Microstructural, Nanomechanical, and Tribological Properties of Thin Dense Chromium Coatings
Source abstract
Abstract
Nowadays, Thin Dense Chromium (TDC) coatings are being industrially used in rolling bearings applications due to their claimed advantages such as high hardness, low wear, and good corrosion resistance. However, despite their broad commercial use, very little has been published in the open scientific literature regarding their microstructure, nanomechanical, and tribological properties. In this paper, TDC coatings with a thickness of about 5 µm were deposited by a customized electrochemical process on ASTM 52100 bearing steel substrates. Surface microstructure and chemical composition analysis of the TDC coatings was carried out by scanning electron microscopy and atomic force microscopy. The results revealed a coating with a dense, nodular, and polycrystalline microstructure. Unlike standard electrodeposited “Hard Chromium” coatings, TDC coatings show no presence of micro/nano-cracks, likely contributing to their superior corrosion resistance. The nanomechanical behavior, studied by nanoindentation as a function of penetration depths, exhibits a pronounced size effect near the coating surface that can be linked to the nodular microstructure. A hard surface with hardness HIT 14.9 ± 0.5 GPa and reduced elastic modulus Er = 216.8 ± 3.9 GPa was observed. Tribological characterization under the presence of lubricants was performed by two single-contact tribometers using coated and uncoated steel balls against flat steel substrates. An in-house fretting wear rig was used to measure the lubricated friction coefficient in pure sliding conditions, whilst the friction performance in rolling/sliding lubricated conditions was evaluated using a WAM test rig. In pure sliding, TDC/TDC contacts show ~13% lower friction than for steel. Under rolling/sliding conditions with 5% sliding, the traction coefficient of TDC/TDC coating contact was at least 20% lower than that for steel/steel contact. The tribological results obtained in various contact conditions demonstrate the benefits of applying TDC coatings to reduce bearing friction.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Diamond and Carbon-based Materials Research · Tribology and Wear Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Research and Technology Development, SKF, 3992 AE Houten, The Netherlands
Department of Materials Science and Engineering, Faculty of Mechanical Engineering, Delft University of Technology, 2628 CD Delft, The Netherlands
Funding
Materials innovation institute · Holland High Tech|TKI HSTM
References (36)
Show source-provided references
1. Bussy, J.D. (1848). Revêtements de Chrome. (3564), France Patent.
2. Electrolytic Chromiun
3. Dennis, J.K., and Such, T.E. (1993). Chapter 1—Introduction and Historical Review. Nickel and Chromiun Plating, Woodhead Publishing.10.1533/9781845698638.1 ↗
4. Nagrale, P. (2024). Global Chrome Plating Market Overview, Market Research Future.
5. Thin, Dense, Chromium Coatings Protects Parts
6. Waskiewicz, W.P. (1984). Extending Bearing Life in Off-Highway Equipment. International Off-Highway & Powerplant Congress & Exposition, Milwaukee.10.4271/841124 ↗
7. Friction, wear, and corrosion control in rolling bearings through coatings and surface10.1116/1.573615 ↗
8. Bamberger, E.N., Averbach, B.L., and Pearson, P.K. (1989). Improved Fatigue Life Bearing Development—Report AFWAL-TR-89-2012, Wright Research and Development Center.
9. Hirvonen, J.K. (1995, January 18–29). Ion Beam Assisted Thin Film Deposition: Fundamentals and Applications of IBAD Processing. Proceedings of the Nato Advance Study on Materials and Processes for Surface and Interface Engineering, Chateau de Bonas, Gers, France.10.1007/978-94-011-0077-9_9 ↗
10. Pearson, P.K. (1998). The history and future of aircraft turbine engine bearing steels. Bearing Steels: Into the 21st Century, ASTM International.10.1520/STP12138S ↗
11. Hoo, J.J.C. (1993). Bearing Material/Treatment Developments at the SKF Engineering and Research Centre. Creative Use of Bearing Steels, ASTM STP 1195, American Society for Testing and Materials.
