Probing dynamic and localised corrosion processes on buried steel under coating disbondments of various geometries
Source abstract
Abstract
Abstract A specially designed multi-electrode array has been utilised to visualise dynamic steel corrosion under disbonded coatings (CUD). The behaviour of CUD was found to be distinctively different under coating disbondments of different gap sizes and in saturated and non-saturated soils. In saturated soil, CUD behaved similarly as it usually does in electrolyte solutions, where CUD is mitigated by a cathodic protection induced high pH environment and a concentration polarisation mechanism. In non-saturated soil, CUD behaviour changed significantly with coating disbondment gap size. These observations have been explained by solution/soil distribution models proposed for coating disbondment of different geometries.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Concrete Corrosion and Durability · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Effects of cathodic potential on the local electrochemical environment under a disbonded coating10.1007/s10800-008-9711-3 ↗
2. Electrochemical behavior of steel A36 under disbonded coating in the presence of sulfate-reducing bacteria10.1016/j.matchemphys.2013.08.024 ↗
3. The effects of sulfate reducing bacteria on corrosion of carbon steel Q235 under simulated disbonded coating by using electrochemical impedance spectroscopy10.1016/j.corsci.2011.01.037 ↗
4. Effect of CO2 and R-ratio on near-neutral pH stress corrosion cracking initiation under a disbonded coating of pipeline steel10.1016/j.corsci.2011.03.017 ↗
5. EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte10.1016/j.corsci.2016.04.006 ↗
6. Cathodic protection of soil buried steel pipelines–a critical discussion of protection criteria and threshold values10.1002/maco.201608862 ↗
7. Electrochemical study of the corrosion rate of carbon steel in soil: evolution with time and determination of residual corrosion rates under cathodic protection10.1016/j.corsci.2011.10.031 ↗
8. Cathodic protection to mitigate external corrosion of underground steel pipe beneath disbonded coating10.5006/1.3293470 ↗
9. Current distribution and electrochemical environment in a cathodically protected crevice10.5006/1.3283983 ↗
10. Understanding the effects of applied cathodic protection potential and environmental conditions on the rate of cathodic disbondment of coatings by means of local electrochemical measurements on a multi-electrode array10.1016/j.porgcoat.2016.10.020 ↗
11. Factors affecting the cathodic disbonding of pipe coatings
12. Experimental studies of crevice corrosion for buried pipeline with disbonded coatings under cathodic protection10.1016/j.jlp.2014.02.007 ↗
13. Using pipeline coatings with cathodic protection protective coatings need to maintain integrity under operating environments and in the presence of CP
14. Chemical and electrochemical conditions on steel under disbonded coatings: the effect of applied potential, solution resistivity, crevice thickness and holiday size10.1016/S0010-938X(99)00136-5 ↗
15. Chemical and electrochemical conditions on steel under disbonded coatings: the effect of previously corroded surfaces and wet and dry cycles10.1016/S0010-938X(00)00103-7 ↗
16. A study on cathodic protection against crevice corrosion in dilute NaCl solutions10.1016/S0010-938X(01)00042-7 ↗
17. Electrochemical measurements using combination microelectrode in crevice simulating disbonded of pipeline coatings under cathodic protection10.1179/174327807X159934 ↗
18. Local environment under simulated disbonded coating on steel pipelines in soil solution10.1016/j.corsci.2008.01.004 ↗
19. Effect of cathodic protection on corrosion of pipeline steel under disbonded coating10.1016/j.corsci.2009.05.027 ↗
20. Stress corrosion cracking initiation under the disbonded coating of pipeline steel in near-neutral pH environment10.1016/j.corsci.2010.07.025 ↗
21. Stress corrosion of pipeline steel under occluded coating disbondment in a red soil environment10.1016/j.corsci.2015.01.001 ↗
22. Probing Potential and Solution pH under Disbonded Coating on Pipelines
23. Current distribution and electrochemical environment in a cathodically protected crevice10.5006/1.3283983 ↗
24. Electrochemical method for studying localized corrosion beneath disbonded coatings under cathodic protection10.1149/2.0301510jes ↗
25. Understanding the effectiveness of cathodic protection under disbonded coatings10.1016/j.electacta.2015.10.171 ↗
26. Modeling influence of gas/liquid/solid three-phase boundary zone on cathodic process of soil corrosion10.1016/j.electacta.2009.01.033 ↗
27. Influence of soil moisture on the corrosion processes of carbon steel in artificial soil: Active area and differential aeration cells10.1016/j.electacta.2016.07.163 ↗
28. Electrochemical monitoring of steel/soil interfaces during wet/dry cycles10.1149/2.0531712jes ↗
29. Varela · 2015
30. Visualising dynamic passivation and localised corrosion processes occurring on buried steel surfaces under the effect of anodic transients10.1016/j.elecom.2016.02.015 ↗
31. Mapping non-uniform corrosion using the wire beam electrode method. III. Water-line corrosion10.1016/S0010-938X(00)00192-X ↗
32. Comparison of water-line corrosion processes in natural and artificial seawater: the role of microbes10.1016/j.elecom.2017.05.003 ↗
33. Influence of soil moisture on the residual corrosion rates of buried carbon steel structures under cathodic protection10.1016/j.electacta.2015.07.097 ↗