Plasma corrosion resistance of RO-Al2O3-SiO2 (R: Alkaline earth) under fluorocarbon plasma with Ar+: Ⅱ. Plasma resistant glass
Source abstract
Abstract
Abstract High-density plasma dry etching was performed with a mixture of CF4/O2/Ar gases, and the plasma resistant properties of RO-Al2O3-SiO2 (R: alkaline earth) glass were analyzed. RAS had etch rates below 25㎚/min, which are lower than that of alumina and sapphire. CAS showed an improvement in the etch rate, which corresponds to 72% of that recorded by sapphire. The plasma resistant properties of RAS glass are more significantly influenced by the sublimation temperature with fluoride than atomic binding energy. The difference in the etch rates of the RAS glass was smaller at higher sublimation temperatures.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Plasma Diagnostics and Applications · ZnO doping and properties · Advanced ceramic materials synthesis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (26)
Show source-provided references
1. Relative sputtering rates of oxides and fluorides of aluminum and yttrium10.1016/j.surfcoat.2016.11.007 ↗
2. Reduction of particle contamination in plasma-etching equipment by dehydration of chamber wall10.1143/JJAP.47.3630 ↗
3. Plasma etching behavior of Y2O3 ceramics: comparative study with Al2O310.1016/j.apsusc.2016.01.092 ↗
4. May · 2006 · 98
5. Y. Chang, G. C. Tzu, S. P. Umotoy, C. T. Kao, W. Kuang, X. Yuan, M. Chang, Apparatus for generating plasma by RF power, United States Patent No. 0130971 A1, (2000).
6. Particle reduction using Y2O3 material in an etching tool
7. High erosion resistant Y2O3-carbon electroconductive composite under the fluorocarbon plasma10.1016/j.ceramint.2012.07.046 ↗
8. Comparison of erosion behavior and particle contamination in mass-production CF4/O2 plasma chambers using Y2O3 and YF3 protective coatings10.3390/nano7070183 ↗
9. Fabrication and plasma resistance of Y2O3 ceramics10.1016/j.ceramint.2015.06.109 ↗
10. Plasma-resistant dense yttrium oxide film prepared by aerosol deposition process10.1111/j.1551-2916.2007.01738.x ↗
11. Surface chemistry associated with plasma etching processes10.1016/S0169-4332(02)00021-1 ↗
12. Characterization of residual defects in plasma-exposed Si substrates using cathodoluminescence and positron annihilation spectroscopy
13. Effects of nitrogen incorporation on plasma erosion behaviors of oxynitride glasses10.1016/j.jnoncrysol.2010.05.057 ↗
14. Effect of rare-earth elements on the plasma etching behavior the RE-Si-Al-O glasses10.1016/j.jnoncrysol.2011.12.082 ↗
15. Characteristics of carbon tetrafluoride plasma resistance of various glasses10.4191/kcers.2016.53.6.700 ↗
16. J. H. Choi, H. B. Park, H. J. Kim, Plasma corrosion resistance of aluminosilicate oxide glasses containing Ca, Y and B under fluorocarbon plasma with Ar+: Ⅰ. Plasma Resistant Glass, Corros. Sci. Manuscript number: CORSCI_2017_1155 (In submitted).
17. NIST-JANAF Thermochemical tables, fourth edition
18. New chamber walls conditioning and cleaning strategies to improve the stability of plasma processes10.1088/0963-0252/14/3/025 ↗
19. Formation and properties of calcium aluminosilicate glasses10.1111/j.1151-2916.1985.tb09656.x ↗
20. Effects of artificial pores and purity on the erosion behaviors of polycrystalline Al2O3 ceramics under fluorine plasma10.2109/jcersj2.117.863 ↗
21. Characterization of masking layers for deep wet etching of glass in an improved HF/HCl solution10.1016/j.surfcoat.2004.10.094 ↗
22. Insight into silicate-glass corrosion mechanisms10.1038/nmat2301 ↗
23. Fluorination mechanisms of Al2O3 and Y2O3 surfaces irradiated by high-density CF4/O2 and SF6/O2 plasmas10.1116/1.3112624 ↗
24. Nojiri · 2015 · 22
25. Jarvholm · 2007
26. Sankaran · 2003