Hot corrosion behavior of APS YSZ coatings treated by laser micro glazing (LMG) under molten salts (V2O5 +Na2SO4)
Source abstract
Abstract
In this study, yttria-stabilized zirconia (YSZ) coatings prepared by atmospheric plasma spraying (APS) were glazed by a nanosecond pulsed laser (laser micro glazing, LMG). The hot corrosion mechanism of as-sprayed, ground, and LMGed YSZ coatings was investigated at a temperature of 1100 ºC in V 2O 5 and Na 2SO 4 molten salts for 20 h. The results show that a dense LMGed layer with narrow network of segmented microcracks (sub-micron level) was formed after the LMG process. Compared to the single-time LMG, pores can be effectively eliminated after six-times laser irradiation. The hot corrosion behavior of YSZ coatings exposed to molten V 2O 5 +Na 2SO 4 demonstrates that pores in the single-time LMGed layer seriously affect its hot corrosion resistance. After multiple LMG, the volume fraction of the m-ZrO 2 decreases from 53% to 27% with the disappearance of pores. The quantity of the corrosion products YVO 4 was greatly reduced and the depth of the damaged area diminished from 37.073 µm to 20.918 µm, which shows a significant improvement in molten salts corrosion resistance.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Glass properties and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (50)
Show source-provided references
1. Thermogravimetric study of the 800°C reaction of zirconia stabilizing oxides with SO3-NaVO310.1149/199216.0632PV ↗
2. Effect of thermal aging on microstructure and functional properties of zirconia-base thermal barrier coatings10.1007/s11666-009-9313-6 ↗
3. Commercial thermal barrier coatings with a double-layer bond coat on turbine vanes and the process repeatability10.1016/j.surfcoat.2009.02.007 ↗
4. Effect of substrate temperature on the microstructure and properties of thick plasma-sprayed YSZ TBCs10.1016/j.jeurceramsoc.2011.07.022 ↗
5. Characteristics of thick columnar YSZ coatings fabricated by plasma spray-physical vapor deposition10.1016/j.jeurceramsoc.2017.10.059 ↗
6. Processing science of advanced thermal-barrier systems10.1557/mrs.2012.233 ↗
7. Investigation on hot-fatigue behaviors of gradient thermal barrier coatings by EB-PVD10.1016/S0257-8972(01)01347-0 ↗
8. Thermodynamic conditions for cluster formation in supersaturated boundary layer during plasma spray-physical vapor deposition10.1016/j.apsusc.2018.12.070 ↗
9. Microscopic observation of laser glazed yttria-stabilized zirconia coatings10.1016/j.apsusc.2010.03.143 ↗
10. CMAS corrosion behavior and protection method of thermal barrier coatings for aeroengine
11. Hot corrosion behavior of EB-PVD YSZ coatings treated by nanosecond pulsed laser10.1016/j.surfcoat.2022.128889 ↗
12. Thermal Barrier Coatings for Gas-Turbine Engine Applications10.1126/science.1068609 ↗
13. Hot corrosion behaviour of Yb2Zr2O7 ceramic coated with V2O5 at temperatures of 600–800°C in air10.1016/j.corsci.2010.06.007 ↗
14. Hot corrosion behavior of solution precursor and atmospheric plasma sprayed thermal barrier coatings10.1016/j.corsci.2015.05.034 ↗
15. Gas turbine coatings – an overview10.1016/j.engfailanal.2012.07.007 ↗
16. Effects of Selective Laser Modification and Al Deposition on the Hot Corrosion Resistance of Ceria and Yttria-Stabilized Zirconia Thermal Barrier Coatings
17. Effect of Al2O3 overlay on hot-corrosion behavior of yttria-stabilized zirconia coating in molten sulfate-vanadate salts10.1016/S0040-6090(03)00670-9 ↗
18. A comparative study on hot corrosion resistance of three types of thermal barrier coatings: YSZ, YSZ + Al2O3 and YSZ/Al2O310.1016/j.msea.2007.06.001 ↗
19. Hot corrosion behavior of dense CYSZ/YSZ bilayer coatings deposited by atmospheric plasma spray in Na2SO4 + V2O5 molten salts10.1016/j.surfcoat.2021.128066 ↗
20. Microscopic observation of degradation behavior in yttria and ceria stabilized zirconia thermal barrier coatings under hot corrosion10.1016/j.surfcoat.2004.04.065 ↗
21. Evolution of hot corrosion resistance of YSZ, Gd2Zr2O7, and Gd2Zr2O7+YSZ composite thermal barrier coatings in Na2SO4+V2O5 at 1050°C10.1016/j.jeurceramsoc.2012.01.006 ↗
