AE response of type 304 stainless steel during stress corrosion crack propagation
Source abstract
Abstract
Acoustic emission (AE) signals generated by transgranular stress corrosion cracking (TGSCC) and intergranular stress corrosion cracking (IGSCC) have been compared by means of slow strain rate tensile tests (SSRT) performed using both solubilised and sensitised type AISI 304 stainless steel in a 1 M NaCl + 1 M HCl solution. Results show that the AE activity during the propagation of TGSCC is much higher than the AE activity during the IGSCC propagation. However, no significant difference was found between the mean amplitude and rise-time of the AE signals registered during the propagation of TGSCC and those measured for IGSCC propagation.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Fatigue and fracture mechanics · Material Properties and Failure Mechanisms
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. AE analysis during stress corrosion and corrosion fatigue processes
2. Acoustic emission during pitting and transgranular crack initiation in Type 304 stainless steel10.5006/1.3315996 ↗
3. Evaluation of stress corrosion crack initiation using acoustic emission10.5006/1.3585225 ↗
4. Characterization by AE technique of emissive phenomena during stress corrosion cracking of stainless steel
5. AE response of 316L SS during SSR test under potentiostatic control10.1016/S0010-938X(98)00178-4 ↗
6. Acoustic emission monitoring of stress corrosion cracking10.1016/0025-5416(88)90565-4 ↗
7. Acoustic emission monitoring of chloride stress corrosion cracking of austenitic stainless steel
8. A correlation between acoustic emission and fractography of cracking during SCC of zircaloys10.5006/0010-9312-30.6.191 ↗
9. Characteristics of acoustic emission during stress corrosion cracking of Inconel 600 alloy10.1016/S1359-6462(97)00222-4 ↗
10. Acoustic emission from intergranular subcritical crack growth10.1007/BF02667582 ↗
11. Investigation on pitting corrosion of stainless steel by means of acoustic emission and potentiodynamic methods10.1016/S0010-938X(03)00021-0 ↗
12. Initiation and propagation steps in pitting corrosion of austenitic stainless steel: monitoring by acoustic emission10.1016/S0010-938X(00)00099-8 ↗
13. Acoustic emission study of active –passive transitions during carbon steel erosion–corrosion in concentrated sulfuric acid10.1016/S0010-938X(01)00148-2 ↗
14. Detecting electrochemical transients generated by erosion–corrosion10.1016/S0013-4686(01)00646-6 ↗
15. AE response of α-brass during stress corrosion crack propagation10.1016/j.corsci.2007.03.043 ↗
16. Acoustic emission amplitude distributions
17. Evaluation of stress corrosion cracking phenomenon in an AISI type 316LN stainless steel using acoustic emission technique10.1016/j.corsci.2006.06.007 ↗
18. The transgranular SCC of a Mg–Al alloy10.1007/BF02658523 ↗
19. Correlation of acoustic and electrochemical noise in the stress corrosion cracking of alpha brass10.1016/0036-9748(83)90389-7 ↗
20. The propagation of transgranular stress corrosion cracks in admiralty metal10.1007/BF02661210 ↗