New Glaze Composition for Chemical Strengthening of Bone China
Source abstract
Abstract
In order to improve the hardness of commercial bone china, we suggested a chemical strengthening process and new glaze for its process. New glaze contained about two times more Na 2 O and Al 2 O 3 and had a higher transition temperature than that of commercial frit. Chemical strengthening enhanced the hardness of the new glaze-coated bone china by over 30% compared to that of commercial product. The change of glaze composition influenced potassium ion diffusion distance and depth of strengthened layer during chemical treatment. After chemical strengthening of new glaze-coated bone china, the residual compressive stress inside the glaze was measured and found to be greater than 160 MPa.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Recycling and utilization of industrial and municipal waste in materials production · Pigment Synthesis and Properties · Bone Tissue Engineering Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Ramsay · 2004 · 161
2. 10.1179/bct.2001.100.6.25610.1179/bct.2001.100.6.256 ↗
3. 10.1016/j.jeurceramsoc.2006.01.01210.1016/j.jeurceramsoc.2006.01.012 ↗
4. 10.1016/j.jeurceramsoc.2003.07.00310.1016/j.jeurceramsoc.2003.07.003 ↗
5. 10.1016/j.jeurceramsoc.2008.04.00910.1016/j.jeurceramsoc.2008.04.009 ↗
6. 10.1016/j.ceramint.2012.02.08110.1016/j.ceramint.2012.02.081 ↗
7. 10.1016/j.jeurceramsoc.2006.05.01110.1016/j.jeurceramsoc.2006.05.011 ↗
8. 10.1016/j.jeurceramsoc.2004.10.01910.1016/j.jeurceramsoc.2004.10.019 ↗
9. Spinosa · 1993
10. Tokunaga · 1992
11. Knapp · 1994
12. 10.1016/S0955-2219(01)00420-410.1016/S0955-2219(01)00420-4 ↗
13. 10.1016/j.dental.2008.12.00910.1016/j.dental.2008.12.009 ↗
14. 10.1177/0022034592071005010110.1177/00220345920710050101 ↗
15. 10.4191/kcers.2014.51.5.48710.4191/kcers.2014.51.5.487 ↗
16. 10.1016/j.jeurceramsoc.2015.10.02210.1016/j.jeurceramsoc.2015.10.022 ↗
17. 10.4191/kcers.2015.52.6.50810.4191/kcers.2015.52.6.508 ↗
18. Nagashima · 2015 · 3
19. Inaba · 2008 · 46
20. Nagashima · 2011 · 5
21. Volf · 1984 · 300
22. Scholze · 1991 · 272
23. Maeng · 2014 · 40
24. 10.1111/j.1151-2916.1964.tb14399.x10.1111/j.1151-2916.1964.tb14399.x ↗
25. 10.1016/j.mseb.2007.11.02910.1016/j.mseb.2007.11.029 ↗
26. 10.1111/j.1151-2916.1955.tb14545.x10.1111/j.1151-2916.1955.tb14545.x ↗
27. 10.1007/s00410-010-0513-310.1007/s00410-010-0513-3 ↗
28. 10.1016/j.jeurceramsoc.2012.11.00810.1016/j.jeurceramsoc.2012.11.008 ↗
29. Ahmed · 2002 · 47
30. 10.1007/s10973-016-5462-210.1007/s10973-016-5462-2 ↗