Corrosion and corrosion inhibition of Cu–20%Fe alloy in sodium chloride solution

Abstract The electrochemical behavior of copper (Cu), iron (Fe) and Cu–20%Fe alloy was investigated in 1.0 M sodium chloride solution of pH 2. The effect of thiourea (TU) addition on the corrosion rate of the Cu–20%Fe electrode was also studied. Open-circuit potential measurements (OCP), polarization and electrochemical impedance spectroscopy (EIS) were used. The results showed that the corrosion rates of the three electrodes follow the sequence: Cu η reach 91%. At [TU] > 5 mM, the dissolution rate of the Cu–20%Fe electrode increases due to formation of soluble thiourea complexes. At cathodic (−0.6 V), the inhibition efficiency of thiourea decreases markedly owing to a decrease of the rate of the selective dissolution reaction and/or desorption of thiourea molecules. The results indicated that thiourea acts mainly as inhibitor of the selective dissolution reaction of the Cu–20%Fe electrode in chloride solution.