Systematic study of the corrosion properties of selected high-resistance alloys in natural seawater
Source abstract
Abstract
Electrochemical measurements were conducted to evaluate localized corrosion on UNS S31603, UNS S31803, UNS S32750, UNS S31254 and UNS N08825 in natural seawater. Critical pitting and crevice temperatures were assessed using a potentiostatic technique and critical potentials for pitting and crevice corrosion initiation and repassivation were identified using potentiodynamic polarization at temperatures from 5 to 40 °C. Passivity breakdown always occurred through pitting and crevice growth above a transition temperature. Below this temperature, pitting corrosion was not observed on any of the alloys regardless of the applied potential, but initiation of crevice corrosion occurred after the alloys reached a transpassive potential.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. Aqueous corrosion of stainless steels
2. Pitting corrosion of sheets of a nickel-base superalloy10.1002/maco.200805009 ↗
3. Influence of microstructure and alloying element on the polarization behaviour within the crevice of UNS S32304 duplex stainless steel10.1016/j.corsci.2011.07.030 ↗
4. Dependence on the critical pitting temperature on surface roughness10.1016/S0010-938X(02)00215-9 ↗
5. Szklarska-Smialowska · 2005
6. A critical crevice solution and IR drop crevice corrosion model10.1016/j.corsci.2008.02.020 ↗
7. Pitting and crevice corrosion of superaustenitic stainless steels10.1002/maco.200303746 ↗
8. Determining the potential independent critical pitting temperature (CPT) by a potentiostatic method using the Avesta cell
9. 2003
10. Critical pitting and repassivation temperatures for duplex stainless steel in chloride solutions10.1016/j.electacta.2008.02.047 ↗
11. Stainless steel crevice corrosion testing in natural and synthetic seawater
12. The metal–solution interface10.1016/S0001-8686(98)00082-7 ↗
13. Critical pitting temperature measurements of stainless steels with an improved electrochemical method10.1016/0010-938X(89)90088-7 ↗
14. Metastable pitting and the critical pitting temperature10.1149/1.1838691 ↗
15. 2004
16. 2003
17. Transpassivation of Fe–Cr–Ni stainless steels10.1016/j.corsci.2004.09.007 ↗
18. Temperature dependence of pitting potentials for austenitic stainless steels above their critical pitting temperature10.1016/S0010-938X(98)00020-1 ↗
19. Temperature and potential dependence of crevice corrosion of AISI 316 stainless steel10.1016/S0010-938X(00)00167-0 ↗
20. Tutorial on cyclic potentiodynamic polarization technique
21. Chemical composition and electronic structure of the oxide films formed on 316L stainless steel and nickel based alloys in high temperature aqueous environment10.1016/S0010-938X(00)00012-3 ↗
22. Repassivation of high alloy stainless steel in chlorinated seawater10.1179/bcj.1995.30.3.237 ↗
23. Friend · 1980
24. A general model for the repassivation potential as a function of multiple aqueous solution species10.1016/j.corsci.2003.10.002 ↗
25. Cyclic thermammetry10.1016/j.elecom.2004.08.006 ↗
26. The effect of dominant alloy additions on the corrosion behavior of some conventional and high alloy stainless steels in seawater10.1016/0010-938X(95)00043-J ↗
27. Alvarez-Armas · 2009
28. Influence of chemical composition on the pitting corrosion resistance of non-standard low-Ni high-Mn–N duplex stainless steels10.1016/S0010-938X(02)00154-3 ↗
29. Effect of nitrogen on corrosion behavior of 28Cr–7Ni duplex and microduplex stainless steels in air-saturated 3.5wt% NaCl solution10.1016/j.corsci.2004.11.017 ↗