Monolithic poly(methylsilsesquioxane) aerogels with glasslike transparency: from sol-gel synthesis to ambient pressure drying
Source abstract
Abstract
Abstract Practical aspects of the successful preparation of monolithic poly(methylsilsesquioxane) (PMSQ) aerogels with glasslike transparency via ambient pressure drying (APD) are discussed in detail. Two-step acid-base process starting from methyltrimethoxysilane (MTMS) in the presence of nonionic poly(ethylene oxide)-block-poly(propylene oxide)-block-poly(ethylene oxide) surfactant and the use of strong base as polycondensation catalyst resulted in fine mesoporous structure, showing low density (0.148 g cm−3) and glasslike transparency (95% at 10 mm thickness). Cracking and irreversible shrinkage during APD have been prevented by optimized aging and drying processes. In particular, aging in an aqueous alcohol solution containing a low concentration of MTMS under controlled temperature has been found to be crucial in obtaining PMSQ aerogels with crack-free, low-density, glasslike transparency, and monolithic nature. A large-area APD aerogel in 120×120×6 mm3, with thermal conductivity of 15.6 mW m−1 K−1, has successfully been obtained due to optimizations of aging and drying conditions. Similar APD aerogels have also been obtained when alkali metal hydroxides, especially lithium hydroxide, are employed as base catalysts. These findings are expected to play important roles in designing industrial productions of monolithic aerogels for thermal superinsulation and other applications.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aerogels and thermal insulation · Silicone and Siloxane Chemistry · Surface Modification and Superhydrophobicity
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Dislich H (1971) New routes to multicomponent oxide glasses. Angew Chem Int Ed 10:363–43410.1002/anie.197103631 ↗
2. Hench LL, West JK (1990) The sol-gel process. Chem Rev 90:33–7210.1021/cr00099a003 ↗
3. Brinker CJ, Scherer GW (1990) Sol-gel science: The physics and chemistry of sol-gel processing. Academic Press, San Diego
4. Sakka S (2022) Birth of the sol–gel method: early history. J Sol Gel Sci Technol 102:478–48110.1007/s10971-021-05640-9 ↗
5. Adachi T, Sakka S (1987) Preparation of monolithic silica gel and glass by the sol-gel method using N,N-dimethylformamide. J Mater Sci 22:4407–441010.1007/BF01132038 ↗
6. Wallace S, Hench LL (1984) The processing and characterization of DCCA modified gel-derived silica. s MRS Online Proc Lib 32:47–5210.1557/PROC-32-47 ↗
7. Kajihara K, Hirano M, Hosono H (2009) Sol-gel synthesis of monolithic silica gels and glasses from phase-separating tetraethoxysilane–water binary system. Chem Commun 18:2580–258210.1039/b900887j ↗
8. Kistler SS (1931) Coherent expanded aerogels and jellies. Nature 127:74110.1038/127741a0 ↗
9. Kistler SS (1932) Coherent expanded aerogels. J Phys Chem 36:52–6410.1021/j150331a003 ↗
10. Hüsing N, Schubert U (1998) Aerogels - Airy materials: Chemistry, structure, and properties. Angew Chem Int Ed 37:22–4510.1002/(SICI)1521-3773(19980202)37:1/2<22::AID-ANIE22>3.0.CO;2-I ↗
11. Pierre AC, Pajonk GM (2002) Chemistry of aerogels and their applications. Chem Rev 102:4243–426510.1021/cr0101306 ↗
12. Buratti C, Belloni E, Merli F, Zinzi M (2021) Aerogel glazing systems for building applications: A review. Energy Build 231:11058710.1016/j.enbuild.2020.110587 ↗
13. Wan W, Zhang R, Ma M, Zhou Y (2018) Monolithic aerogel photocatalysts: a review. J Mater Chem A 6:754–77510.1039/C7TA09227J ↗
