Application of an improved testing device for the study of alumina dissolution in silicate slag
Source abstract
Abstract
This study entailed a dissolution study of alumina fine ceramics in a CaO–Al2O3–SiO2–MgO silicate slag system with a CaO/SiO2 weight ratio of 0.65. Finger-test experiments with several corrosion steps were carried out in a contemporary continuous wear testing device at 1450, 1500, and 1550 °C with 200 rpm. The corroded sample profiles were measured using a high-resolution laser scanner, and the processed measurement data were used to extract the dissolution parameters (i.e. corroded volume, surface area, mean radius, tip radius and immersion length). The diffusivity determination method using Sherwood relations was developed for the dynamic finger-test setup. The diffusivities for all corrosion steps were determined from these dissolution parameters, and those obtained from the Sherwood relations were compared with the ones received by a simulation approach that includes deviations from the cylindrical shape. The results obtained using Sherwood relations are sufficiently accurate in several cases.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Metallurgical Processes and Thermodynamics · Materials Engineering and Processing · Concrete and Cement Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (60)
Show source-provided references
1. Melt corrosion of oxide and oxide–carbon refractories10.1179/095066099101528234 ↗
2. Refractory corrosion by dissolution in slags – challenges and trends of present fundamental research
3. Dynamic and static corrosion of alpha-alumina bonded refractory in contact with molten soda–lime–silica (SLS) glass10.1016/j.ceramint.2018.09.235 ↗
4. Jansson · 2008
5. Comparative evaluation investigation of slag corrosion on Al2O3 and MgO-Al2O3 refractories via experiments and thermodynamic simulations10.1016/j.ceramint.2017.09.034 ↗
6. Investigation of slag-refractory interactions for the Ruhrstahl Heraeus (RH) vacuum degassing process in steelmaking10.1016/j.jeurceramsoc.2012.01.005 ↗
7. Corrosion tests for refractory materials intended for the steel industry – a review10.13168/cs.2020.0017 ↗
8. In situ observation of the dissolution phenomena of SiC particle in CaO–SiO2–MnO slag10.1016/j.jeurceramsoc.2010.07.020 ↗
9. In situ observation of the direct and indirect dissolution of MgO particles in CaO-Al2O3-SiO2-based slags10.1016/j.jeurceramsoc.2006.05.107 ↗
10. Corrosion mechanisms of zirconia/carbon based refractory materials by slag in presence of steel
11. Dynamic corrosion of Al2O3–ZrO2–SiO2 and Cr2O3-containing refractories by molten frits. Part I: Macroscopic analysis10.1016/j.jeurceramsoc.2010.11.023 ↗
12. S. Jansson, V. Brabie, L. Bohlin, Corrosion mechanism and kinetic behaviour of refractory materials in contact with CaO–Al2O3–MgO −SiO2 slags, in: Proceedings of the Int. Conf. on Molten Slags Fluxes and Salts VII, 2004, pp. 341–8.
13. Basic slag attack of spinel-containing refractory castables10.1016/j.ceramint.2011.02.007 ↗
14. Corrosion of MgO-MgAl2O4 spinel refractory bricks by calcium aluminosilicate slag10.1111/j.1151-2916.1997.tb02852.x ↗
15. Effects of additives and temperature on the dissolution rate and diffusivity of lime in Al2O3-CaO-SiO2 based slags10.1007/s11663-006-0059-y ↗
16. Dissolution of MgO based refractories in CaO-Al2O3-MgO-SiO2 slag10.1016/j.jeurceramsoc.2017.09.030 ↗
17. Experimental design for the mechanism study of lime dissolution in liquid slag10.1002/srin.201100258 ↗
18. Dissolution in ceramic systems: I, Molecular diffusion, natural convection, and forced convection studies of sapphire dissolution in calcium aluminum silicate10.1111/j.1151-2916.1964.tb14638.x ↗
19. Quantifying of a dynamic refractory wear test setup for MgO-C products10.1007/s00501-012-0028-5 ↗
20. Dynamic slag/refractory interaction of lightweight Al2O3–MgO castable for refining ladle10.1016/j.ceramint.2015.03.026 ↗
21. Degradation mechanisms of magnesia-chromite refractories by high-alumina stainless steel slags under vacuum conditions10.1016/j.jeurceramsoc.2005.12.025 ↗
22. Effect of carbon content of ferromanganese alloy on corrosion behaviour of MgO–C refractory10.1179/1743281212Y.0000000098 ↗
23. Dissolution behavior of zirconia-refractories during continuous casting of steel10.1007/BF03027711 ↗
24. Corrosion behavior of MgO–C refractory in ferromanganese slags10.2355/isijinternational.52.62 ↗
