Fracture process zone and crack migration in pure mode II bonded composite joints: influence of pre-crack, stacking sequence, normalized crack-geometry
Source abstract
Abstract
This study examines how loading mode during pre-cracking, stacking sequence, and initial delamination ratio ( a 0 /L ) influence Mode II fracture characterization ( G IIC ) of bonded composite joints. 3-point End-Notched Flexural tests were performed on Unidirectional (UD) and Quasi-Isotropic (QI) carbon fibre/epoxy laminates bonded with AF163-2 K adhesive. Results reveal that fracture toughness and crack migration are governed by the morphology of the Fracture Process Zone (FPZ). In UD laminates, Mode I pre-cracking forms localized FPZ, requiring intense plastic deformation to transition into shear-dominated FPZ, capturing the upper-bound fracture resistance. Conversely, Mode II pre-cracked specimens exhibited diffused shear FPZ, resulting in lower G IIC . In QI laminates, diffused FPZ by Mode II pre-cracking delays crack migration into the weaker interlaminar, promoting growth within the bond-layer. However, localized FPZ from Mode I pre-cracks requires intense plastic deformation and shear cracks for the crack to grow in the bond-layer, triggering earlier migration. The crack migration was sensitive to the “ a 0 /L” ratio : a ratio of 0.4 induces independent interlaminar delamination, while 0.6 displays angular crack-migration. These mechanisms remained invariant when the span-length was scaled, provided the normalized crack length was preserved. This study demonstrates that G IIC is process-dependent, underscoring the need to characterize fractures based on FPZ evolution.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Numerical methods in engineering · Epoxy Resin Curing Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (65)
Show source-provided references
1. Pascoe JA. Fracture and Failure of Adhesives. Comprehensive Structural Integrity, Elsevier; 2023, p. V7-2-V7-23. https://doi.org/10.1016/B978-0-12-822944-6.00042-6.10.1016/B978-0-12-822944-6.00042-6 ↗
2. Review on adhesive joints and their application in hybrid composite structures10.1080/01694243.2018.1543528 ↗
3. Fracture behavior and strength enhancement of 3D-printed stepped-lap bonded joints using geometrically graded interfaces: experimental validation and damage modelling
4. On the relationship between disbond growth and the release of strain energy10.1016/j.engfracmech.2014.10.027 ↗
5. Methods for the prediction of fatigue delamination growth in composites and adhesive bonds - a critical review10.1016/j.engfracmech.2013.10.003 ↗
6. Fracture mechanics tests in adhesively bonded joints: a literature review10.1080/00218464.2013.859075 ↗
7. C das Neves PJ, M da Silva LF, Adams RD. Analysis of Mixed Adhesive Bonded Joints Part I: Theoretical Formulation. J Adhes Sci Technol 2009;23:1–34. DOI: 10.1163/156856108X336026.10.1163/156856108X336026 ↗
8. da Silva LFM, das Neves PJC, Adams RD, Spelt JK. Analytical models of adhesively bonded joints—Part I: Literature survey. Int J Adhes Adhes 2009;29:319–30. DOI: 10.1016/J.IJADHADH.2008.06.005.10.1016/j.ijadhadh.2008.06.005 ↗
9. Towards a consensus on mode II adhesive fracture testing: Experimental study10.1016/j.tafmec.2018.09.014 ↗
10. Extension of the crack equivalent method applied to mode II fracture of thermoplastic composites bonded joints using the ENF test10.1016/j.compstruct.2024.118687 ↗
11. Universal slope-based J-integral methods for characterization of the mode I, mode II and mixed mode I/II fracture behaviour of adhesively bonded interfaces10.1016/j.compscitech.2024.110611 ↗
12. Validity of LEFM to measure the Mode II and mixed Mode I/II fracture toughness of adhesively bonded CFRP10.1016/j.compositesa.2025.108777 ↗
13. Design of adhesively bonded lap joints with laminated CFRP adherends: Review, challenges and new opportunities for aerospace structures10.1016/j.compstruct.2021.113923 ↗
14. Test Method for Mixed Mode I-Mode II Interlaminar Fracture Toughness of Unidirectional Fiber Reinforced Polymer Matrix Composites 2022. DOI: 10.1520/D6671_D6671M-22.10.1520/D6671_D6671M-22 ↗
15. Fibre-reinforced plastic composites — Determination of the mode II fracture resistance for unidirectionally reinforced materials using the calibrated end-loaded split (C-ELS) test and an effective crack length approach ISO 15114.
