Residual Stresses of 316L Stainless Steel Laser Direct Metal During Pulsed-Wave and Continuous-Wave Laser Additive Manufacturing: A Comparative Study

Continuous-wave laser (CW) and pulsed-wave laser (PW) are the two laser modes in direct energy deposition (DED). This paper mainly reports on a study into the effects of the two laser modes on residual stresses with a given energy input. The contour method (CM) with non-uniform spatial distribution of inspection points was used to capture residual stress distributions in DED of Fe3000 on a substrate made of 316L stainless steel. Residual stresses in the transition zone between the deposit and the substrate were carefully examined to gain an understanding of cracks frequently observed at the connection between the substrate and the deposit. Furthermore, X-ray diffraction, along with successive material removal, was used to reveal residual stresses at various depths in the substrate. The results showed that significant tensile longitudinal stresses developed at the substrate–deposit junction for both CW and PW laser modes. It increased sharply (about 64%) with the increase in energy input for CW mode, while it showed the opposite trend for PW mode; the longitudinal residual stress decreased 13.2% with the increase in energy input. PW, however, introduced lower residual stress than that of CW under the condition of high-energy input; the maximum longitudinal residual stress decreased by about 10.4% compared to CW mode. This was due to stress relaxation at high-energy inputs in PW mode. In addition, residual stresses were found to be higher than the initial yield stress, and yielding occurred in the deposited part. The results determined by the CM and X-ray diffraction depth profiling were found to be consistent.