NdYbZr2O7 thermal barrier coating resistant to degradation by volcanic ash and CMAS

Yang Wu, Dingyong He

Corrosion Science· Volume 209
Publisher page

Abstract

Environmental silicate debris such as sand, dust and volcanic ash is regarded as a major hazard for aviation safety. During the service process of gas turbines, these ingested silicate ashes can melt, impact and adhere to the thermal barrier coatings (TBCs) covered on the hot-section components, facilitating their structure and property instability. Here, we prepared a novel NdYbZr 2O 7 coating which is expected to mitigate this issue. We comparatively study the infiltration behavior of natural volcanic ash and synthetic CMAS within it at 1250 ºC and 1300 ºC. In the case of volcanic ash, the lower CaO content improves the Nd 3+ and Yb 3+ solubility, suggesting more NdYbZr 2O 7 coating has to be consumed to saturate the melt. The chemical reaction is delayed, and melt has more time to infiltrate. As a result, although volcanic ash has a relatively high viscosity, it exhibits a larger infiltration depth than CMAS. Apatite with a theoretical A 4 Ⅰ A 6 Ⅱ ( Si O 4 ) 6 X 2 structure is the main corrosion product for either volcanic ash or CMAS. The calculated A Ⅰ : A Ⅱ ratios are 0.14 and 0.30 respectively, which indicates that precipitating per unit apatite needs to consume more NdYbZr 2O 7 coating. In comparison with traditional YSZ coating, NdYbZr 2O 7 coating exhibits a better anti-corrosion performance by rapidly precipitating crystalline grains ( c-ZrO 2 and apatite) and further building dense reaction layer.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: High-Temperature Coating Behaviors · Nuclear materials and radiation effects · Advanced ceramic materials synthesis

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (50)

