Preparation of Ultrathin‐Walled Carbon‐Based Nanoporous Structures by Etching Pseudo‐Amorphous Silicon Oxycarbide Ceramics
Source abstract
Abstract
Etching polymer‐derived silicon‐oxycarbide ceramics with hydrofluoric acid creates nanoporous structures of specific surface areas as high as 600 m 2 /g. The change in composition upon etching shows the removal of silica, not carbon. The structure remaining after etching is postulated to consist of a scaffolding of graphene networks with their surfaces decorated with mixed bonds of tetrahedral silicon bonded to both oxygen and carbon (SiO m C 4− m , where m =1, 2, or 3). The pores existing within such scaffoldings are presumed to have been filled with SiO 2 tetrahedra, which are removed by etching. The measurement of the average pore size and pore volumes permits us to estimate the width of the graphitic domain walls, δ W , left behind by the etching process. The smallest value of δ W , which corresponds to the specimen with the highest surface area, is approximately 1 nm, which is about equal to the total width of one graphene layer and two SiO m C 4– m tetrahedra, one on either side of the graphene sheet. This highest surface area specimen is also believed to have the largest size of the silica domains in the unetched samples. In specimens with smaller domains, the etching is only partially successful in removing the silica, presumably because their small size hinders the access of the etchant to the silica tetrahedra. The above behavior is found for samples with low to moderate carbon content. In one sample with a very high carbon content, the etching process removes some carbon as well as silica.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Graphene research and applications · Advanced ceramic materials synthesis · Diamond and Carbon-based Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. 10.1038/273525a010.1038/273525a0 ↗
2. Introduction to the Special Topical Issue on Ultrahigh‐Temperature Polymer‐Derived Ceramics10.1111/j.1151-2916.2001.tb00980.x ↗
3. 10.1111/j.1151-2916.2001.tb00789.x10.1111/j.1151-2916.2001.tb00789.x ↗
4. High Temperature Behaviour of a Gel‐Derived SiOC Glass
5. 10.1016/j.jnoncrysol.2005.06.00810.1016/j.jnoncrysol.2005.06.008 ↗
6. Thermal Behaviour of a Polytitanocarbosilane‐Derived Fibre with a Low Oxygen Content
7. 10.1111/j.1151-2916.2002.tb00308.x10.1111/j.1151-2916.2002.tb00308.x ↗
8. Novel Er‐Doped SiC/SiO2 Nanocomposites
9. 10.1063/1.158787610.1063/1.1587876 ↗
10. Characterization of Nanodomains in Polymer‐Derived SiCN Ceramics Employing Multiple Techniques10.1111/j.1551-2916.2004.00034.x ↗
11. 10.1016/0022-3093(88)90270-010.1016/0022-3093(88)90270-0 ↗
12. Composition and Structure of Ceramic Fibers Prepared from Polymer Precursors10.1111/j.1551-2916.1987.tb00066.x ↗
13. A.Saha R.Raj andD. L.Williamson “A Model for the NanoDomains in Polymer Derived SiCO. J. Am. Ceram. Soc. in press.
14. 10.1021/cm970224p10.1021/cm970224p ↗
15. 10.1002/sia.97110.1002/sia.971 ↗
16. Y.BumandG. A.McDermott “Dehydrocoupling Treatment and Hydrosilylation of Silicon‐Containing Polymer and Compounds and Articles Produced Thereby”; US patent number 5 639 844.
17. 10.1016/S0022-3093(99)00101-510.1016/S0022-3093(99)00101-5 ↗
18. S. J.GreggandK. S. W.Sing “Adsorption Surface Area and Porosity”; pp.285–6.Academic Press London 1982.
19. 10.1021/ja01145a12610.1021/ja01145a126 ↗
20. 10.1021/ja01236a04710.1021/ja01236a047 ↗
21. Structure and Texture Analysis of Colloidal Silica in Porous Glasses
22. 10.1023/A:102743851797310.1023/A:1027438517973 ↗
23. 10.1023/A:102402721312210.1023/A:1024027213122 ↗
24. 10.1023/A:102073882970710.1023/A:1020738829707 ↗
25. 10.1016/S0022-3093(98)00821-710.1016/S0022-3093(98)00821-7 ↗
26. 10.1103/PhysRevB.61.1409510.1103/PhysRevB.61.14095 ↗
27. 10.1021/cm00024a03510.1021/cm00024a035 ↗
28. 10.1021/cm970224p10.1021/cm970224p ↗
29. 10.1111/j.1151-2916.1983.tb15715.x10.1111/j.1151-2916.1983.tb15715.x ↗
30. 10.1023/A:100876582901210.1023/A:1008765829012 ↗