12. Armoloy Corporation (2024, October 21). Nodular Thin Dense Chrome. Available online: https://armoloy.com/coatings/thin-dense-chrome/.
13. U. S. Chrome (2024, October 21). Thin Dense Chrome. Available online: https://www.uschrome.com/thin-dense-chrome/.
14. Duro-Chrome (2024, October 21). Thin Dense Hard Chrome. Available online: https://duro-chrome.com/thin-dense-hard-chrome/.
15. ATC Technology Coatings (2024, October 21). Thin Dense Chromiun Technology. Available online: https://www.atc-armoloy.com/en/general-information/chromium.html.
16. Tribological Investigation on WC/C Coatings Applied on Bearings Subjected to Fretting Wear10.1007/s11249-024-01892-y ↗
17. The Armoloy Corporation (2005). The Electrolizing Thin, Dense, Chromium Process. Coatings Technology Handbook, CRC Press.
18. Indentation Hardness Measurements at Macro-, Micro-, and Nanoscale: A Critical Overview10.1007/s11249-016-0805-5 ↗
19. (2021). Standard Test Method for Microindentation Hardness of Electroplated Coatings (Standard No. ASTM B578-21).
20. Broitman, E. (2022). Coatings to Improve Bearing Perfomance. Evolution, 1–7. Available online: https://evolution.skf.com/coatings-to-improve-bearing-performance/.
21. (2024, October 21). SKF Coatings Catalogue. Available online: https://cdn.skfmediahub.skf.com/api/public/0901d19680a4e17f/pdf_preview_medium/0901d19680a4e17f_pdf_preview_medium.pdf.
22. SKF (2024, October 21). Kaydon Endurakote®—Plated Bearings. Kaydon Bearing Solutions—SKF. Available online: https://www.kaydonbearings.com/Endurakote_bearings.htm&r=1.
23. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments10.1557/JMR.1992.1564 ↗
24. An overview of the potential of quantitative coating adhesion measurement by scratch testing10.1016/j.triboint.2005.04.013 ↗
25. Broitman, E., Ruellan, A., Meeuwenoord, R., Nijboer, D., and Brizme, V. (2023). Comparison of Various Conversion Layers for Improved Friction Performance of Railway Wheel-End Bearings. Coatings, 13.10.3390/coatings13121980 ↗
26. (2015). Metallic Materials—Instrumented Indentation Test for Hardness and Materials Parameters—Part 1: Test Method (Standard No. ISO-14577-1).
27. Fischer-Cripps, A.C. (2011). Nanoindentation, Springer.10.1007/978-1-4419-9872-9 ↗
28. Hybrid Ceramic Bearings for Difficult Applications10.1115/1.2816610 ↗
29. Mohn, J.H., Munson, H.E., Poole, W.E., and Hodgens, H.M. (1984). Improvement of the Corrosion Resistance of Turbine Engine Bearings (Report AFWAL-TR-84-2014), AF Wright Aeronautical Laboratories.
30. (2021). Plating, Chromium Thin, Hard, Dense Deposit (Standard No. AMS2438F).
31. Jones, A., Sugawara, S., and Enloe, J. (2000). Adhesion Testing of Hard Chromium Electrodeposits. AESF SUR/FIN, American Electroplaters & Surface Finishers Society.
32. The study of the adhesion of a TiN coating on steel and titanium alloy substrates using a multi-mode scratch tester10.1016/j.triboint.2005.04.011 ↗
33. Industrial-scale deposition of highly adherent CNx films on steel substrates10.1016/j.surfcoat.2010.03.038 ↗
34. Armoloy of Illinois (2024, October 27). Thin Dense Chrome Plating Performance Characteristics. Available online: https://armoloy-il.com/armoloy-tdc-thin-dense-chrome/.
35. ATC (2024, October 27). Thin, Dense, Chromium Coating Technology. Available online: https://www.solidcomponents.com/files/company/SCCNS20DW/companyfiles/doc/atc-armoloy-general-information_engelsk_version.pdf.
36. Sliding wear evaluation of various coating processes on AISI 52100 and M 50 steels10.1179/mst.1992.8.7.582 ↗