High-temperature corrosion investigations of deposit containing eutectic KCl-K2SO4 mixture on AISI 1015 and SS304 steels
Source abstract
Abstract
This study investigated corrosion behaviours of biomass fly ash containing eutectic KCl-K2SO4 mixture on carbon steel AISI 1015 and stainless steel 304 (SS304) at 700 ℃ for 12 h in air. The observed corrosion behaviours were validated by comparing with corrosion on similar materials, including carbon steel STBA 12 boiler tube and SS304 erosion guard, exposed in actual boiler environments. Similar corrosion behaviours were found in both laboratory-scale and field tests. Active oxidation, caused by chlorine, dominated over internal sulfidation for carbon steels. For SS304, presence of chlorine depleted protective oxide layers of SS304, followed by internal sulfidation from sulphur species.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Metallurgical Processes and Thermodynamics · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. 2 - Biomass fly ash and biomass bottom ash
2. Ash-related issues during biomass combustion: alkali-induced slagging, silicate melt-induced slagging (ash fusion), agglomeration, corrosion, ash utilization, and related countermeasures10.1016/j.pecs.2015.09.003 ↗
3. A study on characterization of biomass fly ash10.4028/www.scientific.net/AMM.891.137 ↗
4. The effects of KCl, K2SO4 and K2CO3 on the high temperature corrosion of a 304-type austenitic stainless steel10.1007/s11085-011-9240-z ↗
5. Alkali induced high temperature corrosion of stainless steel: the influence of NaCl, KCl and CaCl210.1007/s11085-012-9293-7 ↗
6. KCl induced corrosion of a 304-type austenitic stainless steel at 600°C; the role of potassium10.1007/s11085-005-5704-3 ↗
7. High-temperature corrosion due to lead chloride mixtures simulating fireside deposits in boilers firing recycled wood10.1016/j.fuproc.2017.07.017 ↗
8. Effect of sewage sludge addition on initial corrosion of 16Mo3 and 310S when exposed in a used wood fired boiler10.1002/maco.201508693 ↗
9. Characteristics of corrosion related to ash deposition on boiler heating surface during cofiring of coal and biomass10.1155/2020/2175795 ↗
10. Co-firing high ratio of woody biomass with coal in a 150-MW class pulverized coal boiler: properties of the initial deposits and their effect on tube corrosion10.1016/j.fuel.2017.07.053 ↗
11. The quinary reciprocal salt system Na, K, Mg, Ca/Cl, SO4. A review of the literture with new data
12. Fireside corrosion on T24 steel pipes and HVOF NiCr coatings exposed to different salt mixtures10.1016/j.corsci.2020.108747 ↗
13. The influence of KCl on biomass ash melting behaviour and high-temperature corrosion of low-alloy steel10.1016/j.energy.2019.116062 ↗
14. High temperature corrosion of thermally sprayed NiCr and FeCr coatings covered with a KCl–K2SO4 salt mixture10.1016/j.surfcoat.2014.11.012 ↗
15. Study on the high-temperature corrosion behavior of superheater steels of biomass-fired boiler in molten alkali salts’ mixtures10.1177/1687814016678163 ↗
16. Reduction mechanisms of ash deposition in coal and/or biomass combustion boilers10.1016/j.fuel.2012.11.017 ↗
17. Corrosion testing of thermal spray coatings in a biomass co-firing power plant10.3390/coatings6040065 ↗
18. Effect of the temperature of different combustion zones in the boiler grate on changes in physical and chemical parameters of bituminous coal and slags10.1016/j.jsm.2016.07.002 ↗
19. 15 - High-temperature heat exchangers in indirectly fired combined cycle (IFCC) systems: materials management and performance improvement
20. Inhibition of K2SO4 on evaporation of KCl in combustion of herbaceous biomass10.1016/j.fuel.2020.119754 ↗
21. Study of the layered structure of deposit in a biomass-fired boiler (case study)10.1021/ef2003365 ↗
22. The effects of chlorides, hydrogen chloride, and sulfur dioxide in the oxidation of steels below deposits10.1016/0010-938X(95)00011-8 ↗
23. The influence of small amounts of KCl(s) on the high temperature corrosion of a Fe‐2.25Cr‐1Mo steel at 400 and 500°C10.1002/maco.201005942 ↗
24. Hot-corrosion of AISI 1020 steel in a molten NaCl/Na2SO4 eutectic at 700°C10.1063/1.4968319 ↗
25. Fireside corrosion of P92 steel with mixed sulfate deposit at 650 °C10.1007/s11085-020-09994-3 ↗
26. Chloridation and oxidation of iron, chromium, nickel and their alloys in chloridizing and oxidizing atmospheres at 400–700°C10.1016/S0010-938X(99)00142-0 ↗
27. Continuous KCl addition in high temperature exposures of 304 L – a way to mimic a boiler environment10.1016/j.corsci.2020.108511 ↗
28. Ash deposition and fouling tendency of two energy crops (cynara and poplar) and a forest residue (pine chips) co-fired with coal in a pulverized fuel pilot plant10.1021/ef401420j ↗
29. Composition‐vs‐depth profiles obtained with Auger electron spectroscopy of air‐oxidized stainless‐steel surfaces10.1063/1.1663236 ↗
30. Oxidation after breakdown of the chromium-rich scale on stainless steels at high temperature: internal oxidation10.1007/s11085-016-9610-7 ↗
31. High-temperature oxidation of FeCr(Ni) alloys: the behaviour after breakaway10.1007/s11085-017-9731-7 ↗
32. Corrosion of super-heater steel materials under alkali salt deposits. Part 2: SEM analyses of different steel materials10.1016/j.corsci.2009.11.026 ↗
33. The oxidation behavior of the new nickel-based superalloy Inconel 740 with and without Na2SO4 deposit10.1016/j.surfcoat.2003.12.003 ↗