Physical Properties and Rheological Characteristics of Cigarette Butt-Modified Asphalt Binders

Cigarette butt (CB) waste is abundant and difficult to biodegrade, which is dangerous for both the environment and human health. The key reason CBs are littered is that people do not know much about the harm CBs pose to the environment. Recycling CBs in infrastructure construction can help raise people’s awareness. To promote the recycling of CB waste, this paper aimed to determine the feasibility of using CBs as a modifier for asphalt binders. In this research, CBs were preprocessed and mixed with virgin asphalt binder as a fiber modifier. Comprehensive laboratory investigations, including a softening point test, viscosity test, storage stability test, and temperature sweep test, were performed, along with a frequency sweep test, to evaluate the performance of the modified samples. During this investigation, samples were prepared with 1%, 2%, 3%, and 4% CBs. The results of the CB-modified samples were compared with the sample consisting of fresh bitumen (0% fiber). The results show that the physical and rheological properties of bitumen with incorporated CBs improved significantly, and CBs could be used instead of virgin cellulose fiber as a fiber modifier. However, CB-modified asphalt reduced the storage stability and low-temperature performance of the samples. Further research should focus on improving the storage stability and low-temperature performance of CB-modified asphalt binders to facilitate their application in asphalt pavements.