Corrosion behaviour of Lotus-type porous high nitrogen nickel-free stainless steels
Source abstract
Abstract
Abstract Corrosion behaviour of three austenitic Lotus-type porous high nitrogen Ni-free stainless steels exposed to an acidic chloride solution has been investigated by electrochemical tests and weight loss measurements. Polarization resistance indicates that the corrosion rate of Lotus-type porous high nitrogen Ni-free stainless steels is an order of magnitude lower than that of Lotus-type porous 316L stainless steel in acidic environment. The localised corrosion resistance of the investigated high nitrogen Ni-free stainless steels, measured as pitting potential, E b , also resulted to be higher than that of type 316L stainless steel. The influences of porous structure, surface finish and nitrogen addition on the corrosion behaviour were discussed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Hydrogen embrittlement and corrosion behaviors in metals · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (34)
Show source-provided references
1. V.G. Gavriljuk, H. Berns, Springer, Berlin, Heidelberg, New York, 1999, pp. 267–268.
2. Menzel · 1990 · 365
3. Torkhov · J. Metals · 1978 · 30 · 20
4. Eklund · J. Electrochem. Soc. · 1974 · 121 · 46710.1149/1.2401840 ↗
5. Katada · Mater. Manufact. Proc. · 2004 · 19 · 1910.1081/AMP-120027495 ↗
6. M. Kikuchi, M. Kajihara, K. Frisk, Solubility of nitrogen in austenitic stainless steels, in: J. Foct, A. Hendry (Eds.), HNS 88, Lille, France, May 1988, The Institute of Metals, London, 1989, p. 63.
7. Hänninen · J. Mater. Proc. Technol. · 2001 · 117 · 42410.1016/S0924-0136(01)00804-4 ↗
8. Kuroda · Mater. Trans. · 2003 · 44 · 41410.2320/matertrans.44.414 ↗
9. Nakajima · 2003 · 191
10. Nakajima · Adv. Eng. Mater. · 2004 · 6 · 37710.1002/adem.200405149 ↗
11. Ikeda · Metall. Mater. Trans. A · 2005 · 36A · 7710.1007/s11661-005-0140-1 ↗
12. Nakajima · 2005
13. K. Alvarez, S.K. Hyun, H. Nakajima, Unpublished result, Osaka University, Osaka, Japan.
14. Feddrizzi · Brit. Corros. J. · 1991 · 26 · 4610.1179/000705991798269378 ↗
15. Angelini · Werks. Korros. · 1994 · 45 · 39210.1002/maco.19940450705 ↗
16. Velasco · Brit. Corros. J. · 1996 · 31 · 29510.1179/bcj.1996.31.4.295 ↗
17. Feddrizzi · Werks. Korros. · 1991 · 42 · 40310.1002/maco.19910420804 ↗
18. Velasco · Int. J. Powder Metall. · 1995 · 31 · 309
19. Raghu · Corrosion · 1989 · 45 · 69810.5006/1.3585020 ↗
20. Raghu · Brit. Corros. J. · 1988 · 23 · 10910.1179/000705988798270992 ↗
21. K. Alvarez, K. Sato, S.K. Hyun, H. Nakajima, Fabrication and properties of Lotus-type porous nickel-free stainless steel with high temperature nitriding, Mater. Sci. Eng. C, in press, doi:10.1016/j.msec.2007.01.010.10.1016/j.msec.2007.01.010 ↗
22. Fuseya · Mater. Trans. · 2006 · 47 · 222910.2320/matertrans.47.2229 ↗
23. Standard test method for making potentiostatic and potentiodynamic anodic polarisation measurements. ASTM Designation: G5-94. Annual Book of ASTM Standards, pp. 54–64.
24. Stern · J. Electrochem. Soc. · 1957 · 104 · 5610.1149/1.2428496 ↗
25. Standard test method for pitting and crevice corrosion resistance of stainless steels and related alloys by use of ferric chloride solution. ASTM Designation: G48-99. Annual Book of ASTM Standards, pp. 185–193.
26. Truman · Brit. Corros. J. · 1977 · 12 · 23610.1179/000705977798318973 ↗
27. Bandy · Corrosion · 1985 · 41 · 22810.5006/1.3581995 ↗
28. Newman · Corros. Sci. · 1987 · 27 · 82710.1016/0010-938X(87)90040-0 ↗
29. Claes-Olof Olsson · Corros. Sci. · 1995 · 37 · 46710.1016/0010-938X(94)00148-Y ↗
30. Jargelius-Petterson · Corros. Sci. · 1999 · 41 · 163910.1016/S0010-938X(99)00013-X ↗
31. Olefjord · Corros. Sci. · 1996 · 38 · 120310.1016/0010-938X(96)00018-2 ↗
32. Ernest · Corros. Sci. · 1997 · 39 · 113310.1016/S0010-938X(97)00043-7 ↗
33. Electropolishing-stainless steel. Part I
34. Hänninen · Mater. Sci. Forum · 1999 · 318–320 · 47910.4028/www.scientific.net/MSF.318-320.479 ↗