Effect of precipitated Mg-containing corrosion products on the anodic behavior of steel in aqueous corrosion for Zn-Al-Mg coated steel
Source abstract
Abstract
The role of precipitated Mg-containing corrosion product in the anodic behavior of the steel in aqueous corrosion was ascertained to analyze the corrosion protection mechanism at steel substrate of the Zn-Al-Mg coated steel. For the Zn-Al-Mg coating, the corrosion products that formed during the immersion test passivated the steel in the deaerated solution at pH 8.2. EDS analysis revealed that Mg-species remained on the steel after polarization. However, the concentration of Mg decreased after polarization. The results indicated that the alkalization and barrier effect by the Mg-containing corrosion products passivated the steel substrate, preventing red rust generation at the cut-edge.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Concrete Corrosion and Durability · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Effect of quenching in aqueous polyvinylpyrrolidone solutions on the microstructure and pitting corrosion resistance of AISI 1045 carbon steel10.1002/maco.202213658 ↗
2. Beneficial role of retained austenite in pitting corrosion resistance of Fe-C-Si-Mn steel in chloride environments10.1016/j.corsci.2022.110251 ↗
3. Excellent corrosion-resistant Zn-Al-Mg-Si alloy hot-dip galvanized steel sheet SUPER DYMA
4. New corrosion resistant coated steel ZEXEED
5. The effects of RE and Si on the microstructure and corrosion resistance of Zn–6Al–3Mg hot dip coating10.1016/j.apsusc.2015.09.172 ↗
6. Effect of Zn-Mg interlayer on the corrosion resistance of multilayer Zn-based coating fabricated by physical vapor deposition process10.1016/j.corsci.2022.110330 ↗
7. Improving corrosion stability of ZnAlMg by alloying for protection of car bodies10.1016/j.surfcoat.2016.03.062 ↗
8. Composition of corrosion products formed on Zn–Mg, Zn–Al and Zn–Al–Mg coatings in model atmospheric conditions10.1016/j.corsci.2014.05.016 ↗
9. Effect of Mg content on microstructure and corrosion behavior of hot dipped Zn–Al–Mg coatings10.1016/j.jallcom.2016.02.026 ↗
10. Influence mechanism of different elements and alloy phases on the corrosion resistance of Zn-Al-Mg coated steel in the atmospheric environment: a review10.1016/j.corcom.2023.11.001 ↗
11. Study of the corrosion behavior and mechanism of a hot-dipping Zn–6Al–3Mg alloy coating in 3.5 wt% neutral NaCl solution10.1016/j.surfcoat.2023.129576 ↗
12. Corrosion behavior of erbium modified Zn-11Al-3Mg cast alloy in stagnant 3.5 wt% NaCl solution
13. Initial stages of localized corrosion at cut-edges of adhesively bonded Zn and Zn-Al-Mg galvanized steel10.1016/j.electacta.2016.06.045 ↗
14. Coil-coated Zn–Mg and Zn–Al–Mg: effect of climatic parameters on the corrosion at cut edges10.1016/j.porgcoat.2015.01.023 ↗
15. Effect of cerium salts on the cut-edge of zinc-based sacrificial coatings: influence of Al and Mg alloying elements on galvanic corrosion10.1016/j.jallcom.2024.173711 ↗
16. Long-term atmospheric corrosion rates of hot dip galvanised steel and zinc-aluminium-magnesium coated steel10.1002/maco.201911010 ↗
17. Corrosion mechanism of model zinc–magnesium alloys in atmospheric conditions10.1016/j.corsci.2008.06.008 ↗
18. Corrosion Resistance of Zn-11%Al-3%Mg-0.2%Si Alloy Coated Steel Sheet in the Marine Atmospheric after Long Term Outdoor Exposure
19. Investigation of corrosion resistance of pre-painted Zn-11%Al-3%Mg-0.2%Si alloy coated steel sheet through outdoor exposure test in Okinawa
20. Mechanistic study on the cut-edge corrosion behaviors of Zn-Al-Mg alloy coated steel sheets in chloride containing environments10.1016/j.corsci.2019.108170 ↗
21. Surface and cut-edge corrosion behavior of Zn-Mg-Al alloy-coated steel sheets as a function of the alloy coating microstructure10.1007/s12540-015-5411-9 ↗
22. The effect of magnesium additions on the microstructure and cut edge corrosion resistance of zinc aluminium alloy galvanised steel10.1016/j.corsci.2008.02.005 ↗