16. The determination of the mode II adhesive fracture resistance, GIIC, of structural adhesive joints: an effective crack length approach10.1016/j.engfracmech.2004.08.007 ↗
17. Mode II fracture testing of composites: a new look at an old problem10.1016/j.engfracmech.2006.05.022 ↗
18. Iso 25217, · 2009
19. Failure behaviour of the adhesive layer and angle ply composite adherends in single lap joints: a numerical study10.1016/j.ijadhadh.2018.10.010 ↗
20. Failure behaviour of the single lap joints of angle-plied composites under three point bending tests10.1080/01694243.2019.1674101 ↗
21. On the fracture behaviour of aerospace-grade Polyether-ether-ketone composite-to-aluminium adhesive joints10.1016/j.coco.2022.101098 ↗
22. The influence of epoxy adhesive toughness on the strength of hybrid laminate adhesive joints10.1186/s40563-020-00132-5 ↗
23. Strength of CFRP joints reinforced with adhesive layers10.1016/j.ijadhadh.2019.102475 ↗
24. The joint strength of hybrid composite joints reinforced with different laminates materials10.1016/j.jajp.2022.100103 ↗
25. In situ optical observation of damage and failure process in adhesively bonded CFRP joints under mixed-mode loading10.1016/j.compstruct.2022.116453 ↗
26. Failure mechanism investigation of the adhesively bonded joints using Finite Element and Discrete Element methods10.1016/j.compstruct.2024.118574 ↗
27. On mixed-mode fracture of brittle orthotropic solids: a novel micromechanical damage model10.1016/j.engfracmech.2024.110628 ↗
28. Fernlund G, Spelt JK. Mixed-mode fracture adhesive characterization of joints. vol. 50. 1994.10.1016/0266-3538(94)90052-3 ↗
29. Uncovering the toughening mechanisms of bonded joints through tailored CFRP layup10.1016/j.compositesb.2023.110853 ↗
30. Reinforcement of CFRP single lap joints using metal laminates10.1016/j.compstruct.2019.111492 ↗
31. An experimental data reduction method for the mixed Mode Bending test based on the J-integral approach10.1016/j.compscitech.2015.05.021 ↗
32. On the validity of linear elastic fracture mechanics methods to measure the fracture toughness of adhesive joints10.1016/j.ijsolstr.2015.11.016 ↗
33. Birnie · Influence of R-ratio and fracture process zone development on mode II fatigue delamination · 2026
34. How differences in fracture process zone behavior prevent transferability of mixed-mode fracture toughness measurements in toughened adhesive CFRP joints10.1016/j.tafmec.2026.105617 ↗
35. Influence of ENF Specimen Geometry and Friction on the Mode II Delamination Resistance of Carbon/PEEK10.1177/089270579701000404 ↗
36. Comparison of test configurations for determination of mode II interlaminar fracture toughness results from international collaborative test programme10.1179/146580199101540600 ↗
37. Guidelines for selecting the dimensions of adhesively bonded end-loaded split joints: an approach based on numerical cohesive zone length10.1016/j.engfracmech.2018.05.019 ↗
38. Liu H (Hannah), Qi G, Renaud G, Li G, Li C (Lucy). Application of the effective crack length method to model delamination of unidirectional composite laminates under Mode II shear loadings. Composites Part C: Open Access 2023;12. DOI: 10.1016/j.jcomc.2023.100401.10.1016/j.jcomc.2023.100401 ↗
39. Mechanics Testing Methods for Polymers, Adhesives and Composites
40. Mode-II fracture toughness and crack propagation of pultruded carbon Fiber-Epoxy composites10.1016/j.engfracmech.2022.109042 ↗
41. The role of broken fibres on crack migration into 0° surface plies in adhesively bonded carbon fibre composite joints10.1016/j.compstruct.2021.114530 ↗
42. Influence of yarn bundle orientation and areal density on the interlaminar fracture toughness of ENF composites10.1016/j.engfracmech.2025.110806 ↗
43. Comparing Mode I, Mode II and Mixed-Mode I/II interlaminar fracture toughness of glass and carbon fiber reinforced polymer laminates with the same epoxy matrix system10.1016/j.engfracmech.2025.111009 ↗
44. On mode-I and mode-II interlaminar crack migration and R-curves in carbon/epoxy laminates with hybrid toughening via core-shell rubber particles and thermoplastic micro-fibre veils10.1016/j.compositesb.2022.109900 ↗
