On experimental investigation of failure process of woven-fabric composites
Source abstract
Abstract
In this paper an experimental investigation is performed to describe the fracture behaviour and failure mechanisms of woven fabrics composites, under static loading, using a compact tension test (CT). We studied the development of the different damage phases using the digital image correlation and the compliance method. The crack length was estimated at in the front of the notch tip. The approach of the effective crack length via the compliance procedure was compared to the measures of the damage in the epoxy/glass fiber composite obtained by the Digital Image Correlation (DIC).
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Textile materials and evaluations · Optical measurement and interference techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Experimental study of fracture toughness and energy in composite materials10.1007/BF02256042 ↗
2. Vibration damping for crack detection in composite laminates10.1016/j.compositesa.2004.01.003 ↗
3. Study of fracture toughness evaluation of FRP10.1007/BF00543818 ↗
4. Damage and fracture prediction of plastic-bonded explosive by digital image correlation processing10.1016/j.optlaseng.2004.09.003 ↗
5. Scaling global fracture behavior of structures-sized laminated composites10.1023/A:1023351115322 ↗
6. An experimental analysis of fracture mechanisms of short glass fibre reinforced polyamide 6,6 (SGFR-PA66)10.1016/j.compscitech.2009.07.003 ↗
7. Benmedekhene S. Etude Phénoménologique du Comportement à l’Impact des Matériaux Composites. Thèse de doctorat UTC, Université de Compiègne; 1996 [Chapitre 2].
8. Fracture toughness of the tensile and compressive fibre failure modes in laminated composites10.1016/j.compscitech.2005.12.023 ↗
9. ASTM. Standard test method for plane-strain fracture toughness of metallic materials. ASTM standard E399-90; 1993.
10. Intralaminar fracture toughness of a cross-ply laminate and its constituent sub-laminates10.1016/S0266-3538(01)00011-2 ↗
11. Experimental study of damage propagation in over-height compact tension tests10.1016/j.compositesa.2009.08.017 ↗
12. The interlaminar and intralaminar fracture toughness of carbon-fibre/polymer composites: the effect of temperature10.1016/S0266-3538(97)00047-X ↗
13. Wide range stress intensity factor expressions of ASTM E 399 standard fracture toughness specimens10.1007/BF00032844 ↗
14. Irwin GR. Analytical aspects of crack stress field problems. TAM report no. 213, University of Illinois, Urbana, IL; 196.
15. Mathematical theories of brittle fracture
16. Thermoelastique determination of stress intensity factors in orthotropic composites using the J-integral10.1016/S0013-7944(96)00062-8 ↗
17. Mechanisms of crack propagation in dry plaster10.1016/S0955-2219(03)00094-3 ↗
18. Wood: a quasibrittle material R-curve behavior and peak load evaluation10.1007/s10704-004-7513-0 ↗
19. On the fracture toughness of ceramic matrix composites10.1016/S0921-5093(98)00605-4 ↗
20. Fracture energy measurements of 2-D carbon/carbon composites10.1016/S0955-2219(97)00100-3 ↗
21. Tada · 1973
22. Fracture and tensile properties of polyvinyl alcohol fiber reinforced cementitous composites10.1007/s11595-006-1007-z ↗
23. The fracture behaviour and toughness of woven fax fiber reinforced epoxy composites10.1016/j.compositesa.2008.07.008 ↗
24. Application of photon emission technique to the determination of micro-fracture behavior in glass fiber-reinforced epoxy matrix composite10.1016/S1468-6996(01)00014-6 ↗
25. Behavior of woven composites containing various cracks geometry10.1177/0021998303037001679 ↗
26. Absorption mechanisms during dynamic fracturing of fibre-reinforced composites10.1007/BF00353170 ↗
27. Crack resistance curves of GLARE laminates by elastic compliance10.1016/j.engfracmech.2006.05.008 ↗
28. Notch Strength and fracture behavior of 2-D carbon–carbon composites10.1111/j.1151-2916.1993.tb05318.x ↗
29. Fracture toughness evaluation based on tension-softening model and its application to hydraulic fracturing10.1007/s00024-006-0066-6 ↗
30. Jortner J. Effects of crimp angle on the tensile strength of a carbon–carbon laminate. In: Proc symposium on high temperature composites. Lancaster; 1989. p. 243–51.
31. Impact and delamination failure of woven-fabric composites10.1016/S0266-3538(99)00166-9 ↗