Effect of coating degradation on the hot corrosion behaviour of directionally solidified superalloy
Source abstract
Abstract
The effect of coating degradation on the hot corrosion performance of coated alloys was investigated in Na 2 SO 4 /NaCl (75:25, wt./wt.) salt at 900 °C. Degraded coatings were obtained by thermal exposure before the hot corrosion test. The results indicate that when the β-NiAl phases within the coating were completely depleted, the hot corrosion process was delayed due to the Al-rich interdiffusion zone (IDZ) formed after the 900 °C thermal exposure to provide Al for the healing of the Al 2 O 3 layer. Nevertheless, the Cr-rich IDZ formed after 1000 °C thermal exposure failed to repair the Al 2 O 3 layer, causing the alloy to corrode aggressively even though Cr has been substituted for Al to participate in the corrosion process.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Nuclear Materials and Properties · High Temperature Alloys and Creep
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Hot corrosion in gas turbine components10.1016/S1350-6307(00)00035-2 ↗
2. Preparation and hot corrosion behaviour of Pt modified AlSiY coating on a Ni-based superalloy10.1016/j.corsci.2015.12.007 ↗
3. Aluminium depletion in NiCrAlY bond coatings by hot corrosion as a function of projection system10.1016/j.surfcoat.2007.07.068 ↗
4. Investigation of the mechanisms of Type-II hot corrosion of superalloy CMSX-410.1016/j.corsci.2013.11.048 ↗
5. A method for investigation of hot corrosion by gaseous Na2SO410.1016/j.corsci.2013.04.006 ↗
6. Preparation and hot corrosion behaviour of an Al-gradient NiCoCrAlYSiB coating on a Ni-base superalloy10.1016/j.corsci.2009.01.003 ↗
7. Thermal barrier coatings for gas-turbine engine applications10.1126/science.1068609 ↗
8. Thermal-barrier coatings for more efficient gas-turbine engines10.1557/mrs.2012.232 ↗
9. Mechanisms controlling the durability of thermal barrier coatings10.1016/S0079-6425(00)00020-7 ↗
10. Oxidation and hot corrosion behavior of gradient NiCoCrAlYSiB coatings deposited by a combination of arc ion plating and magnetron sputtering techniques10.1016/j.corsci.2005.09.014 ↗
11. Coatings for blade and vane applications in gas turbines10.1016/0010-938X(89)90104-2 ↗
12. Identification of hot corrosion resistant MCrAlY based bond coatings for gas turbine engine applications10.1016/S0257-8972(00)01156-7 ↗
13. Effect of experimental procedures on the cyclic, hot-corrosion behavior of NiCoCrAlY-type bondcoat alloys10.1023/A:1004698211940 ↗
14. Hot corrosion of an EB-PVD thermal-barrier coating system at 950 °C10.1023/A:1004634400479 ↗
15. Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys10.1016/j.surfcoat.2003.12.020 ↗
16. High-temperature oxidation and hot-corrosion behavior of a sputtered NiCrAlY coating with and without aluminizing10.1016/j.surfcoat.2005.10.042 ↗
17. Modelling the microstructural evolution and degradation of M-Cr-Al-Y coatings during high temperature oxidation10.1016/0257-8972(87)90095-8 ↗
18. Modeling of microstructural evolution and lifetime prediction of MCrAlY coatings on nickel based superalloys during high temperature oxidation10.1016/j.surfcoat.2013.05.008 ↗
19. Lifetime modelling for MCrAlY coatings in industrial gas turbine blades10.1590/S1516-14392004000100007 ↗
20. Some aspects on modelling of the β-phase depletion behaviour under different oxide growth kinetics in HVOF CoNiCrAlY coatings10.1016/j.surfcoat.2017.01.075 ↗
21. Influence of cryomilling on the morphology and composition of the oxide scales formed on HVOF CoNiCrAlY coatings10.1023/B:OXID.0000025332.26757.41 ↗
