Sulphur diffusion through a growing chromia scale and effects of water vapour
Source abstract
Abstract
Fe-30Cr (wt. %) alloy was exposed to Ar-0.5%SO2 and Ar-10%H2O-0.5%SO2 gases at 650 ◦C, forming Cr2O3 scales. In dry SO2 for 20 h, sulphur enrichment and scattered Cr-sulphides were observed at the scale-alloy interface, together with internal Cr-sulphide precipitates. After 100 h, sulphur disappeared from the interface, while more internal Cr-sulphides were produced. In wet SO2, the sulphur enrichment and Cr-sulphides were maintained in both times, but no internal sulphidation was seen. Atom probe analysis revealed sulphur enrichment on chromia grain boundaries in both gases, to a greater extent in wet SO2. These effects are discussed in terms of chromia grain boundary diffusion.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · High-Temperature Coating Behaviors · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Fireside corrosion in oxy-fuel combustion of coal10.1149/1.4718001 ↗
2. Buckthorpe, D., J. Baker, and P. Sherlock. Materials for Advanced Gas-cooled Nuclear Systems. in Advanced Materials Research. 2009. Trans Tech Publ.10.4028/3-908454-01-8.239 ↗
3. Complementary methods for the characterization of corrosion products on a plant-exposed superheater tube10.1007/s13632-016-0325-6 ↗
4. Rosendahl · 2013
5. Theoretical analysis of the diffusion processes determining the oxidation rate of alloys10.1149/1.2779605 ↗
6. Effect of alloy composition and exposure conditions on the selective oxidation behavior of ferritic Fe–Cr and Fe–Cr–X alloys10.1007/s11085-010-9215-5 ↗
7. Carburization of Fe‐Cr Alloys During Oxidation in Dry Carbon Dioxide.10.1149/1.2426622 ↗
8. High temperature corrosion of pure Fe, Cr and Fe–Cr binary alloys in O2 containing trace KCl vapour at 750° C10.1016/j.corsci.2009.05.014 ↗
9. The effect of water vapor on high temperature oxidation of Fe-Cr alloys at 1073 K10.2320/matertrans.M2009212 ↗
10. High temperature oxidation of Fe-Cr alloys in atmospheres containing 2.0% SO2+ 5.0% O210.1016/j.corsci.2021.109481 ↗
11. The problem of sulfur in high-temperature corrosion10.1007/BF01046727 ↗
12. High temperature corrosion of pure chromium in CO-CO2-SO2-N2 atmospheres10.1016/0010-938X(94)90004-3 ↗
13. Comprehensive insights into competitive oxidation/sulfidation reactions on binary ferritic alloys at high temperatures10.1016/j.corsci.2022.110236 ↗
14. Solubility of sulfur in pure Cr2O3 at 1000° C10.1007/BF00751795 ↗
15. Atom probe study of impurity segregation at grain boundaries in chromia scales grown in CO2 gas10.1016/j.corsci.2017.12.024 ↗
16. Penetration of protective chromia scales by carbon10.1016/j.scriptamat.2014.01.009 ↗
17. Perry, R.H., D.W. Green, and J. Maloney, Perry's Chemical Engineers' Handbook (ed.). Seventh, International edition, 1997.
18. The chromium-sulphur system between 873 K and 1364 K10.1016/0022-5088(77)90194-1 ↗
19. Mechanisms of simultaneous sulfidation and oxidation of Fe-Cr and Fe-Cr-Ni-alloys and of the failure of protective chromia scales10.1016/0010-938X(90)90211-M ↗
20. Sulphide formation after pre-oxidation of chromia formers10.1016/S0010-938X(96)00069-8 ↗
21. The impact of the microstructure of Fe-16Cr-0.2C on high-temperature oxidation–sulphidation in SO210.1016/j.corsci.2021.109618 ↗
22. Internal sulphidation phenomena of heat-resistant alloys at low sulphur pressures10.1016/0921-5093(89)90715-6 ↗
23. Identification and 3D reconstruction of Cr5S6 precipitates along grain boundaries in Fe13Cr10.1007/s11837-018-2940-y ↗
24. Diffusion of cations in chromia layers grown on iron-base alloys10.1007/BF00665632 ↗
25. Cation tracer diffusion in Cr2O3 and Cr2O3–0.09 wt% Y2O3.10.1111/j.1151-2916.1987.tb04910.x ↗
26. Graham, M.J., et al. Anion transport in growing Cr2O3 scales. in Materials science forum. 1989. Trans Tech Publ.
27. Young · 2016 · 1
28. Flatley, T. and N. Birks, JISI, 209, 523 (1971). F. Gesmundo, C. Asmundis, S. Merlo, & C. Bottino: Werkst. Korros, 1979. 30: p. 179.
29. The high temperature corrosion of metals in sulfidizing-oxidizing environments: a critical review10.1515/HTMP.1989.8.3.149 ↗
30. Kofstad, P., High temperature corrosion. Elsevier Applied Science Publishers, Crown House, Linton Road, Barking, Essex IG 11 8 JU, UK, 1988., 1988.
31. The breakaway corrosion of Fe-Cr alloys in atmospheres containing sulfur and oxygen10.1016/0025-5416(87)90384-3 ↗
32. Role of water vapor in chromia-scale growth at low oxygen partial pressure10.1023/A:1023040010859 ↗
33. In situ observation of whiskers, pyramids and pits during the high-temperature oxidation of metals10.1007/BF00659470 ↗
34. The transient oxidation of Fe‐Cr and Ni‐Cr alloys10.1149/1.2407761 ↗
35. Corrosion behaviour of Fe–Cr–(Mn, Si) ferritic alloys in wet and dry CO2–SO2 atmospheres at 650° C10.1007/s11085-017-9826-1 ↗
36. The oxidation behaviour of metals and alloys at high temperatures in atmospheres containing water vapour: A review10.1016/j.pmatsci.2007.11.001 ↗
37. Michalik, M., M. Hänsel, and W.J. Quadakkers, Effect of water vapour on growth and adherence of chromia scales on pure chromium. 2007: Forschungszentrum, Zentralbibliothek.
38. Kingery · 1976 · 17
39. A structural study of the Fe-Cr system alloys10.1016/S1359-6454(96)00088-2 ↗
40. Sigma-phase formation in high chromium ferritic steels at 650C10.1016/j.jallcom.2015.03.076 ↗
41. Segregation of sulfur during growth of oxide scales10.1016/0169-4332(91)90038-L ↗