Innovation in the Use of Recycled and Heat-Treated Glass in Various Applications: Mechanical and Chemical Properties

By decreasing manufacturing costs for different civic purposes, glass recycling is an economically significant technology that also helps conserve natural resources and mitigates environmental problems. Throughout the recycling process, this study used recycled domestic glass in compliance with European guidelines for recycling of household garbage. The purpose of this research is to examine the chemical and mechanical properties of recycled and crushed glass with particle sizes varying from 0.1 mm to 2 mm as a function of various treatment temperatures. This might pave the way for novel building materials, artwork, and interior design components, among other potential uses. “Silica glass”, the most common and ancient kind of glass, which includes SiOk, NakO, CaO, and small amounts of other elements, was utilized in the investigation. Several materials can be successfully modified or altered using step heat treatment. The mechanical and chemical properties of recycled and shattered glass were assessed using microhardness, compressive, and chemical testing. These samples were then compared to mosaics from Murano, Italy, and Dynasty Smalti, China. The recycled and heat-treated glass produced microhardness values of 550.6 HV and 555.0 HV, respectively, when tested with forces of 0.981 N and 2.942 N. These values were higher than those of Murano (Italy) and were comparable to those of Dynasty Smalti mosaic (China). Furthermore, compression testing demonstrated that tempered and heat-tempered glass, which might include up to 5 g of TiO2, could endure compressive strains of up to 16 MPa. This is in sharp contrast to Dynasty Smalti, which could only withstand tensions of 6–8 MPa, and Murano, which could only withstand stresses of 3–4 MPa. Tests conducted chemically over a seven-day period using KOH at 30 g/L and 100 g/L, along with HCl at 3% and 18%, showed that the samples did not alter in any way; their surface, color, and weight were untouched. Crushing and heating recycled glass makes it a viable alternative to using new glass in civil engineering projects. This helps make material reuse more efficient, which in turn helps the environment. Sturdy and resilient in a variety of contexts, the material shares mechanical and chemical properties with standard mosaics.