14. Maleki H, Hüsing N (2018) Current status, opportunities and challenges in catalytic and photocatalytic applications of aerogels: Environmental protection aspects. Appl Catal B Environ 221:530–55510.1016/j.apcatb.2017.08.012 ↗
15. Stergar J, Maver U (2016) Review of aerogel-based materials in biomedical applications. J Sol Gel Sci Technol 77:738–75210.1007/s10971-016-3968-5 ↗
16. Xie X, Zheng Z, Wang X, Kaplan DL (2021) Low-density silk nanofibrous aerogels: Fabrication and applications in air filtration and oil/water purification. ACS Nano 15:1048–105810.1021/acsnano.0c07896 ↗
17. Zhang X, Hu Z, Sun Q, Liang X, Gu P, Huang J, Zu G (2023) Bioinspired gradient stretchable aerogels for ultrabroad-range-response pressure-sensitive wearable electronics and high-efficient separators. Angew Chem Int Ed 62:e20221395210.1002/anie.202213952 ↗
18. Gu P, Lu L, Yang X, Hu Z, Zhang X, Sun Z, Liang X, Liu M, Sun Q, Huang J, Zu G (2024) Highly Stretchable Semiconducting Aerogel Films for High-Performance Flexible Electronics. Adv Funct Mater https://doi.org/10.1002/adfm.20240058910.1002/adfm.202400589 ↗
19. Parale VG, Kim T, Choi H, Phadtare VD, Dhavale RP, Kanamori K, Park H-H (2024) Mechanically strengthened aerogels through multi-scale, multi-composition, and multi-dimensional approaches: A review. Adv Mater 36:230777210.1002/adma.202307772 ↗
20. Abraham E, Cherpak V, Senyuk B, ten Hove JB, Lee T, Liu Q, Smalyukh II (2023) Highly transparent silanized cellulose aerogels for boosting energy efficiency of glazing in buildings. Nat Energy 8:381–39610.1038/s41560-023-01226-7 ↗
21. He H, Wei X, Yang B, Liu H, Sun M, Li Y, Yan A, Tang CY, Lin Y, Xu L (2022) Ultrastrong and multifunctional aerogels with hyperconnective network of composite polymeric nanofibers. Nat Commun 13:424210.1038/s41467-022-31957-2 ↗
22. Xu X, Zhang Q, Hao M, Hu Y, Lin Z, Peng L, Wang T, Ren X, Wang C, Duan X (2019) Double-negative-index ceramic aerogels for thermal superinsulation. Science 363:723–72710.1126/science.aav7304 ↗
23. Wang S, Li L, Zha L, Koskela S, Berglund LA, Zhou Q (2023) Wood xerogel for fabrication of high-performance transparent wood. Nat Commun 14:282710.1038/s41467-023-38481-x ↗
24. Zhao S, Siqueira G, Drdova S, Norris D, Ubert C, Bonnin A, Galmarini S, Ganobjak M, Pan Z, Brunner S, Nyström G, Wang J, Koebel MM, Malfait WJ (2020) Additive manufacturing of silica aerogels. Nature 584:387–39210.1038/s41586-020-2594-0 ↗
25. Kanamori K, Aizawa M, Nakanishi K, Hanada T (2007) New transparent methylsilsesquioxane aerogels and xerogels with improved mechanical properties. Adv Mater 19:1589–159310.1002/adma.200602457 ↗
26. Kanamori K, Nakanishi K (2011) Controlled pore formation in organotrialkoxysilane-derived hybrids: from aerogels to hierarchically porous monoliths. Chem Soc Rev 40:754–77010.1039/C0CS00068J ↗
27. Shimizu T, Kanamori K, Nakanishi K (2017) Silicone‐based organic–inorganic hybrid aerogels and xerogels. Chem Eur J 23:5176–518710.1002/chem.201603680 ↗
28. Kanamori K (2024) Homogeneous silicone network formation in aqueous sol–gel systems toward low-density porous materials. J Ceram Soc Jpn 132:69–7810.2109/jcersj2.23150 ↗
29. Ueoka R, Hara Y, Maeno A, Kaji H, Nakanishi K, Kanamori K (2024) Unusual flexibility of transparent poly(methylsilsesquioxane) aerogels by surfactant-induced mesoscopic fiber-like assembly. Nat Commun 15:46110.1038/s41467-024-44713-5 ↗
30. Prakash SS, Brinker CJ, Hurd AJ, Rao SM (1995) Silica aerogel films prepared at ambient pressure by using surface derivatization to induce reversible drying shrinkage. Nature 374:439–44310.1038/374439a0 ↗
