Push‐Pull Fatigue of Sintered Silicon Nitride Ceramics at Elevated Temperatures

The fatigue tests under push‐pull completely reversed loading and pulsating loading were performed for silicon nitride ceramics at elevated temperatures. Then the effects of stress wave form, stress rate, and cyclic understressing on fatigue strength, and cyclic straining behavior, were examined. The cycle‐number‐based fatigue life is found to be shorter under trapezoidal stress wave loading than under triangular stress wave loading, and to become shorter with increasing hold time under the trapezoidal stress wave loading. Meanwhile, the equivalent time‐based life curve, which is estimated from the concept of slow crack growth, almost agrees with the static fatigue life curve in the short and intermediate life regions, showing the small cyclic stress effect and the dominant stress‐imposing period effect on cyclic fatigue life. The fatigue strength increased in stepwise stress amplitude increasing test, where stress amplitude is increased stepwise every given number of stress cycles, at 1100° and 1200°C. Occurrence of cyclic strengthening was proved through a gradual decrease in strain amplitude during a pulsating loading test at 1200°C in this material, corresponding to the above cyclic understressing effect on fatigue strength.