Determination of J–R curves of thermoplastic starch composites containing crossed quasi-unidirectional flax fiber reinforcement

G. Romhány, T. Czigány, J. Karger-Kocsis

Composites Science and Technology· Volume 66· Issue 16
Publisher page

Abstract

Abstract Thermoplastic starch (MaterBi) composites reinforced with quasi-unidirectional flax fiber in cross-ply (CP) arrangement were produced by film stacking followed by hot pressing. These composites, containing various amount of flax, failed ductilely with pronounced crack growth. Therefore, to determine their fracture mechanical behaviour the J -integral resistance curve concept ( J – R ) was applied. As the crack growth could not be traced, attempt was made to use the located acoustic emission (AE) events for that purpose. It was established that weighting and smoothing the located cumulative AE amplitudes the crack path can be correctly reconstructed. This was proved by collating the AE results with those derived from infrared thermographic (IT) inspection. Knowing the crack propagation at each point of the force–displacement curves the J – R curves could be determined. Both critical or initiation J -integral and tearing modulus went through a minimum with increase of flax content in the composites.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Natural Fiber Reinforced Composites · Mechanical Engineering and Vibrations Research · Mechanical Behavior of Composites

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (17)

Show source-provided references
1. Friedrich · 1989
2. Joyce JA. Elastic–plastic fracture test method: the user’s experience, vol. 2. American Society for Testing and Materials, ASTM STP 1114, ASTM PCN 04-011140-30.
3. Grellmann · 2001
4. Williams · 2000
5. Moore · 2004
6. Determination of the damage zone size in textile fabric reinforced polypropylene composites by locating the acoustic emission
7. Microstructural aspects of fracture in polypropylene and in its filled chopped fiber and fiber mat reinforced composites10.1007/978-94-011-0523-1_4 ↗
8. A comparison of several analytical techniques for calculating J–R curves from load–displacement data and their relation to specimen geometry10.1016/0013-7944(89)90060-X ↗
9. Failure mode and damage zone development in a GM-TPP by acoustic emission and thermography10.1177/073168449401300901 ↗
10. Fracture and failure behaviour of partially consolidated discontinuous glass fiber mat-reinforced polypropylene composites (Azdel Superlite®)10.1002/1521-3900(200106)170:1<165::AID-MASY165>3.0.CO;2-R ↗
11. Comparative study of the fracture behaviour of flow-molded GMT-PP with random and chopped-fiber mats10.1016/S0266-3538(01)00160-9 ↗
12. Mode I fracture resistance of glass fiber mat-reinforced polypropylene composites at various degree of consolidation10.1016/S1359-835X(02)00045-3 ↗
13. Tensile fracture and failure behavior of thermoplastic starch with unidirectional and cross-ply flax fiber reinforcements10.1002/mame.200300040 ↗
14. Comparison of the fracture and failure behavior of polypropylene composites reinforced by long glass fibers and by glass mats10.1016/0266-3538(95)00068-2 ↗
15. Determination of fracture toughness of poly (ethylene terephthalate) film by essential work of fracture and J integral measurements10.1179/146580101322913257 ↗
16. Microstructural efficiency and fracture toughness of short fiber/thermoplastic matrix composites10.1016/0266-3538(85)90090-9 ↗
17. Fracture and fatigue of unfilled and reinforced polyamides and polyesters