Source abstract
Abstract
Abstract The aim of this research was to understand why the cracks in a stress corrosion cracking (SCC) colony developed in the pipeline steels exposed to near-neutral pH environments, can be either very dense or sparse, a key puzzling feature of SCC cracks found in the field. Results showed that crack population in a crack colony was increased with increasing the area of mill scale coverage and the length of time the damaged mill scale can be maintained on the steel surface. Various mechanical, chemical and physical conditions that can preserve or remove the mill scale from surface have been studied.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (68)
Show source-provided references
1. An overview of near-neutral pH stress corrosion cracking in pipelines and mitigation strategies for its initiation and growth10.5006/1967 ↗
2. CEPA · 2007
3. Baker · 2004
4. Determination of the enhancement or shielding interaction between two parallel cracks under fatigue loading10.3390/ma12081331 ↗
5. Initiation of stress-corrosion cracking on gas transmission piping
6. The role of residual stress in neutral pH stress corrosion cracking of pipeline steels - Part II: crack dormancy10.1016/j.actamat.2006.07.021 ↗
7. The role of residual stress in neutral pH stress corrosion cracking of pipeline steels. Part I: Pitting and cracking occurrence10.1016/j.actamat.2006.08.037 ↗
8. The influence of multiple welding repairs of pipelines in residual stress assessment related to stress corrosion cracking10.9734/BJAST/2015/14931 ↗
9. Cheng · 2013
10. Effect of elastic stress and alternating current on corrosion of X80 pipeline steel in simulated soil solution10.1016/j.engfailanal.2019.02.059 ↗
11. Stress corrosion of pipeline steel under disbonded coating in a SRB-containing environment10.1016/j.corsci.2019.06.026 ↗
12. EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte10.1016/j.corsci.2016.04.006 ↗
13. Stress corrosion crack initiation behavior for the X70 pipeline steel beneath a disbonded coating10.3724/SP.J.1037.2012.00254 ↗
14. Stress corrosion cracking of X80 pipeline steel in near-neutral pH environment under constant load tests with and without preload10.1016/S1005-0302(11)60184-9 ↗
15. Stress corrosion crack initiation in X-65 pipeline steel under disbonded coating with cathodic protection
16. Effects of different parameters on initiation and propagation of stress corrosion cracks in pipeline steels: a review10.3390/met9050590 ↗
17. Microstructure dependence of stress corrosion cracking initiation in X-65 pipeline steel exposed to a near-neutral pH soil environment10.5006/1.3287732 ↗
18. Effect of precyclic loading on stress-corrosion-cracking initiation in an X-65 pipeline steel exposed to near-neutral pH soil environment10.1007/s11661-003-0019-y ↗
19. Mechanism of MnS-mediated pit initiation and propagation in carbon steel in an anaerobic sulfidogenic media10.1016/j.corsci.2013.06.049 ↗
20. A review of iron carbonate (FeCO3) formation in the oil and gas industry10.1016/j.corsci.2018.07.021 ↗
21. Characterisation of rust surfaces formed on mild steel exposed to marine atmospheres using XRD and SEM/Micro-Raman techniques10.1016/j.corsci.2016.04.034 ↗
22. Effect of CO2 and R-ratio on near-neutral pH stress corrosion cracking initiation under a disbonded coating of pipeline steel10.1016/j.corsci.2011.03.017 ↗
23. Influence of inclusions on initiation of pitting corrosion and stress corrosion cracking of X70 steel in near-neutral pH environment10.1016/j.corsci.2018.11.007 ↗
24. Microscopic investigation of mill scale and its proposed effect on the variability of chloride-induced depassivation of carbon steel rebar10.1016/j.corsci.2010.11.025 ↗
25. Carbon steel corrosion under anaerobic–aerobic cycling conditions in near-neutral pH saline solutions. Part 2: corrosion mechanism10.1016/j.corsci.2011.07.008 ↗
26. Effect of alternating current on cathodic protection on pipelines10.1016/j.corsci.2012.09.028 ↗
27. Microbiologically influenced corrosion of X52 pipeline steel in thin layers of solution containing sulfate-reducing bacteria trapped under disbonded coating10.1016/j.corsci.2018.10.012 ↗
28. High temperature oxidation and its effects on microstructural changes of hot-rolled low carbon non-oriented electrical steels during air annealing10.1007/s11085-014-9518-z ↗
29. Surface decarburization of the hypo-eutectoid carbon steel C45 during annealing in steady air at temperatures t& AC110.3390/met8060425 ↗
