A Preparation Method for Improving the Thermal Conductivity of Graphene Film

Graphene films are widely used in thermal management of electronic devices due to their excellent properties such as high flexibility, high thermal conductivity and light weight. However, in the traditional preparation process, some structural defects are introduced, which will lead to an increase in phonon scattering, thereby reducing the thermal conductivity of graphene. Therefore, a new method for preparing graphene thin films is proposed by using the evaporation method; the graphene oxide composite film is prepared by adding carbon-rich molecules (CRMs) to the graphene oxide dispersion liquid. The experimental results show that the addition of a mass fraction of 0.15% CRMs helps to form continuous strips and channels, which are beneficial to the construction of the internal aromatic structure of graphene and improve the crystallinity of graphene film. The in-plane thermal conductivity of the composite film increased from 598.74 W/(m·K) to 704.27 W/(m·K) after adding carbon-rich molecules. However, excess CRMs can lead to the formation of disordered structures during graphitization, which will reduce the thermal conductivity of the film to a certain extent. The radiation properties of graphene films are also proposed to verify the validity of the above conclusions, and the results show that the graphene film with a mass fraction of 0.24% CRMs has better heat dissipation performance, which can be reduced by 5 °C compared with that of pure graphene film. Through the application of graphene in new energy car seats, it is proved that compared with the resistance wire seats, graphene seats have better performance in terms of a fast heating speed and uniform heating.