Influence of hole eccentricity on failure progression in a double shear bolted joint (DSBJ)
Source abstract
Abstract
Abstract Experimental results on the influence of bolt hole to edge eccentricity for Double Shear Bolted Joints (DSBJ) used to attach fiber reinforced composite laminates are presented. Four different eccentricities of DSBJs were examined and microCT imaging conducted at different stages of the loading history are presented. The macroscopic load-hole elongation results along with the microCT images exhibit a distinct progression of failure which dictate not only the bearing load but also the ultimate load of the joint. The experimental procedure, microCT images and failure progression mechanisms are reported in this paper. The results can serve to develop a mechanism based model of DSBJ failure progression.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Optical measurement and interference techniques · Mechanical stress and fatigue analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (14)
Show source-provided references
1. Bolted joints in graphite-epoxy composites
2. The strength of bolted joints in multi-directional cfrp laminates10.1016/0010-4361(77)90027-1 ↗
3. Bolt-bearing fatigue of a graphite/epoxy laminate
4. Bolt clampup relaxation in a graphite/epoxy laminate
5. The effect of bolt clamping force on the fracture strength and the stress intensity factor of a plate containing a fastener hole with edge cracks10.1016/j.engfailanal.2008.03.002 ↗
6. Bearing strength and failure behavior of bolted composite joints (part i: experimental investigation)10.1016/j.compscitech.2005.02.011 ↗
7. P. Davidson, A. M. Waas, Mechanics of Kinking in Fiber-reinforced Composites under Compressive Loading, Mathematics and Mechanics of SolidsarXiv:http://mms.sagepub.com/content/early/2014/05/29/1081286514535422.full.pdf+html, https://doi.org/10.1177/1081286514535422. URL http://mms.sagepub.com/content/early/2014/05/29/1081286514535422.abstract.
8. Interaction between kinking and splitting in the compressive failure of unidirectional fiber reinforced laminated composites10.1016/j.compstruct.2012.11.005 ↗
9. Compressive response and failure of fiber reinforced unidirectional composites10.1023/A:1018779307931 ↗
10. Multi scale progressive damage and failure analysis of bolted joints
11. Progressive damage and failure analysis of single lap shear and double lap shear bolted joints10.1016/j.compositesa.2018.07.018 ↗
12. Open hole and filled hole progressive damage and failure analysis of composite laminates with a countersunk hole10.1016/j.compstruct.2018.06.120 ↗
13. Intra-inter crack band model (i2cbm) for progressive damage and failure analysis of joints
14. Failure analysis of composite multi-bolt joints using intra-inter crack band model (i2cbm)