High-temperature steam oxidation behavior of alumina-forming duplex FeNiCrAl and ferritic FeCrAl alloys at 800 °C to 1050 °C
Source abstract
Abstract
Abstract Two alumina-forming Fe-based alloys, duplex FeNiCrAl (alumina-forming duplex stainless steel, ADSS) and ferritic FeCrAl (APM) alloys, were oxidized in steam at 800 °C to 1050 °C for up to 72 h. Formation of spinel oxides on ADSS resulted in larger weight gain than APM, while the highest weight gain was observed at 900 °C. Outer γ- and/or θ-alumina and inner α-alumina were formed on APM, whereas dispersed spinel oxides as well as γ- and α-alumina on ADSS. Similar alumina formation kinetics was observed for both alloys, while transient alumina formation resulted in faster kinetics at 900 °C.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · High-Temperature Coating Behaviors · Fusion materials and technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Material selection for accident tolerant fuel cladding
2. Development and property evaluation of nuclear grade wrought FeCrAl fuel cladding for light water reactors10.1016/j.jnucmat.2015.10.019 ↗
3. Development of status of accident-tolerant fuel for light water reactors in Korea10.1016/j.net.2015.11.011 ↗
4. Current status of materials development of nuclear fuel cladding tubes for light water reactors10.1016/j.nucengdes.2017.02.031 ↗
5. A study of the oxidation of FeCrAl alloy in pressurized water and high-temperature steam environment10.1016/j.corsci.2015.02.027 ↗
6. Uniform corrosion of FeCrAl alloys in LWR coolant environments10.1016/j.jnucmat.2016.06.047 ↗
7. High temperature oxidation of fuel cladding candidate materials in steam-hydrogen environments10.1016/j.jnucmat.2013.05.047 ↗
8. Processability evaluation of a Mo-containing FeCrAl alloy for seamless thin-wall tube fabrication10.1016/j.msea.2017.06.036 ↗
9. Microstucture and texture evolution and ring-tensile properties of recrystallized FeCrAl ODS cladding tubes10.1016/j.msea.2019.138636 ↗
10. Development of alumina-forming duplex stainless steels as accident-tolerant fuel cladding materials for light water reactors10.1016/j.jnucmat.2018.04.027 ↗
11. Feasibility assessment of the alumina-forming duplex stainless steels as accident tolerant fuel cladding materials for light water reactors
12. Influence of composition and heating schedules on compatibility of FeCrAl alloys with high-temperature steam10.1016/j.jnucmat.2018.09.026 ↗
13. Effect of zirconium and oxygen on the oxidation of FeCrAl-ODS alloys under air and steam conditions up to 1500 °C10.1016/j.jnucmat.2019.01.041 ↗
14. Results of the QUENCH-LOCA experimental program at KIT10.1016/j.jnucmat.2020.152143 ↗
15. Pasamehmetoglu · 2018
16. Oxidation studies on the iron-chromium-aluminum heater alloys10.1149/1.2427333 ↗
17. TEM analysis of the growth of oxide scales at different temperature in FeAl grade 3 intermetallic alloy10.1179/mht.2005.065 ↗
18. Intermediate temperature corrosion behavior of Fe-12Cr-6Al-2Mo-0.2Si-0.03Y alloy (C26M) at 300-600 °C10.1016/j.corsci.2019.05.029 ↗
19. Oxidation characteristics of two FeCrAl alloys in air and steam from 800 °C to 1300 °C10.1007/s11837-018-2979-9 ↗
20. 400 °C aging embrittlement of FeCrAl alloys: microstructure and fracture behavior10.1016/j.msea.2018.11.084 ↗
21. Corrosion characteristics of Ni-base superalloys in high temperature steam with and without hydrogen10.1016/j.jnucmat.2013.04.023 ↗
22. Abnormal high growth rates of metastable aluminas on FeCrAl alloys10.1007/s11085-005-5715-0 ↗
23. Early stages of the oxidation of a FeCrAlRe alloy (Kanthal AF) at 900 °C: a detailed microstructural investigation10.1016/j.corsci.2008.05.019 ↗
24. Characterization of alumina scale formed on FeCrAl steel10.2478/amm-2014-0013 ↗
25. Oxidation behaviors of Fe-25Cr-20Ni-xNb austenite weld metals at 1100 °C in ambient air:role of elemental niobium10.1016/j.corsci.2019.108137 ↗
26. Oxidation behaviors of Fe-20Cr-25Ni-Nb austenitic stainless steel in high-temperature environment with small amount of water vapor10.1016/j.corsci.2018.09.016 ↗
27. Impurity and chemical diffusion of Al in BCC and FCC iron10.4028/www.scientific.net/DDF.95-98.709 ↗
28. Effect of microstructure on early oxidation of MCrAlY coatings10.1016/j.actamat.2018.08.018 ↗
29. Diffusion of cations in chromia layers grown on iron-base alloys10.1007/BF00665632 ↗
30. Metastable alumina polymorphs: crystal structures and transition sequences10.1111/j.1151-2916.1998.tb02581.x ↗
31. Rapid formation of α-Al2O3 scale on an Fe-Al alloy by pure-metal coatings at 900 °C10.1007/s11085-009-9184-8 ↗
32. The effect of grain size on the oxidation of NiCoCrAlY10.1016/j.apsusc.2014.02.056 ↗
33. On the competitive growth of alpha and transient aluminas during the first stages of thermal oxidation of FeCrAl alloys at intermediate temperatures10.1007/s11085-008-9126-x ↗