The effects of air pollution and climatic factors on atmospheric corrosion of marble under field exposure

Abstract The atmospheric corrosion of marble was evaluated in terms of SO 2 concentration as air pollution and climatic factors such as rainfall, relative humidity, temperature and so on under the field exposure. Marble of calcite type (CaCO 3 ) was exposed to outdoor atmospheric environment with and without a rain shelter at four test sites in the southern part of Vietnam for 3-month, 1- and 2-year periods from July 2001 to September 2003. The thickness loss of marble was investigated gravimetrically. X-ray diffraction and X-ray fluorescent methods were applied to study corrosion products on marble. The corrosion product of marble was only gypsum (CaSO 4 · 2H 2 O) and was washed out by rain under the unsheltered exposure condition. It was found that the most substantial factors influencing the corrosion of marble were rainfall, SO 2 concentration in the air and relative humidity. Based on the results obtained, we estimated the dose–response functions for the atmospheric corrosion of marble in the southern part of Vietnam.