45. HexPLy 8552 Data Sheet. www.hexcel.com. Physical Properties. n.d.
46. 3M Scotch-Weld Structural Adhesive Film AF 163-2. n.d.
47. Pure mode II fracture characterization of composite bonded joints10.1016/j.ijsolstr.2008.12.001 ↗
48. On the Analysis and Design of the End Notched Flexure (ENF) Specimen for Mode II Testing10.1177/002199838602000606 ↗
49. Estimating crack tip position in adhesively bonded joints subjected to mode II quasi-static loading10.1111/ffe.14237 ↗
50. Wang Y, Williams JG. Corrections for Mode II fracture toughness specimens of composites materials. vol. 43. 1992.10.1016/0266-3538(92)90096-L ↗
51. Understanding fracture mode-mixity and its effects on bond performance10.1016/B978-0-323-91214-3.00015-6 ↗
52. Equivalent crack based analyses of ENF and ELS tests10.1016/j.engfracmech.2007.03.005 ↗
53. Equivalent crack based mode II fracture characterization of wood10.1016/j.engfracmech.2006.01.004 ↗
54. Experimental and numerical analysis of the effect of temperature on the mode I and mode II delamination of glass fiber woven composites10.1016/j.compositesb.2025.112131 ↗
55. Influence of 3D printing parameters on the fracture behavior of adhesive joints under mode II quasi-static loading: experimental and numerical insights10.1080/00218464.2025.2602654 ↗
56. Study of the mode i and mode II interlaminar behaviour of a carbon fabric reinforced thermoplastic10.1016/j.polymertesting.2011.12.009 ↗
57. Brunner AJ. Experimental aspects of Mode I and Mode II fracture toughness testing of ®bre-reinforced polymer-matrix composites. n.d.
58. A re-evaluation of mixed-mode cohesive zone modeling based on strength concepts instead of traction laws10.1016/j.engfracmech.2021.107704 ↗
59. Effect of notch length and pre-crack size on mode II fracture energy of brittle adhesives10.1016/j.engfracmech.2019.03.024 ↗
60. Experimental study on delamination migration in composite laminates10.1016/j.compositesa.2015.02.018 ↗
61. Wanthal S, Schaefer J, Justusson B, Hyder I, Engelstad S, Rose C. Paper Number: Session Topic: Verification & Validation of Progressive Damage/Failure Analysis for Stiffened Composite Structures Title: Verification and Validation Process for Progressive Damage and Failure Analysis Methods in the NASA Advanced Composites Consortium. n.d.
62. Propagation rate transients in J-controlled fatigue characterization of adhesives10.1016/j.ijfatigue.2024.108377 ↗
63. An updated review of adhesively bonded joints in composite materials10.1016/j.ijadhadh.2016.10.010 ↗
64. Review on damage and failure in Adhesively Bonded Composite Joints: a Microscopic Aspect10.3390/polym17030377 ↗
65. International Journal of Adhesion and Adhesives Strength improvement and failure analysis of dissimilar FDM printed single-lap joints with tailored interface geometry10.1016/j.ijadhadh.2024.103876 ↗