31. Dong H, Brook MA, Brennan JD (2005) A new route to monolithic methylsilsesquioxanes: gelation behavior of methyltrimethoxysilane and morphology of resulting methylsilsesquioxanes under one-step and two-step processing. Chem Mater 17:2807–281610.1021/cm050271e ↗
32. Cordes DB, Lickiss PD, Rataboul F (2010) Recent Developments in the Chemistry of Cubic Polyhedral Oligosilsesquioxanes. Chem Rev 110:2081–217310.1021/cr900201r ↗
33. Abe Y, Gunji T (2004) Oligo- and polysiloxanes. Prog Polym Sci 29:149–18210.1016/j.progpolymsci.2003.08.003 ↗
34. Scherer GW (2019) Stress and strain during supercritical drying. J Non Cryst Solids 90:8–19
35. Zhu Y, Morimoto Y, Shimizu T, Morisato K, Takeda K, Kanamori K, Nakanishi K (2015) Synthesis of hierarchically porous polymethylsilsesquioxane monoliths with controlled mesopores for HPLC separation. J Ceram Soc Jpn 123:770–77810.2109/jcersj2.123.770 ↗
36. Iswar S, Malfait WJ, Balog S, Winnefeld F, Lattuada M, Koebel MM (2017) Effect of aging on silica aerogel properties. Microporous Mesoporous Mater 241:293–30210.1016/j.micromeso.2016.11.037 ↗
37. Reichenauer G, Scherer GW (2000) Nitrogen adsorption in compliant materials. J Non Cryst Solids 277:162–17210.1016/S0022-3093(00)00304-5 ↗
38. Reichenauer G, Scherer GW (2001) Extracting the pore size distribution of compliant materials from nitrogen adsorption. Colloids Surf A 187-188:41–5010.1016/S0927-7757(01)00619-7 ↗
39. Tayefi M, Eesaee M, Hassanipour M, Elkoun S, David E, Nguyen-Tri P (2023) Recent progress in the accelerated aging and lifetime prediction of elastomers: A review. Polym Degrad Stab 214:11037910.1016/j.polymdegradstab.2023.110379 ↗
40. Moghadam MK, Morshedian J, Ehsani M, Bahrami M, Saddadi H (2013) Lifetime prediction of HV silicone rubber insulators based on mechanical tests after thermal ageing. IEEE Trans Dielectr Electr Insul 20:711–71610.1109/TDEI.2013.6518939 ↗
41. Tewari PH, Hunt AJ, Lofftus KD (1985) Ambient-temperature supercritical drying of transparent silica aerogels. Mater Lett 3:363–36710.1016/0167-577X(85)90077-1 ↗
42. Yoda S, Ohshima S (1999) Supercritical drying media modification for silica aerogel preparation. J Non-Cryst Solids 248:224–23410.1016/S0022-3093(99)00250-1 ↗
43. Hayase G, Kanamori K, Maeno A, Kaji H, Nakanishi K (2016) Dynamic spring-back behavior in evaporative drying of polymethylsilsesquioxane monolithic gels for low-density transparent thermal superinsulators. J Non Cryst Solids 434:115–11910.1016/j.jnoncrysol.2015.12.016 ↗
44. Hæreid S, Einarsrud M-A, Scherer GW (1994) Mechanical strengthening of TMOS-based alcogels by aging in silane solutions. J Sol Gel Sci Technol 3:199–20410.1007/BF00486558 ↗
45. Hæreid S, Dahle M, Lima S, Einarsrud MA (1995) Preparation and properties of monolithic silica xerogels from TEOS-based alcogels aged in silane solutions. J Non Cryst Solids 186:96–10310.1016/0022-3093(95)00039-9 ↗
46. Rolo LI, Caço AI, Queimada AJ, Marrucho IM, Coutinho JA (2002) Surface tension of heptane, decane, hexadecane, eicosane, and some of their binary mixtures. J Chem Eng Data 47:1442–144510.1021/je025536+ ↗
47. Scherer GW (1987) Drying gels III. Warping plate. J Non Cryst Solids 91:83–10010.1016/S0022-3093(87)80087-X ↗
48. Dong H, Lee M, Thomas RD, Zhang Z, Reidy RF, Mueller DW (2003) Methyltrimethoxysilane sol-gel polymerization in acidic ethanol solutions studied by 29Si NMR spectroscopy. J Sol Gel Sci Technol 28:5–1410.1023/A:1025690300105 ↗
49. Shimizu T, Kanamori K, Nakanishi K (2017) Transparent polyvinylsilsesquioxane aerogels: investigations on synthetic parameters and surface modification. J Sol Gel Sci Technol 82:2–1410.1007/s10971-017-4339-6 ↗