Peridynamics for fatigue life and residual strength prediction of composite laminates
Source abstract
Abstract
Abstract This study presents an application of peridynamics to predict damage initiation and growth in fiber reinforced composites under cyclic loading. The fatigue model utilizes standard S-N fatigue data for a lamina along with the critical energy release rate values. The fidelity of this model is established by simulating the tests conducted by the Air Force Research Laboratory under the Tech Scout Project. As part of this project, the AFRL tested open-hole composite laminates made of IM7/977-3 for three different layups under cyclic loads for strength and failure progression. The peridynamic predictions agree with the reduction in stiffness and strength as a function of number of load cycles. Also, the progressive damage predictions capture the general characteristics of the experimentally observed damage patterns.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Numerical methods in engineering · Geotechnical Engineering and Underground Structures · Geophysical Methods and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Talreja · 2012
2. Physical modelling of failure in composites10.1098/rsta.2015.0280 ↗
3. Fatigue damage modeling of fibre-reinforced composite materials: Review10.1115/1.1381395 ↗
4. Fatigue damage modeling of composite structures: the onera viewpoint
5. Reformulation of elasticity theory for discontinuities and long-range forces10.1016/S0022-5096(99)00029-0 ↗
6. A meshfree method based on the peridynamic model of solid mechanics10.1016/j.compstruc.2004.11.026 ↗
7. Askari E, Xu J, Silling SA. Peridynamic analysis of damage and failure in composites. In: 44th AIAA Aerospace Sciences Meeting and Exhibit, Reno, Nevada. Reston, VA; 2006.10.2514/6.2006-88 ↗
8. Xu J, Askari A, Weckner O, Razi H, Silling S.A.. Damage and failure analysis of composite laminates under biaxial loads. In: 48th AIAA Structures, Structural Dynamics, and Materials Conference, Honolulu, Hawaii; 2007.10.2514/6.2007-2315 ↗
9. Oterkus E, Barut A, Madenci E. Damage Growth Prediction from Loaded Composite Fastener Holesby Using Peridynamic Theory. In: 51th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference, Orlando, Florida; 2010.10.2514/6.2010-3026 ↗
10. Peridynamic Analysis of Impact Damage in Composite Laminates10.1061/(ASCE)0893-1321(2008)21:3(187) ↗
11. Hail impact characteristics of a hybrid material by advanced analysis techniques and testing10.1061/(ASCE)AS.1943-5525.0000034 ↗
12. Peridynamic model for dynamic fracture in unidirectional fiber-reinforced composites10.1016/j.cma.2012.01.016 ↗
13. Peridynamic analysis of fiber-reinforced composite materials10.2140/jomms.2012.7.45 ↗
14. Peridynamic theory for progressive damage prediction in center-cracked composite laminates10.1016/j.compstruct.2009.02.015 ↗
15. Combined finite element and peridynamic analyses for predicting failure in a stiffened composite curved panel with a central slot10.1016/j.compstruct.2011.07.019 ↗
16. Bond-based peridynamic modeling of composite laminates with arbitrary fiber orientation and stacking sequence10.1016/j.compstruct.2016.05.063 ↗
17. Silling SA, Askari A. Peridynamic model for fatigue cracking Tech. rep. no. SAND2014-18590. Albuquerque (NM, United States): Sandia National Laboratories (SNL-NM); 2014.
18. Oterkus E, Guven I, Madenci E. Fatigue failure model with peridynamic theory. In: IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm), Las Vegas, NV; June 2010.10.1109/ITHERM.2010.5501273 ↗
19. Validation of a peridynamic model for fatigue cracking10.1016/j.engfracmech.2016.05.008 ↗
20. GMRES: A generalized minimal residual algorithm for solving nonsymmetric linear systems10.1137/0907058 ↗
21. Hu YL, Madenci E, Phan N. Peridynamic Modeling of Defects in Composites. In: 56th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference; 2015.10.2514/6.2015-1875 ↗
22. Peridynamic modeling of delamination growth in composite laminates10.1016/j.compstruct.2015.05.079 ↗
23. Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus10.1016/0266-3538(96)00005-X ↗
24. Mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites under fatigue loading10.1016/S0266-3538(97)00021-3 ↗
25. A critical analysis of crack propagation laws10.1115/1.3656900 ↗
26. Engelstad SP. Assessment of Composite Damage Growth Tools for Aircraft Structure Part II. In: 57th AIAA/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, San Diego, California; 2016.10.2514/6.2016-0725 ↗
27. Fang E, Cui XD, Lua J. A Continuum Damage and Discrete Crack Approach for Fatigue Damage Prediction of Laminated Composites. In: 57th AIAA/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, San Diego, California; 2016.10.2514/6.2016-0727 ↗
28. Hoos K, Iarve EV. Braginsky M, et al. Progressive Failure Simulation in Laminated Composites under Fatigue Loading by Using Discrete Damage Modeling. In: 57th AIAA/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, San Diego, California; 2016.10.2514/6.2016-0726 ↗
29. Sertse H, Yu W. A Micromechanical Approach to Low Cycle Fatigue Analysis and Life Prediction of Composites. In: 57th AIAA/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, San Diego, California; 2016.10.2514/6.2016-0728 ↗
30. Yuan Z, Crouch R, Wollschlager J. Assessment of Multiscale DeSigner for Fatigue Life Prediction of Advanced Composite Aircraft Stuctures. In: 57th AIAA/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, San Diego, California; 2016.
31. Dalgarno RW, Robbins DH, Action JE, et al. Simulation of Fatigue Damage in Quasi-Isotropic Open-Hole Tension Coupon using the kinetic Theory of Fracture. In: 57th AIAA/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, San Diego, California; 2016.10.2514/6.2016-0723 ↗
32. Mixed-mode delamination growth in carbon-fibre composite laminates under cyclic loading10.1016/j.ijsolstr.2004.02.040 ↗
33. An experimental and numerical investigation into the damage mechanisms in notched composites10.1016/j.compositesa.2009.02.021 ↗