Assessing the Printability of Rene 65 Powder for Repairing Degraded GTD 111 Gas Turbine Blades Using L-DED and L-PBF

Restoring components in the hot gas path of turbine engines after service-induced degradation is crucial for economic efficiency. This study investigates the printability of Rene 65 powder on a degraded first-stage turbine blade using two additive manufacturing techniques: Laser Powder Bed Fusion (L-PBF) and Laser Powder Directed Energy Deposition (L-DED). Deposited material was evaluated using optical microscopy (OM), scanning electron microscopy (SEM), and Electron Backscatter Diffraction (EBSD) to characterize its crystallographic texture, while microhardness testing provided insight into its mechanical properties. Our results show that L-PBF excels at replicating intricate features, such as small cooling holes, and produces a highly texturized microstructure oriented parallel to <001> under optimal parameters (80 W, 400 mm/s, unidirectional scanning), although at a slower pace. In contrast, L-DED offers a versatile, rapid, and cost-effective method for repairing medium to large parts, yielding an equiaxed microstructure and higher as-printed hardness—approaching GTD 111 values due to an aging effect from high heat input. Both processes effectively restored the dimensional integrity of degraded blade tips, paving the way for more sustainable and economical maintenance strategies in the aerospace industry.