22. Hot corrosion behaviour of low Al NiCoCrAlY cladded coatings reinforced by nano-particles on a Ni-base super alloy10.1016/j.corsci.2010.07.011 ↗
23. Hot corrosion behavior and microstructural change of Al-gradient CoNiCrAlYSi coatings, produced by LVPS and diffusional processes10.1007/s11085-012-9288-4 ↗
24. Hot corrosion of arc ion plating NiCrAlY and sputtered nanocrystalline coatings on a nickel-based single-crystal superalloy10.1016/j.corsci.2017.04.004 ↗
25. High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900 °C10.1016/j.surfcoat.2011.06.037 ↗
26. Influence of sputtered nanocrystalline coating on oxidation and hot corrosion of a nickel-based superalloy M95110.1016/j.jmst.2014.01.001 ↗
27. Hot corrosion behaviour of Pt modified aluminized NiCrAlYSi coating on a Ni-based single crystal superalloy10.1016/j.corsci.2019.01.014 ↗
28. Hot corrosion and cyclic oxidation performance of a PtAl2-dispersed (Ni,Pt)Al coating prepared by low-activity high-temperature aluminizing10.1016/j.jallcom.2022.164978 ↗
29. Preparation and hot corrosion behaviour of a MCrAlY+AlSiY composite coating10.1016/j.corsci.2008.08.018 ↗
30. Hot corrosion properties of composite coatings in the presence of NaCl at 700 and 900 °C10.1016/j.corsci.2013.01.004 ↗
31. The role that bond coat depletion of aluminum has on the lifetime of APS-TBC under oxidizing conditions10.1002/maco.200804137 ↗
32. Bond coat oxidation and its significance for life expectancy of thermal barrier coating systems10.1179/026708304225012143 ↗
33. The failure of protective oxides on plasma-sprayed NiCrAlY overlay coatings10.1023/A:1004549219013 ↗
34. The oxidation of finite samples of heat-resistant alloys10.1016/S0010-938X(72)80016-7 ↗
35. High temperature stress and its influence on surface rumpling in NiCoCrAlY bond coat10.1016/j.actamat.2017.08.001 ↗
36. Microstructural evolution of NiCoCrAlY coated directionally solidified superalloy10.1016/j.surfcoat.2022.128487 ↗
37. On the mechanism of secondary reaction zone formation in a coated nickel-based single-crystal superalloy containing ruthenium10.1016/j.scriptamat.2013.03.015 ↗
38. Effect of Pt-Al bond coat on the high-cycle fatigue behaviour of a second-generation single crystal nickel-based superalloy at different temperatures10.1016/j.jmrt.2021.06.091 ↗
39. Influence of thermal exposure on the creep properties of an aluminized Ni-based single crystal superalloy in different surface orientations10.1016/j.matdes.2013.11.075 ↗
40. Effect of Pt-aluminide bond coat on tensile and creep behavior of a nickel-base single crystal superalloy10.1016/j.msea.2015.05.051 ↗
41. On the high-temperature oxidation of MCrAlY coatings10.3139/146.110201 ↗
42. High temperature corrosion behaviour of a gradient NiCoCrAlYSi coating I: Microstructure evolution10.1016/j.corsci.2010.01.025 ↗
43. Na2SO4 induced accelerated oxidation (hot corrosion) of nickel10.1007/BF02642794 ↗
44. Influence of alloying elements on hot corrosion resistance of nickel-based single crystal superalloys coated with Na2SO4 salt at 900 °C10.1016/j.matdes.2020.109197 ↗
45. Oxidation of single crystal PWA 1483 at 950 °C in flowing air10.1016/j.corsci.2008.06.033 ↗
46. Oxidation of Ni-Cr-Al alloys between 1000 °C and 1200 °C10.1149/1.2407837 ↗
47. The influence of sulfides on the oxidation behavior of nickel-base alloys10.1007/BF03037874 ↗
48. Oxidation of nickel-based single-crystal superalloys for industrial gas turbine applications10.1016/j.actamat.2010.09.027 ↗
49. Corrosion kinetics of a directionally solidified Ni-base superalloy10.1016/j.actamat.2007.01.034 ↗