Cathodic reduction of the duplex oxide films formed on copper in air with high relative humidity at 60°C

Abstract The cathodic reduction of duplex air-formed oxide film on copper was performed at a constant current density of i c = −50 μA cm −2 in deaerated 0.1 M KCl solution to investigate the sequence of cathodic reduction of each oxide layer and its mechanism. The single-phase thick CuO film on copper was also cathodically reduced at i c = −50 μA cm −2 or −2.5 mA cm −2 . The surface characterizations of the air-formed oxide film and single-phase CuO film before cathodic reduction and after partial or complete cathodic reduction were performed by XPS and X-ray diffraction, respectively. The two plateau regions appeared in the potential vs. time curve during cathodic reduction of the duplex air-formed oxide film on copper, while one plateau region was observed in the potential–time curve during cathodic reduction of the single-phase CuO film on copper. The potential in the first plateau region for the air-formed film coincided with that in the plateau region for the CuO film. The results of XPS and X-ray diffraction suggested that in the first plateau region, the outer CuO layer is directly reduced to metallic Cu, while in the second plateau region, the inner Cu 2 O layer is reduced to metallic Cu.