22. Corrosion Behavior of ( Gd0.9Sc0.1) 2Zr2O7 /YSZ thermal barrier coatings exposed to V2O5+ Na2SO4 molten salts
23. Opportunities for TBCs in the ZrO2–YO1.5–TaO2.5 system10.1016/j.surfcoat.2006.11.011 ↗
24. Surface laser-glazing of plasma-sprayed thermal barrier coatings10.1016/j.apsusc.2005.01.047 ↗
25. Effects of laser surface remelting on the molten salts corrosion resistance of yttria-stabilized zirconia coatings10.1016/j.ceramint.2018.09.041 ↗
26. Molten sodium corrosion of laser surface remelted yttria-stabilized zirconia thermal barrier coatings10.1016/j.corsci.2021.109740 ↗
27. The role of the surface morphology and segmented cracks on the damage forms of laser re-melted thermal barrier coatings in presence of a molten salts (Na2SO4+V2O5)10.1016/j.corsci.2016.11.011 ↗
28. Microstructure modification of Y2O3 stabilized ZrO2 thermal barrier coatings by laser glazing and the effects on the hot corrosion resistance10.1007/s40145-020-0363-z ↗
29. Femtosecond laser polishing yttria-stabilized zirconia coatings for improving molten salts corrosion resistance10.1016/j.corsci.2021.109367 ↗
30. Thermochemical Interaction of Thermal Barrier Coatings with Molten CaO–MgO–Al2O3–SiO2 (CMAS) Deposits10.1111/j.1551-2916.2006.01209.x ↗
31. What is the suitable segmentation crack density for atmospheric plasma sprayed thick thermal barrier coatings with the improved thermal shock resistance?10.1016/j.apsusc.2017.05.030 ↗
32. Effects of laser remelting on microstructure and solid particle erosion characteristics of ZrO2–7wt%Y2O3 thermal barrier coating prepared by plasma spraying10.1016/j.ceramint.2014.01.101 ↗
33. A model to predict the ablation width and calculate the ablation threshold of femtosecond laser10.1016/j.apsusc.2018.06.093 ↗
34. Comparison of hot corrosion behaviors of plasma-sprayed nanostructured and conventional YSZ thermal barrier coatings exposure to molten vanadium pentoxide and sodium sulfate10.1016/j.jeurceramsoc.2013.08.006 ↗
35. Evaluation of hot corrosion behavior of plasma sprayed ceria and yttria stabilized zirconia thermal barrier coatings in the presence of Na2SO4+V2O5 molten salts10.1016/j.ceramint.2012.05.047 ↗
36. Microstructure evolution in yttria stabilized zirconia during laser hybrid induction modification10.1016/j.jallcom.2019.151898 ↗
37. Fabrication and evaluation of plasma- sprayed nanostructured and conventional YSZ thermal barrier coatings10.2174/157341312800620250 ↗
38. Hot corrosion behavior of rare earth zirconates and yttria partially stabilized zirconia thermal barrier coatings, Surface and Coatings Technology
39. Hot corrosion evaluation of Gd2O3-Yb2O3 co-doped Y2O3 stabilized ZrO2 thermal barrier oxides exposed to Na2SO4+V2O5 molten salts10.1016/j.ceramint.2016.11.109 ↗
40. Initial phase hot corrosion mechanism of gas tunnel type plasma sprayed thermal barrier coatings10.1016/j.mseb.2011.12.037 ↗
41. Evaluation of hot corrosion behavior of CSZ, CSZ/micro Al2O3 and CSZ/nano Al2O3 plasma sprayed thermal barrier coatings10.1016/j.ceramint.2013.08.135 ↗
42. Thermogravimetric Study of the 800°C Reaction of Zirconia Stabilizing Oxides with SO 3 – NaVO310.1149/1.2068981 ↗
43. Hot corrosion behavior of Al2O3 laser clad plasma sprayed YSZ thermal barrier coatings10.1016/j.ceramint.2016.08.090 ↗
44. The influence of laser treatment on hot corrosion behavior of plasma-sprayed nanostructured yttria stabilized zirconia thermal barrier coatings10.1016/j.jeurceramsoc.2014.01.031 ↗
45. Fluid flow through granular beds10.1016/S0263-8762(97)80003-2 ↗
46. Simple expression for the tortuosity of porous media10.1007/s11242-011-9734-9 ↗
47. Evaluation of microstructural evolution and corrosion types in ultrasonic assisted laser re-melted thermal barrier coatings under exposure to molten salts10.1016/j.matlet.2016.11.037 ↗
48. Microstructure and thermal cyclic performance of laser-glazed plasma-sprayed ceria–yttria-stabilized zirconia thermal barrier coatings10.1016/j.surfcoat.2008.06.118 ↗
49. Phase stability and hot corrosion behavior of ZrO2–Ta2O5 compound in Na2SO4–V2O5 mixtures at elevated temperatures10.1016/j.ceramint.2013.08.062 ↗
50. Vanadia reactions with yttria stabilized zirconia10.1063/1.340327 ↗