30. Near-neutral pH corrosion of mill-scaled X-65 pipeline steel with paint primer
31. Ebnesajjad · 2014
32. Review of pipeline coating systems from an operator’s perspective10.1179/1743278215Y.0000000038 ↗
33. Bayliss · 2014
34. Study on anticorrosion properties of epoxy primers on steel
35. Electrochemical characterization in CO2 saturated environment of Zn-rich epoxy nanocoatings on API X52 pipeline grade steel substrate under flow conditions
36. Damage to paint coatings caused by electrolyte immersion as observed in situ by scanning electrochemical microscopy10.1016/j.corsci.2004.06.002 ↗
37. CEPA study on characterization of pipeline pressure fluctuations in terms relevant to stress corrosion cracking
38. Statistical analysis on underload-type pipeline spectra10.1061/(ASCE)PS.1949-1204.0000241 ↗
39. Stress corrosion cracking
40. Crack growth modeling and life prediction of pipeline steels exposed to near-neutral pH environments: dissolution crack growth and occurrence of crack dormancy in stage I10.1007/s11661-016-3951-3 ↗
41. Pit to crack transition in X-52 pipeline steel in near neutral pH environment: part 1 - Formation of blunt cracks from pits under cyclic loading10.1179/147842208X386304 ↗
42. A study on bacteria-assisted cracking of X80 pipeline steel in soil environment10.1080/1478422X.2018.1456633 ↗
43. Microbial corrosion of X52 pipeline steel under soil with varied thicknesses soaked with a simulated soil solution containing sulfate-reducing bacteria and the associated galvanic coupling effect10.1016/j.electacta.2018.02.002 ↗
44. Corrosion of the stressed pipe steel in carbonate–bicarbonate solution studied by scanning localized electrochemical impedance spectroscopy10.1016/j.electacta.2007.10.077 ↗
45. Mechanistic investigation of hydrogen-enhanced anodic dissolution of X-70 pipe steel and its implication on near-neutral pH SCC of pipelines10.1016/j.electacta.2007.07.015 ↗
46. Localized dissolution of millscale-covered pipeline steel surfaces10.5006/1.3287824 ↗
47. Shirband · 2016
48. Field assessment of FBE-coated pipelines and the implications for stress corrosion cracking
49. Mechanical and environmental influences on stress corrosion cracking of an X-70 pipeline steel in dilute near-neutral pH solutions10.5006/1.3278395 ↗
50. Crack initiation and early propagation of X70 steel in simulated near-neutral pH groundwater10.5006/1.3278297 ↗
51. Fracture behavior on SCC of API X52 pipeline steel under cathodic protection10.1557/PROC-1275-S3-P55 ↗
52. Effect of hydrogen-induced plasticity on the stress corrosion cracking of X70 pipeline steel in simulated soil environments10.1016/j.msea.2016.02.019 ↗
53. Fatigue crack initiation on low-carbon steel pipes in a near-neutral-pH environment under potential control conditions10.5006/1.3280786 ↗
54. Crack growth behavior of pipeline steel in near-neutral pH soil environments10.1007/s11661-007-9184-8 ↗
55. Correlating corrosion field data with experimental findings for the development of pipeline mitigation strategies
56. Precyclic-loading-induced stress corrosion cracking of pipeline steels in a near-neutral-pH soil environment10.5006/1.3277644 ↗
57. Li · 2018
58. Corrosion fatigue crack growth behavior of pipeline steel under underload-type variable amplitude loading schemes10.1016/j.actamat.2015.05.049 ↗
59. Stress corrosion cracking of X-70 pipeline steel in near neutral pH solution subjected to constant load and cyclic load testing10.1179/174327807X196843 ↗
60. Environmentally assisted cracking mechanism of pipeline steel in near-neutral pH groundwater10.1016/j.corsci.2010.02.020 ↗
61. Corrosion behavior of X65 pipeline steel: comparison of wet–dry cycle and full immersion10.1016/j.corsci.2018.01.007 ↗
62. Effects of dissolved hydrogen and elastic and plastic deformation on active dissolution of pipeline steel in anaerobic groundwater of near-neutral pH10.1016/j.actamat.2008.08.035 ↗
63. Developing cathodic protection based on disbondment geometry
64. The effect of microstructure on pit-to-crack transition and crack growth in an X-52 pipeline steel in near-neutral pH environment
65. Strain evolution around corrosion pits under fatigue loading10.1016/j.tafmec.2018.02.015 ↗
66. Characteristics of near-neutral-pH stress corrosion cracks in an X-65 pipeline10.5006/1.3279878 ↗
67. Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: the role of hydrogen10.1016/j.actamat.2009.08.047 ↗
68. The effect of ageing on cathodic protection shielding by fusion bonded epoxy coatings10.1016/j.porgcoat.2019.04.074 ↗