Multiscale considerations for interface engineering to improve fracture toughness of ductile fiber/thermoset matrix composites

Robert C. Wetherhold, Mathieu Corjon, Pradipta Kumar Das

Composites Science and Technology· Volume 67· Issue 11-12
Publisher page

Abstract

Abstract Mechanical interlocking at both large-scale and fine-scale as well as continuous and intermittent chemical bonding were employed to engineer the friction during fiber pullout to improve toughness. Excellent toughening results have been achieved over a large range of typical fracture feature size in the large micro-/small meso-scale of 1–100 μm. Interphase engineered features for size scales below the microscale were smoothed over or subsumed during fracture. For mechanical interlocking at the large scale, the overall fiber shape is critical and there is little interfacial adhesion. For mechanical interlocking at the fine scale, a protruding “break-away” feature performs better than a concave, cavity-like feature. For chemical bonding, intermittent coating gives superior toughness. In all of the interface or interphase designs, it is found that there is an intermediate anchoring of the fiber to best utilize fiber plasticity to improve composite toughness.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Mechanical Behavior of Composites · Natural Fiber Reinforced Composites · Tribology and Wear Analysis

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (25)

Show source-provided references
1. Damage detection in CFRP by electrical conductivity mapping10.1016/S0266-3538(00)00178-0 ↗
2. Anon. “LNP∗ Stat-kon∗ Compounds: a guide to thermoplastic composites for electrostatic discharge protection,” GE Plastics, 2005. Available from: http://www.geplastics.com/gep/Plastics/global/jsp/Literature/LiteratureSearch.jsp.
3. Bhattacharya · 1986
4. The effect of metal fibers on the friction performance of automotive brake friction materials10.1016/S0043-1648(03)00445-9 ↗
5. Improvement in fracture toughness of an epoxy/copper composite through the use of various end-shaped fibers10.1016/S0921-5093(03)00558-6 ↗
6. Debond behavior of copper fibers in thermoset matrices and their effect on fracture toughening10.1163/156856103772150797 ↗
7. Fiber pullout behavior and impact toughness of short end-modified copper fibers in thermoset matrices10.1016/j.compositesa.2004.07.011 ↗
8. Wetherhold RC, Das PK. Oxidation of copper fiber surface to improve fracture toughness of cu/epoxy composite. Mater Sci Eng A 2007; in press.10.1016/j.msea.2007.01.055 ↗
9. Corjon M. Copper fiber-thermoset matrix interface design using a mesoscale spraying technique of a γ-aminopropyltriethoxysilane (γ-APS) coupling agent. MS Project, University at Buffalo, SUNY, 9/05.
10. Why interface testing by single-fibre methods can be misleading10.1016/S0266-3538(97)00036-5 ↗
11. Characterization and design of interphases in glass fiber reinforced polypropylene10.1002/pc.10194 ↗
12. Interphase characterization in polymer composites—monitoring of interphasial behavior in dependence on the mode of loading10.1163/156855400300185270 ↗
13. End-shaped copper fibers in an epoxy matrix—predicted versus actual fracture toughness10.1016/j.tafmec.2005.01.003 ↗
14. Bagwell RM. Multifunctional short shaped copper fiber/thermoset matrix composites with improved toughness and EMI shielding capabilities. PhD dissertation, University at Buffalo, SUNY, 2004.
15. Fiber pullout experiments with thermoplastics10.1002/pen.760311703 ↗
16. Shaped fibers to improve toughness of composite materials10.1016/S0266-3538(00)00217-7 ↗
17. Bagwell RM. Improved fracture toughness of brittle composites through the use of shaped ductile fibers. MS thesis, University at Buffalo, SUNY, 2002.
18. The toughness of brittle matrix composites reinforced with discontinuous fibers10.1016/0921-5093(92)90205-F ↗
19. Effect of deposition conditions for γ-aminopropyltriethoxy silane on adhesion between copper and epoxy resins10.1016/S0169-4332(96)00857-4 ↗
20. Parks JM. Copper fiber-thermoset matrix interface improvement using γ-aminopropyltriethoxysilane (γ-APS) coupling agent. MS project, University at Buffalo, SUNY, January 2005.
21. Effects of surface modification on the peel strength of copper based polymer/metal interfaces with characteristic morphologies10.1080/00218469308031280 ↗
22. Adhesion improvement of copper/epoxy joint10.1007/BF01119743 ↗
23. Analysis of failure of nanobelt-coated copper-based leadframe/epoxy-based moulding compound systems after pullout test10.1016/j.msea.2005.06.042 ↗
24. Microstructure, adhesion strength and failure path at a polymer/roughened metal interface10.1163/156856103762302005 ↗
25. Das PK. Oxidation treatment of copper surface for improved adhesion to epoxy matrix and improved fracture toughness of composite. MS project, University at Buffalo, SUNY, March 2006.