Quantitative analysis of interface crack propagation along a single carbon fiber under off-axis cyclic loading using nanoscopic three-dimensional imaging
Bibliographic record
Abstract
No abstract is available for this record. The assistant can identify its topic from the title, but cannot infer the study’s results.
Source: Not provided · Quality: missing
Research context
OpenAlex topics: Fiber-reinforced polymer composites · Mechanical Behavior of Composites · Smart Materials for Construction
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Characterisation and analysis of transverse crack-induced delamination in cross-ply composite laminates under fatigue loadings10.1016/j.ijfatigue.2019.105217 ↗
2. Progressive matrix cracking in carbon/epoxy cross-ply laminates under static and fatigue loading10.1016/j.ijfatigue.2018.10.008 ↗
3. Fatigue life prediction for transverse crack initiation of CFRP cross-ply and Quasi-isotropic laminates10.3390/ma11071182 ↗
4. Prediction of the crack density evolution in multidirectional laminates under fatigue loadings10.1016/j.compscitech.2017.03.013 ↗
5. Prediction of transverse crack multiplication of CFRP cross-ply laminates under tension-tension fatigue load10.1080/09243046.2022.2113700 ↗
6. Prediction of initiation of transverse cracks in cross-ply CFRP laminates under fatigue loading by fatigue properties of unidirectional CFRP in 90 ◦ direction10.1016/j.compositesa.2014.10.022 ↗
7. Micromechanisms in tension-compression fatigue of composite laminates containing transverse plies10.1016/S0266-3538(98)00061-X ↗
8. Improved wettability and interfacial adhesion in carbon fiber/epoxy composites via an aqueous epoxy sizing agent10.1016/j.compositesa.2018.06.026 ↗
9. Wettability of a single carbon fiber10.1021/acs.langmuir.6b02072 ↗
10. Micromechanical model of the single-fiber fragmentation test10.1016/j.mechmat.2016.10.002 ↗
11. Evaluation of interfacial strength between fiber and matrix based on cohesive zone modeling10.1016/j.compositesa.2016.06.024 ↗
12. Mechanical properties of fiber/matrix interface in polymer matrix composites10.1080/09243046.2014.915125 ↗
13. Quantitative evaluation of fatigue damage growth in CFRP laminates that changes due to applied stress level10.1016/j.ijfatigue.2010.12.017 ↗
14. Nanoscopic origin of cracks in carbon fiber-reinforced plastic composites10.1038/s41598-019-55904-2 ↗
15. Nanoscale in-situ observations of crack initiation and propagation in carbon fiber/epoxy composites using synchrotron radiation X-ray computed tomography10.1016/j.compscitech.2020.108244 ↗
16. X-ray nanoimaging of a transversely embedded carbon fiber in epoxy matrix under static and cyclic loads10.1038/s41598-022-12724-1 ↗
17. Decreasing propagation rate of interfacial debonding between a single carbon fiber and epoxy matrix under cyclic loading10.1016/j.compscitech.2024.110900 ↗
18. In situ analysis of three-dimensional microcrack propagation in cross-ply laminates using synchrotron radiation X-ray computed tomography10.1016/j.compscitech.2024.110918 ↗
19. Influence of polymer properties and fiber–matrix interface on the kink band initiation in compression-compression fatigue loading of continuous fiber reinforced plastics10.1016/j.ijfatigue.2025.109191 ↗
20. Influence of irradiation with synchrotron radiation X-ray on Nano-Scale CT for carbon fibers and epoxy matrix10.1016/j.compositesa.2025.109060 ↗
21. Fracture toughness of CFRP with modified epoxy resin matrices10.1016/0266-3538(92)90099-O ↗
22. Nanoscale debonding of carbon fiber/matrix interface in humid environments and silane coupling agent modification effects: insights from molecular dynamics simulations10.1016/j.compstruct.2025.119519 ↗
23. Stress-intensity factor equations for cracks in three-dimensional finite bodies subjected to tension and bending loads
24. Beevers · 1980
25. Interface crack onset at a circular cylindrical inclusion under a remote transverse tension. Application of a coupled stress and energy criterion10.1016/j.ijsolstr.2008.10.036 ↗
26. Determining the interphase thickness and properties in carbon fiber reinforced fast and conventional curing epoxy matrix composites using peak force atomic force microscopy10.1016/j.compscitech.2019.107877 ↗
27. The short crack problem10.1111/j.1460-2695.1982.tb01250.x ↗