Energy dissipation during delamination in composite materials – An experimental assessment of the cohesive law and the stress-strain field ahead of a crack tip
Source abstract
Abstract
This paper presents detailed experimental information on mode-II delamination development in fibre/epoxy composite materials and provides observations about the process zone in the vicinity of the crack tip. It is shown that the energy dissipated in delamination propagation is spent on two ways (i) creating new fracture surfaces (delamination) and (ii) nonlinear shear deformation in the composite plies adjacent to the delaminating interface. Therefore, the nonlinear process zone is not restricted to the resin-rich interface between the layers, but also extends into the fibre/epoxy composite layers. This is different from the conventional assumption in modelling delamination using cohesive elements where the fibre/epoxy layers are fully linear-elastic and the process zone is lumped at the plane of fracture. Based on the accurately measured displacement field around the crack tip, the experimental traction-separation relation at the interface is found to be trapezoidal which is again different from the conventional bilinear cohesive law.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Fatigue and fracture mechanics · Structural Behavior of Reinforced Concrete
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Experimental and analytical studies on the onset of delamination in laminated composites10.1177/002199838401800106 ↗
2. Quadratic stress criterion for initiation of delamination10.1177/002199838802201205 ↗
3. Characterization of delamination onset and growth in a composite laminate
4. Shear driven delamination propagation in two dimensions10.1016/S1359-835X(97)00015-8 ↗
5. Damage analysis of pseudo-ductile thin-ply UD hybrid composites - a new analytical method10.1016/j.compositesa.2014.11.006 ↗
6. Modelling discrete failures in composites with interface elements10.1016/j.compositesa.2010.02.011 ↗
7. Delamination of laminates governed by free edge interlaminar stresses using interface element10.4028/www.scientific.net/KEM.385-387.821 ↗
8. Free edge delamination in carbon-epoxy laminates: a novel numerical/experimental approach10.1016/0263-8223(94)90118-X ↗
9. Numerical modeling of diffuse transverse cracks and induced delamination using cohesive elements10.1177/0954406212460974 ↗
10. Homogenization of diffuse delamination in composite laminates10.1016/j.compstruct.2012.12.022 ↗
11. Experimental and numerical study of oblique transverse cracking in cross-ply laminates under tension10.1016/j.compositesa.2014.08.004 ↗
12. Numerical modelling of the damage modes in UD thin carbon/glass hybrid laminates10.1016/j.compscitech.2014.01.013 ↗
13. Effects of bondline thickness on Mode-II interfacial laws of bonded laminated composite plate10.1007/s10704-010-9571-9 ↗
14. Elastic-plastic mode-II fracture of adhesive joints10.1016/S0020-7683(00)00221-3 ↗
15. Determination of cohesive laws of composite bonded joints under mode II loading10.1016/j.compositesb.2013.04.007 ↗
16. Cohesive law and notch sensitivity of adhesive joints10.1016/S1359-6454(01)00404-9 ↗
17. The stress-elongation relation for an adhesive layer loaded in peel using equilibrium of energetic forces10.1016/j.ijsolstr.2003.09.039 ↗
18. A straightforward method to obtain the cohesive laws of bonded joints under mode I loading10.1016/j.ijadhadh.2012.07.008 ↗
19. An experimental analysis of the fracture behavior of composite bonded joints in terms of cohesive laws10.1016/j.compositesa.2016.07.004 ↗
20. Determination of mixed mode cohesive laws10.1016/j.engfracmech.2006.04.006 ↗
21. Bridging tractions in mode I delamination: measurements and simulations10.1016/j.compscitech.2007.08.024 ↗
22. Crack equivalent concept applied to the fracture characterization of bonded joints under pure mode I loading10.1016/j.compscitech.2008.04.003 ↗
23. The cohesive zone model: advantages, limitations and challenges10.1016/S0013-7944(01)00083-2 ↗
24. On the increase in fracture energy with thickness in delamination of unidirectional glass fibre-epoxy with cut central plies10.1177/073168449201100802 ↗
25. An experimental and analytical study of delamination of unidirectional specimens with cut central plies10.1177/073168449401300804 ↗
26. A numerical investigation into the size effect in the transverse crack tension test for mode II delamination10.1016/j.compositesa.2013.07.013 ↗
27. Novel experimental procedure and determination of full displacement fields of delaminating composite layer interfaces for evaluation of the mode II cohesive law10.1016/j.engfracmech.2015.06.060 ↗
28. Demonstration of pseudo-ductility in high performance glass-epoxy composites by hybridisation with thin-ply carbon prepreg10.1016/j.compositesa.2013.04.006 ↗
29. Demonstration of pseudo-ductility in unidirectional hybrid composites made of discontinuous carbon/epoxy and continuous glass/epoxy plies10.1016/j.compositesa.2015.01.019 ↗
30. Pseudo-ductility and damage suppression in thin ply CFRP angle-ply laminates10.1016/j.compositesa.2014.11.004 ↗
31. Extracting interlaminar cohesive laws from displacement field measurements