23. Initial dissolution of Mg-containing phase and corrosion product formation in cut-edge corrosion of Zn-11%Al-3%Mg-0.2%Si coated steel10.1016/j.corsci.2023.111605 ↗
24. Effect of Iron Rust on Hydrogen Uptake during Steel Corrosion under an Aqueous NaCl Droplet10.2355/isijinternational.ISIJINT-2020-528 ↗
25. The electrochemical reduction of rust films on weathering steel surfaces10.1149/1.2123648 ↗
26. Study of lepidocrocite γ-FeOOH electrochemical reduction in neutral and slightly alkaline solutions at 25°C10.1016/j.electacta.2005.05.049 ↗
27. Role of steel and zinc coating thickness in cut edge corrosion of coil coated materials in atmospheric weathering conditions; Part 1: laboratory study10.1016/j.porgcoat.2016.06.013 ↗
28. Role of steel and zinc coating thickness in cut edge corrosion of coil coated materials in atmospheric weathering conditions; Part 2: field data and model10.1016/j.porgcoat.2016.06.019 ↗
29. Micro-electrochemical investigation on the role of Mg in sacrificial corrosion protection of 55mass%Al-Zn-Mg coated steel10.1016/j.corsci.2017.07.020 ↗
30. Cathodic self-healing at cut-edges: the effect of Zn2+ and Mg2+ ions10.1016/j.corsci.2012.08.008 ↗
31. Effect of environmental cation species on corrosion near shear cut edge of 55%Al–Zn alloy coated steel sheet10.2355/isijinternational.49.574 ↗
32. Effect of environmental conditions on the corrosion near shear cut edge of 55 mass% Al–Zn alloy coated steel sheets10.2355/isijinternational.51.462 ↗
33. The effect of synthetic zinc corrosion products on corrosion of electrogalvanized steel: I. Cathodic reactivity under zinc corrosion products10.1016/j.corsci.2013.11.045 ↗
34. The effect of synthetic zinc corrosion products on corrosion of electrogalvanized steel. II. Zinc reactivity and galvanic coupling zinc/steel in presence of zinc corrosion products10.1016/j.corsci.2013.12.024 ↗
35. Mechanism of Corrosion Protection at Cut Edge of Zn-11%Al-3%Mg-0.2%Si Coated Steel Sheets10.2355/tetsutohagane.TETSU-2018-149 ↗
36. The atmospheric corrosion of iron—a discussion of the physico-chemical fundamentals of this omnipresent corrosion process invited review10.1002/bbpc.19900940603 ↗
37. Understanding corrosion via corrosion product characterization: I. Case study of the role of Mg alloying in Zn–Mg coating on steel10.1016/j.corsci.2009.03.005 ↗
38. Understanding corrosion via corrosion product characterization: II. Role of alloying elements in improving the corrosion resistance of Zn–Al–Mg coatings on steel10.1016/j.corsci.2011.03.016 ↗
39. HSC Chemistry Thermo-chemical Database, Version 6.1, Outotec Research Oy
40. Corrosion mechanisms of Zn(Mg, Al) coated steel in accelerated tests and natural exposure: 1. The role of electrolyte composition in the nature of corrosion products and relative corrosion rate10.1016/j.corsci.2014.05.014 ↗
41. Corrosion mechanisms of Zn(Mg,Al) coated steel: 2. The effect of Mg and Al alloying on the formation and properties of corrosion products in different electrolytes10.1016/j.corsci.2014.07.042 ↗
42. Effect of Magnesium on Corrosion Behavior of Hot-Dip Zn-Al-Mg Coating10.1007/s11665-021-05718-z ↗
43. Marcus · 2011
44. Effect of the microstructure of Zn-Al and Zn-Al-Mg model alloys on corrosion stability10.1016/j.corsci.2016.04.022 ↗
45. Characterization of corrosion products of Zn and Zn–Mg–Al coated steel in a marine atmosphere10.1016/j.corsci.2014.06.017 ↗
46. Influence of microstructure of zinc-aluminium-magnesium alloy coated steel on the corrosion behavior in outdoor marine atmosphere10.1016/j.surfcoat.2019.06.052 ↗
47. The Effect of Microstructure on Local Corrosion Product Formation during Initial SO2- Induced Atmospheric Corrosion of ZnAlMg Coating Studied by FTIR-ATR FPA Chemical Imaging10.3390/cmd4030026 ↗
48. Corrosion mechanisms of Zn (Mg, Al) coated steel: the effect of HCO3− and NH4+ ions on the intrinsic reactivity of the coating10.1016/j.electacta.2014.09.140 ↗
49. Environmental effects on selective dissolution from ZnAlMg alloy under low frequency alternating current perturbations10.1016/j.electacta.2017.03.210 ↗