Preparation and corrosion behavior of the Al-modified MoSi2/Al2O3 coating on the surface of molybdenum metal core
Source abstract
Abstract
Abstract The Al-modified MoSi2/Al2O3 coating was designed on molybdenum metal surface, and then its corrosion-resistant property was evaluated in a GTD111 superalloy. Results showed the Al-modified MoSi2 coating obtained by pack cementation was comprised of Mo(Si,Al)2, Al8Mo3, and AlMo3. Then, the oxidation behavior of the coating at 1300 ℃ was systematically investigated to generate a protective Al2O3 scale. After casting test, corrosion behaviors of Al-modified MoSi2/Al2O3 coating without and with Al8Mo3 phase were contrasted to illustrate the mechanism resisting to the molten superalloy at 1550 ℃. The Al8Mo3 phase and thermal shock give rise to the coating failure.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Intermetallics and Advanced Alloy Properties · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (25)
Show source-provided references
1. C. D. Greskovich, R.C. DeVrries, B. Hills, Alumina-based ceramics for core materials, US4,156,614, (1977).
2. R. V. Naik, J. Corrigan, Reinforced quartz cores for directional solidification castingprocesses, US6,029,736, (2000).
3. An overview of ceramic molds for investment casting of nickel superalloys10.1016/j.jeurceramsoc.2020.07.013 ↗
4. J. T. Beals, D.M. Shah, J. Snyder, J. Wiedemer, Refractory metal core, US6,91,3064, (2005).
5. J. T.Beals, J. Persky, D. M. Shah, V. Seetharaman, S. Bose, J. Snyder, et.al, Refractory metalcore coatings, US7,575,039, (2009).
6. Microstructure evolution and properties of silica-based ceramic cores reinforced by mullite fibers10.1016/j.jallcom.2020.154494 ↗
7. Mechanical and kinetic studies on the refractory fused silica of integrally cored ceramic mold fabricated by additive manufacturing10.1016/j.jeurceramsoc.2018.09.013 ↗
8. J. T. Beals, C.M. Lomasney, J. Joseph, J. Parkos, Method for casting core removal, US7,882,884, (2011).
9. Resistance to molten superalloy at 1550 °C for molybdenum metal core with a silica/silicide coating10.3390/coatings11030275 ↗
10. Oxidation behavior of MoSi2 and Mo(Si, Al)2 coated Mo–0.5Ti–0.1Zr–0.02C alloy10.1016/j.intermet.2010.12.002 ↗
11. Deposition and oxidation behavior of Mo(Si,Al)2/MoB layered coatings on TZM alloy10.1016/j.ijrmhm.2017.04.008 ↗
12. Oxidation behaviour of the Mo–Si–B and Mo–Si–B–Al alloys in the temperature range of 700–1300 °C10.1016/j.intermet.2007.02.012 ↗
13. Oxidation behavior of a Mo (Si, Al)2-based composite at 300–1000 °C10.1016/j.intermet.2009.10.019 ↗
14. Oxidation behaviour of a Mo(Si,Al)2 based composite at 1500 °C10.1016/j.intermet.2011.05.002 ↗
15. Microstructure and oxidation behavior of Mo-Si-Al coating on Nb-based alloy10.1016/j.jallcom.2017.11.339 ↗
16. The intermediate and high-temperature oxidation behaviour of Mo(Si1 − xAlx)2 intermetallic alloys10.1016/S0966-9795(96)00068-4 ↗
17. Improvement of stress-rupture life of GTD-111 by second solution heat treatment10.1016/j.matdes.2012.09.011 ↗
18. Development of Mo(Si,Al)2-MoB composite coatings to protect TZM alloy against oxidation at 1400 °C10.1016/j.intermet.2017.12.002 ↗
19. Phase equilibria in the Al–Mo–Si system10.1016/j.intermet.2010.11.010 ↗
20. Preparation of alumina/aluminide coatings on molybdenum metal substrates, and protection performance evaluation utilizing a DZ40M superalloy casting test10.1016/j.surfcoat.2020.125931 ↗
21. Codeposition of Al and Si to form oxidation-resistant coatings on γ-TiAl by the pack cementation process10.1016/S0254-0584(02)00551-5 ↗
22. Study on reaction and diffusion in the Mo–Si system by ZrO2 marker experiments10.1016/S1359-6462(02)00029-5 ↗
23. Binary System Mo-Ni: Datasheet from Landolt-Börnstein - Group IV Physical Chemistry·Volume 19C1: "Ternary Steel Systems: Phase Diagrams and Phase Transition Data"
24. B. Predel, Al-Mo (Aluminum-Molybdenum): Datasheet from Landolt-Börnstein - Group IV Physical Chemistry, "Ac-Au – Au-Zr", in: SpringerMaterials, Springer-Verlag Berlin Heidelberg, 5A. 〈https://doi.org/10.1007/10000866_120〉.10.1007/10000866_120 ↗
25. Die Kristallstruckturen von TiSi, Ti(Al,Si)2 und Mo(Al,Si)210.1007/BF00918638 ↗