Show source-provided references
1. Thermal barrier coatings for gas-turbine engine applications10.1126/science.1068609 ↗
2. Thermal-barrier coatings for more efficient gas-turbine engines10.1557/mrs.2012.232 ↗
3. Overview on advanced thermal barrier coatings10.1016/j.surfcoat.2010.08.151 ↗
4. Thermophysical properties and cyclic lifetime of plasma sprayed SrAl12O110.1111/jace.17319 ↗
5. Role of environmental deposits and operating surface temperature in spallation of air plasma sprayed thermal barrier coatings10.1016/S0257-8972(96)02994-5 ↗
6. Degradation of thermal barrier coatings at very high temperatures10.1557/S0883769400048223 ↗
7. Jet engine coatings for resisting volcanic ash damage10.1002/adma.201004783 ↗
8. Outlet-boundary-condition influence for large eddy simulation of combustion instabilities in gas turbines10.2514/1.33739 ↗
9. Evaluation of the gas turbine inlet temperature with relation to the excess air10.4236/epe.2011.34063 ↗
10. A delamination mechanism for thermal barrier coatings subject to calcium-magnesium-alumino-silicate (CMAS) infiltration10.1016/j.actamat.2004.11.028 ↗
11. Thermochemical interaction of thermal barrier coatings with molten CaO-MgO-Al2O3-SiO2 (CMAS) deposits10.1111/j.1551-2916.2006.01209.x ↗
12. Environmental degradation of thermal-barrier coatings by molten deposits10.1557/mrs.2012.230 ↗
13. The tetragonal-monoclinic transformation in zirconia: lessons learnt and future trends10.1111/j.1551-2916.2009.03278.x ↗
14. Failure of plasma sprayed nano-zirconia-based thermal barrier coatings exposed to molten CaO-MgO-Al2O3-SiO2 deposits10.1111/jace.16498 ↗
15. Silicate deposit degradation of engineered coatings in gas turbines: Progress toward models and materials solutions10.1146/annurev-matsci-010917-105000 ↗
16. CaO-MgO-Al2O3-SiO2 corrosion behavior of air-plasma-sprayed (LaxYb1−x)2Zr2O710.1111/jace.16044 ↗
17. Zirconates as new materials for thermal barrier coatings10.1111/j.1151-2916.2000.tb01506.x ↗
18. Infiltration-inhibiting reaction of gadolinium zirconate thermal barrier coatings with CMAS melts10.1111/j.1551-2916.2007.02175.x ↗
19. Composition effects of thermal barrier coating ceramics on their interaction with molten Ca-Mg-Al-silicate (CMAS) glass10.1016/j.actamat.2012.06.053 ↗
20. Effects of Yb3+ doping on phase structure, thermal conductivity and fracture toughness of (Nd1−xYbx)2Zr2O710.1016/j.ceramint.2018.10.213 ↗
21. Novel thermal barrier coatings that are resistant to high-temperature attack by glassy deposits10.1016/j.actamat.2007.08.028 ↗
22. J.L. Smialek, The chemistry of Saudi Arabian sand: a deposition problem on helicopter turbine airfoils, 1991.
23. Glass transition temperatures of natural hydrous melts: a relationship with shear viscosity and implications for the welding process10.1016/j.jvolgeores.2004.10.015 ↗
24. The thermal stability of Eyjafjallajökull ash versus turbine ingestion test sands10.1186/2191-5040-3-4 ↗
25. Effects of the dissolution of thermal barrier coating materials on the viscosity of remelted volcanic ash10.2138/am-2020-7334 ↗
26. Volcanic ash melting under conditions relevant to ash turbine interactions10.1038/ncomms10795 ↗
27. The influence of thermal barrier coating dissolution on CMAS melt viscosities10.1016/j.jeurceramsoc.2020.11.037 ↗
28. Rheological and chemical interaction between volcanic ash and thermal barrier coatings10.1016/j.surfcoat.2021.127049 ↗
29. Dynamic spreading of re-melted volcanic ash bead on thermal barrier coatings10.1016/j.corsci.2020.108659 ↗
30. Resistance of pure and mixed rare earth silicates against calcium-magnesium-aluminosilicate (CMAS): a comparative study10.1111/jace.17328 ↗
31. Lanthanum hexaaluminate–a new materials for atmospheric plasma spraying of advanced thermal barrier coatings10.1361/105996301770349105 ↗
32. Viscosity–temperature relationship in the system Na2Si2O5-Na4Al2O510.1016/0016-7037(86)90409-6 ↗
33. Silicate ash-resistant novel thermal barrier coatings in gas turbines10.1016/j.corsci.2021.109929 ↗
34. Spreading of liquid drops over dry porous layers: complete wetting case10.1006/jcis.2002.8450 ↗
35. Wetting, infiltration and interaction behavior of CMAS towards columnar YSZ coatings deposited by plasma spray physical vapor10.1016/j.jeurceramsoc.2018.04.013 ↗
36. Equimolar YO1.5 and TaO2.5 co-doped ZrO2 as a potential CMAS-resistant material for thermal barrier coatings
37. Dissolution and diffusion kinetics of yttria-stabilized zirconia into molten silicates10.1016/j.jeurceramsoc.2020.10.056 ↗
38. Volcanic ash-induced decomposition of EB-PVD Gd2Zr2O7 thermal barrier coatings to Gd-oxyapatite, zircon, and Gd, Fe-zirconolite10.1111/jace.12251 ↗
39. Interaction and infiltration behavior of Eyjafjallajökull, Sakurajima volcanic ashes and a synthetic CMAS containing FeO with/in EB-PVD ZrO2-65 wt% Y2O3 coating at high temperature10.1016/j.actamat.2017.06.055 ↗
40. Equilibrium relationships between thermal barrier oxides and silicate melts10.1016/j.actamat.2016.08.077 ↗
41. D.R. Poirer, G.H. Geiger, Transport phenomena in materials processing, The Minerals, Metals and Materials Society, Warrendale, PA, 1994.
42. Wetting and spreading of molten volcanic ash in jet engines10.1021/acs.jpclett.7b00417 ↗
43. An estimation of the surface tension for silicate glass melts at 1400 ºC using statistical analysis
44. Rare-earth elements in silicate glass melt systems: Ⅰ. Effects of composition on the coordination environments of La, Gd, and Yb10.1016/0016-7037(89)90166-X ↗
45. Local structures of rare-earth ions in glasses: the ‘crystal-chemistry’ approach10.1016/0022-3093(93)91303-K ↗
46. Comparative study of EB-PVD gadolinium-zirconate and yttria-rich zirconia coatings performance against Fe-containing calcium-magnesium-aluminosilicate (CMAS) infiltration10.1016/j.corsci.2021.109660 ↗
47. Phase equilibria and crystal chemistry in the calcia-silica-yttria system10.1016/j.jeurceramsoc.2016.01.046 ↗
48. Effects of cation substitution and temperature on the interaction between thermal barrier oxides and molten CMAS10.1016/j.jeurceramsoc.2014.09.006 ↗
49. Ionic-conductivity of lanthanoid silicates, In10(SiO4)6O3 (LnLa, Nd, Sm, Gd, Dy, Y, Ho, Er and Yb)10.1039/jm9950501801 ↗
50. Thermal expansion and glass transition temperature of the rare-earth doped oxynitride glasses10.1016/j.jeurceramsoc.2003.10.012 ↗