25. Corrosion mechanism and kinetic behaviour of MgO–C refractory material in contact with CaO-Al2O3-SiO2-MgO slag10.1111/j.1600-0692.2005.00748.x ↗
26. Corrosion-erosion behavior of MgAl2O4 spinel refractory in contact with high MnO slag10.1016/j.ceramint.2017.08.034 ↗
27. Dissolution behavior of a novel Al2O3-SiC-SiO2-C composite refractory in blast furnace slag10.1016/j.ceramint.2017.02.138 ↗
28. Corrosion behavior of alumina-carbon composite brick in typical blast furnace slag and iron10.1016/j.ceramint.2018.07.265 ↗
29. Improvement of the corrosion resistance of alumina-chromia ceramic materials in molten slag10.1016/S0955-2219(03)00023-2 ↗
30. Dissolution of alumina in mold fluxes10.1007/s11663-997-0094-3 ↗
31. Degradation of MgO refractory in CaO-SiO2-MgO-FeOx and CaO-SiO2-Al2O3-MgO-FeOx slags under forced convection10.1007/s11663-005-0036-x ↗
32. Corrosion mechanisms of low porosity ZrO2 based materials during near net shape steel casting10.1016/S0955-2219(99)00149-1 ↗
33. Effect of ZnO level in secondary copper smelting slags on slag/magnesia-chromite refractory interactions10.1016/j.jeurceramsoc.2016.02.004 ↗
34. Interaction of Al2O3-rich slag with MgO-C refractories during VOD refining-MgO and spinel layer formation at the slag/refractory interface10.1016/j.jeurceramsoc.2008.07.063 ↗
35. An investigation into the wear mechanisms of carbon- and silicon carbide-based refractory materials by silicomanganese alloy10.17159/2411-9717/959/2020 ↗
36. Corrosion mechanism of commercial doloma refractories in contact with CaO-Al2O3-SiO2-MgO slag10.1179/030192307X231595 ↗
37. Dissolution kinetics of alumina into mold fluxes for continuous steel casting10.2355/isijinternational.45.1856 ↗
38. Design, operation and evaluation of an improved refractory wear testing technique10.1016/j.measurement.2021.109429 ↗
39. Dynamic interaction of refractory and molten steel: corrosion mechanism of alumina–magnesia castables10.1016/j.ceramint.2018.05.085 ↗
40. Slag corrosion and penetration behaviors of MgAl2O4 and Al2O3 based refractories10.1007/s11148-016-9876-y ↗
41. Determination of the dissolution mechanism of Al2O3 in CaO-Al2O3-SiO2 liquids using a combined experimental-numerical approach10.1063/1.2830852 ↗
42. Post-mortem analysis of alumina–magnesia-carbon refractory bricks used in steelmaking ladles10.1016/j.ceramint.2018.09.150 ↗
43. Direct and indirect dissolution of sapphire in calcia-magnesia–alumina–silica melts: dissolution kinetics10.1111/j.1151-2916.1990.tb04269.x ↗
44. Slag corrosion of alumina–magnesia-carbon refractory bricks: experimental data and thermodynamic simulation10.1016/j.ceramint.2016.12.114 ↗
45. Microstructural analysis of corroded alumina–spinel castable refractories10.1016/S0955-2219(96)00073-8 ↗
46. Dissolution and diffusion behavior of Al2O3 in a CaO–Al2O3–SiO2 liquid: an experimental-numerical approach10.1063/1.2786854 ↗
47. B.J. Monaghan, S.A. Nightingale, L. Chen, G.A. Brooks, The dissolution behaviour of selected oxides in CaO-SiO2-Al2O3 slags, in: Proceedings of the Int. Conf. on Molten Slags Fluxes and Salts VII, 2004, pp. 585–94.
48. Comparative study of oxide inclusion dissolution in CaO-SiO2-Al2O3 slag10.1179/174328105X28793 ↗
49. Dissolution behavior of alumina micro-particles in CaO–SiO2–Al2O3 liquid oxide10.1016/j.jnoncrysol.2004.09.011 ↗
50. Determination of dissolution time of Al2O3 and MgO inclusions in synthetic Al2O3-CaO-MgO slags10.1034/j.1600-0692.2003.20631.x ↗
51. In situ observation of the dissolution of spherical alumina particles in CaO-Al2O3-SiO2 melts10.1111/j.1551-2916.2007.02062.x ↗
52. Kinetics of Al2O3 dissolution in CaO-MgO-SiO2-Al2O3 slags: in situ observations and analysis10.1007/s11663-000-0059-2 ↗
53. Dissolution of alumina particles in CaO-Al2O3-SiO2-MgO slags10.1179/030192302225001965 ↗
54. The flow due to a rotating disc10.1017/S0305004100012561 ↗
55. Levich · 1962
56. Ionic mass transfer and concentration polarization at rotating electrodes10.1149/1.2781252 ↗
57. Mass-transfer from solid metal cylinder into liquid metal10.2355/tetsutohagane1955.52.12_1748 ↗
58. Convective heat transfer of the rotational and axial flow between two concentric cylinders10.1299/jsme1958.7.385 ↗
59. Method for determination of effective binary diffusivities in dissolution of dense ceramic materials
60. Accurate density calculation for molten slags in SiO2-Al2O3-CaO-MgO systems10.2355/isijinternational.ISIJINT-2017-070 ↗