The effect of salt composition on the stress-free and corrosion-fatigue performance of a fine-grained nickel-based superalloy
Source abstract
Abstract
This paper describes work to study hot corrosion damage in the nickel-based gas turbine alloy RR1000 coated with various salts at 600 °C. Interest in type-II hot corrosion on the fatigue resistance of gas turbine alloys has increased to minimise power/thermal inefficiencies. Stress-free corrosion demonstrated a greater impact of sulphate (versus chloride) on maximum pit depth, a key influencing factor of fatigue lives. In corrosion-fatigue testing, at low stresses sulphate was shown to be more influential of fatigue life. At high stresses, the presence of greater crack initiation sites, reduced initiation lives and cracked oxide suggests chlorine influenced the crack-initiation behaviour.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: High Temperature Alloys and Creep · High-Temperature Coating Behaviors · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Nickel-based superalloys for advanced turbine engines: chemistry, microstructure, and properties10.2514/1.18239 ↗
2. Darecki · Flightpath · 2011 · 2050
3. A. Encinas-Oropesa, G.L. Drew, M.C. Hardy, A.J. Leggett, J.R. Nicholls, N.J. Simms, Effects of oxidation and hot corrosion in a nickel disc alloy, in: Proceedings of Superalloys 2008 11th Int. Symp. Superalloys, 2008, pp. 609–618. 〈https://doi.org/10.7449/2008/Superalloys_2008_609_618〉.10.7449/2008/Superalloys_2008_609_618 ↗
4. Hot corrosion in gas turbines
5. Na2SO4-induced accelerated oxidation (Hot Corrosion) of nickel10.1007/BF02642794 ↗
6. J.K. Tien, T. Caulfield, Superalloys, supercomposites and superceramics, (n.d.).
7. Low temperature hot corrosion of Co-Cr-Al Alloys10.1016/0025-5416(87)90395-8 ↗
8. The effects of KCl, K 2SO 4 and K 2CO 3 on the high temperature corrosion of a 304-type austenitic stainless steel10.1007/s11085-011-9240-z ↗
9. High temperature corrosion of inconel 600 in NaCl-KCl molten salts10.1155/2014/696081 ↗
10. Study on the high-temperature corrosion behavior of superheater steels of biomass-fired boiler in molten alkali salts’ mixtures10.1177/1687814016678163 ↗
11. T.P. Gabb, J. Telesman, B. Hazel, D.P. Mourer, The effects of hot corrosion pits on the fatigue resistance of a disk superalloy, 2009. 〈https://doi.org/10.1007/s11665-009-9399-5〉.10.1007/s11665-009-9399-5 ↗
12. Influence of hot corrosion on low cycle fatigue behavior of nickel base superalloy SU 26310.1016/j.ijfatigue.2013.02.006 ↗
13. Fatigue resistance of a hot corrosion exposed disk superalloy at varied test temperatures10.1080/09603409.2016.1179000 ↗
14. Pre-notched and corroded low cycle fatigue behaviour of a nickel-based alloy for disc rotor applications10.1016/j.ijfatigue.2017.08.009 ↗
15. Corrosion-fatigue testing of Ni-based superalloy RR100010.1080/02670836.2016.1242827 ↗
16. Influence of environmental factors on the corrosion-fatigue response of a nickel-based superalloy10.1080/02670836.2017.1300419 ↗
17. On the effect of environmental exposure on dwell fatigue performance of a fine-grained nickel-based superalloy10.1007/s11661-018-4752-7 ↗
18. Developing damage tolerance and creep resistance in a high strength nickel alloy for disc applications10.7449/2004/Superalloys_2004_83_90 ↗
19. Reed · Superalloys: Fundam. Appl. · 2015
20. H. Rosier, M. Dowd, K. Perkins, G. Gibson, Development and Validation of an Automated Salt Spray Procedure for SILOET II WP 17.2.4.1, 2015.
21. Optimisation of a salt deposition technique for the corrosion-fatigue testing of nickel based superalloys10.1080/09603409.2017.1380943 ↗
22. M.L. Hendery, M.T. Whittaker, B.J. Cockings, P.M. Mignanelli, The Effect of Salt Chemistry on the Zero and Cyclic Load Performance of a High Temperature Nickel-Based Superalloy, in: Proc. 8th E[1] M.L. Hendery, M.T. Whittaker, B.J. Cockings, P.M. Mignanelli, Eff. Salt Chem. Zero Cycl. Load Perform. a High Temp. Nickel-Based Superalloy, Proc. 8th Eng. Integr. Soc. Int. Conf. Durab., Engineering Integrity Society, Cambridge, 2021.10.1016/j.corsci.2022.110113 ↗
23. On the hot corrosion of nickel at 700 °C10.1007/s11085-015-9588-6 ↗
24. Type II hot corrosion: kinetics studies of CMSX-410.1007/s11085-013-9395-x ↗
25. The effect of near-surface plastic deformation on the hot corrosion and high temperature corrosion-fatigue response of a nickel-based superalloy10.1016/j.jallcom.2020.154889 ↗
26. H.L. Rosier, Role of the Environment and its Effects on the High Temperature Corrosion-Fatigue Life in Nickel Based Superalloys, n.d.
27. Modelling hot corrosion in industrial gas turbines10.3184/096034007X263587 ↗
28. Type II hot corrosion: behavior of CMSX-4 and IN738LC as a function of corrosion environment10.1002/maco.201307425 ↗
29. On the hot corrosion of nickel at 700 °C10.1007/s11085-015-9588-6 ↗
30. Talbot · 2007
31. Mechanism of Na2SO4 induced corrosion at 600–900 °C10.1149/1.2129375 ↗
32. The influence of KCl on biomass ash melting behaviour and high-temperature corrosion of low-alloy steel10.1016/j.energy.2019.116062 ↗
33. Influence of shot peening on high-temperature corrosion and corrosion-fatigue of nickel based superalloy 720Li10.1080/09603409.2016.1161945 ↗
34. Hot corrosion behavior of superalloy IN718 at 550 and 650°C10.1007/s11665-013-0532-0 ↗
35. Salt induced corrosion behaviour of superalloy IN71810.1016/j.matpr.2017.11.368 ↗
36. Metallurgical factors in stress corrosion cracking (SCC) and hydrogen-induced cracking (HIC)10.1007/s10008-009-0799-0 ↗
37. High-temperature corrosion of superalloys10.1080/02670836.1987.11782259 ↗
38. HOTPITS: The DARWIN approach to assessing risk of hot corrosion-induced fracture in gas turbine components10.1016/j.engfracmech.2020.106889 ↗
39. K.S. Chan, M.P. Enright, J.P. Moody, S.H.K. Fitch, Physics-based modelling tools for predicting type II hot corrosion in nickel-based superalloys, in: M. Hardy, E. Huron, U. Glatzel, B. Griffin, B. Lewis, C. Rae, V. Seetharaman, S. Tin (Eds.), Superalloys 2016 Proc. 13th Int. Symp. Superalloys, TMS, 2016: pp. 917–925.10.1002/9781119075646.ch98 ↗
40. USAF damage tolerant design handbook: guidelines for the analysis and design of damage tolerant aircraft structures
41. Cyclic oxidation behavior of ni- and fe-based superalloys in air and Na2SO4-25%NaCl molten salt environment at 800°C