MSF.461-464.907 ↗
17. Hot corrosion of coated and uncoated single crystal gas turbine materials10.1002/maco.200804130 ↗
18. Draft code of practice for discontinuous corrosion testing in high temperature gaseous atmospheres, European Commission Project SMT4-CT95-2001,*TESTCORR’, ERA Technology, UK, 2000.
19. Laboratory and field corrosion behaviour of coatings for turbine blades10.1016/S0257-8972(97)00481-7 ↗
20. The influence of Pt on oxidation and sodium sulfate induced corrosion of NiAl diffusion coatings10.3184/096034011X13188762374132 ↗
21. Birks · 2006
22. Khanna · 2002
23. Hot corrosion of materials: a fluxing mechanism?10.1016/S0010-938X(01)00057-9 ↗
24. Rapp · 2001 · 3790
25. R.A. Rapp, Hot corrosion by fused salts, Ditto 3834–3835.10.1016/B0-08-043152-6/00682-3 ↗
26. FactSage 6.2, C.f.R.i.C. Thermochemistry, Editor. 2009, CRCT.
27. The system Na2SO4–Na2CrO4 and the structure of Na2SO4 (III)10.1107/S0365110X5400237X ↗