Initial oxidation mechanisms of stainless steel Sanicro 28 (35Fe27Cr31Ni) exposed to KCl, NaCl, and K2CO3 under dry and humid conditions at 535 °C
Source abstract
Abstract
Abstract The initial stage of oxidation reactions at the surface of the stainless steel Sanicro 28 (Fe31Cr27Ni) exposed to KCl, NaCl, or K2CO3 in flowing dry and humid air at 535 °C was investigated using chronoamperometry, SEM–EDX and XPS. All studied salts accelerated the corrosion process. Na+ resulted in a higher amount of Na2CrO4 and a thicker chromium–rich scale compared to K+. CO32− was involved in a reaction with iron only under humid conditions. The results show that humidity affects the corrosion mechanisms and it should thus be taken into account especially in the combustion of biomasses with high humidity.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Thermal and Kinetic Analysis · Thermochemical Biomass Conversion Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. Corrosion in biomass combustion: a materials selection analysis and its interaction with corrosion mechanisms and mitigation strategies10.1016/j.corsci.2013.07.013 ↗
2. A review on biomass as a fuel for boilers10.1016/j.rser.2011.02.015 ↗
3. Energy supply and consumption
4. Biomass combustion in fluidized bed boilers: potential problems and remedies10.1016/j.fuproc.2008.07.012 ↗
5. Implications of chlorine-associated corrosion on the operation of biomass-fired boilers10.1016/S0360-1285(00)00003-4 ↗
6. A comparative study on the high temperature corrosion of TP347H stainless steel, C22 alloy and laser-cladding C22 coating in molten chloride salts10.1016/j.corsci.2014.03.012 ↗
7. An ESEM in situ investigation of initial stages of the KCl induced high temperature corrosion of a Fe-2.25Cr-1Mo steel at 400 °C10.1016/j.corsci.2011.03.007 ↗
8. Corrosion of superheater steel materials under alkali salt deposits. Part 1: the effect of salt deposit composition and temperature10.1016/j.corsci.2008.01.010 ↗
9. Ash-related issues in fluidized-bed combustion of biomasses: recent research highlights10.1021/ef201169k ↗
10. Are NaCl and KCl equally corrosive on superheater materials of steam boilers?10.1016/j.fuel.2012.07.020 ↗
11. Alkali induced high temperature corrosion of stainless steel: the influence of NaCl, KCl and CaCl210.1007/s11085-012-9293-7 ↗
12. NaCl-induced accelerated oxidation of chromium10.1007/BF00659184 ↗
13. Corrosion resistance of Hastelloys in molten metal-chloride heat-transfer fluids for concentrating solar power applications10.1016/j.solener.2014.02.002 ↗
14. High temperature corrosion of superheater steels by KCl and K2CO3 under dry and wet conditions10.1016/j.fuproc.2012.05.020 ↗
15. The effects of KCl, NaCl and K2CO3 on the high-temperature oxidation onset of Sanicro 28 steel10.1007/s11085-016-9613-4 ↗
16. Comparison of potassium chloride and potassium carbonate with respect to their tendency to cause high temperature corrosion of stainless 304L steel10.1016/j.fuproc.2011.12.016 ↗
17. High temperature oxidation of metallic chromium exposed to eight different metal chlorides10.1016/j.corsci.2011.06.007 ↗
18. The effects of KCl, K2SO4 and K2CO3 on the high temperature corrosion of a 304-type austenitic stainless steel10.1007/s11085-011-9240-z ↗
19. The onset of potassium chloride induced high temperature corrosion: a novel experimental approach10.1007/s11085-014-9501-8 ↗
20. The influence of small amounts of KCl(s) on the initial stages of the corrosion of alloy sanicro 28 at 600 °C10.1007/s11085-008-9118-x ↗
21. KCl-induced high temperature corrosion of the austenitic Fe-Cr-Ni alloys 304L and Sanicro 28 at 600 °C10.1016/j.corsci.2005.05.018 ↗
22. Comparison of the sputter rates of oxide films relative to the sputter rate of SiO210.1116/1.3456123 ↗
23. Applicability of ToF-SIMS and stable oxygen isotopes in KCl-induced corrosion studies at high temperatures10.1016/j.corsci.2017.05.022 ↗
24. High temperature oxidation of the austenitic (35Fe27Cr31Ni) alloy sanicro 28 in O2+H2O environment10.1007/s11085-010-9199-1 ↗
25. In Situ ESEM investigation of KCl-Induced corrosion of a FeCrAl and a model FeNiCrAl alloy in lab air at 450 °C10.1149/2.0581514jes ↗
26. KCl induced corrosion of a 304-type austenitic stainless steel at 600 °C; the role of potassium10.1007/s11085-005-5704-3 ↗
27. Internal oxidation and phase transformations of multi-phase Fe-Ni-Al and Fe-Ni-Al-Cr alloys induced by KCl corrosion10.1016/j.corsci.2011.02.034 ↗
28. High temperature corrosion of pure Fe, Cr and Fe-Cr binary alloys in O2 containing trace KCl vapour at 750 °C10.1016/j.corsci.2009.05.014 ↗
29. Laboratory studies of potassium-halide-Induced high-temperature corrosion of superheater steels. Part 1: exposures in dry air10.1021/ef502245f ↗
30. Chlorine corrosion degradation of low alloyed ferritic steels in temperature range 450–550 °C10.1007/s11085-016-9617-0 ↗
31. KCl-induced high temperature corrosion of selected commercial alloys: part II: alumina and silica-formers10.1002/maco.201408215 ↗
32. Effect of water vapor on high-temperature corrosion under conditions mimicking biomass firing10.1021/acs.energyfuels.5b01045 ↗
33. Local reactions of KCl particles with iron, nickel and chromium surfaces10.1002/maco.200503903 ↗
34. The influence of small amounts of KCl(s) on the high temperature corrosion of a Fe-2.25Cr-1Mo steel at 400 and 500 °C10.1002/maco.201005942 ↗
35. Thermogravimetric studies of high temperature reactions between potassium salts and chromium10.1016/j.corsci.2012.02.013 ↗
36. High-temperature corrosion of superheater tube materials exposed to zinc salts10.1021/ef801012z ↗
37. Laboratory studies of potassium-halide-induced high-temperature corrosion of superheater steels. Part 2: exposures in wet air10.1021/acs.energyfuels.5b00204 ↗
38. Oxidation after breakdown of the chromium-rich scale on stainless steels at high temperature: internal oxidation10.1007/s11085-016-9610-7 ↗
39. Cicek · 2017