Effect of automated fiber placement (AFP) manufacturing signature on mechanical performance of composite structures
Source abstract
Abstract
Abstract A comprehensive and detailed experimental study of the influence of imperfections caused during Automated Fiber Placement (AFP) manufacturing is reported. Specimens with controlled gap and overlap imperfections of varying sizes and distribution were manufactured and tested. Pre-test microscopy inspection has been conducted to quantify the change in geometry due to compaction. Test results show significant knockdown in stiffness and strength due to gaps, specifically with larger gap sizes showing higher knockdown. Overlaps, on the other hand, may provide improvement in tensile properties and show negligible change in compressive properties. Digital image correction (DIC), in situ inspection with edge cameras and post-test microscopy analyses provide a detailed insight into the failure progression and modes.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Epoxy Resin Curing Processes · Electronic Packaging and Soldering Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (17)
Show source-provided references
1. The engineering aspects of automated prepreg layup: history, present and future10.1016/j.compositesb.2011.12.003 ↗
2. Astrom · 1997
3. Evans · 1998
4. Prediction of progressive failure in multidirectional composite laminated panels10.1016/j.ijsolstr.2006.08.010 ↗
5. Probabilistic defect analysis of fiber reinforced composites using kriging and support vector machine based surrogates10.1016/j.compstruct.2018.03.007 ↗
6. Experimental study of the effect of automated fiber placement induced defects on performance of composite laminates10.1016/j.compositesa.2011.01.007 ↗
7. Influence of embedded gap and overlap fiber placement defects on the microstructure and shear and compression properties of carbon-epoxy laminates10.1016/j.compositesa.2015.12.007 ↗
8. Understanding and predicting defect formation in automated fibre placement pre-preg laminates10.1016/j.compositesa.2017.08.008 ↗
9. Manufacturing characteristics of the continuous tow shearing method for manufacturing of variable angle tow composites10.1016/j.compositesa.2014.02.019 ↗
10. Effect of automated fiber placement (AFP) manufacturing signature on mechanical performance
11. Particle toughened interfaces enhance mechanical response of composites
12. Particle-toughened interlayers enhance mechanical response of composite laminates10.1016/j.compscitech.2019.107761 ↗
13. American Society for Testing and Materials D3039/D3039M-17. Standard test method for tensile properties of polymer matrix composite materials.
14. American Society for Testing and Materials D6641/D6641M-14. Standard test method for compressive properties of polymer matrix composite materials using a combined loading compression (CLC) test fixture.
15. Characterization of delamination onset and growth in a composite laminate
16. Transverse cracking and delamination in cross-ply glass-fiber and carbon-fiber reinforced plastic laminates: static and fatigue loading10.1115/1.1519557 ↗
17. Jones · 1999