Physical and Chemical Properties of High-Temperature Silicone-Based Polymer Coatings Applied on Different Surface Roughnesses
Source abstract
Abstract
High-temperature coatings play a crucial role in protecting surfaces exposed to extreme temperatures, corrosion, and other harsh environments. This paper focuses on the physical and chemical properties of solvent-borne and water-borne high-temperature silicone-based polymer coatings applied on two types of surface roughness of carbon steel plates. The corrosion protection performance of the coatings was characterized using a salt spray chamber, humidity chamber, electrochemical impedance spectroscopy (EIS) measurements, and differential scanning calorimetry (DSC). The physical properties of high-temperature coatings were determined using the Shore D hardness method and cross-cut adhesion tests. This study investigates the effects of different surface preparation methods on coating adhesion, which is considered to be a crucial property of organic coatings for corrosion protection durability. The thermal stability of the coating was tested using furnace cyclic testing. The results show that high-temperature coatings in general exhibit excellent thermal stability, high adhesion strength, and good resistance to warm and humid environments, except in the conditions of a salty atmosphere. This study reveals that coating performance is affected by the composition and surface preparation method. This study can be useful for coating manufacturers and researchers interested in understanding the physical and chemical properties of high-temperature coatings and their applications in various environments.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Diamond and Carbon-based Materials Research · Tribology and Wear Analysis · Surface Modification and Superhydrophobicity
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, 10000 Zagreb, Croatia
Funding
European Regional Development Fund
References (33)
Show source-provided references
1. Bose, S. (2017). High Temperature Coatings, Butterworth-Heinemann.10.1016/B978-0-12-804622-7.00005-X ↗
2. Lai, G.Y. (2007). High-Temperature Corrosion and Materials Applications, ASM International.10.31399/asm.tb.htcma.9781627083041 ↗
3. Zielecka, M., Rabajczyk, A., Cygańczuk, K., Pastuszka, Ł., and Jurecki, L. (2020). Silicone Resin-Based Intumescent Paints. Materials, 13.10.3390/ma13214785 ↗
4. State of the art on high-temperature corrosion-resistant coatings
5. Characterization of high-temperature paints for infrared thermography in fire research10.1016/j.firesaf.2023.103775 ↗
6. Studies on the properties of silicone resin films on mild steel10.1108/03699420010362519 ↗
7. Evaluation of heat resistant properties of silicone-based coatings by SEM and a.c. Impedance techniques10.1016/0300-9440(95)00599-4 ↗
8. Ramakrishnan, M. (2017, January 26–30). Epoxy High Temperature Coatings and Considerations. Proceedings of the Corrosion 2017, New Orleans, LO, USA.
9. The degradation of silicone coatings in high-temperature atmospheres10.1108/00035599810236504 ↗
10. Greatly improving thermal stability of silicone resins by modification with POSS10.1016/j.polymdegradstab.2020.109082 ↗
11. Molecular Dynamics Simulation of Interface Properties between Water-Based Inorganic Zinc Silicate Coating Modified by Organosilicone and Iron Substrate10.32604/jrm.2022.024023 ↗
12. Electrochemical impedance spectroscopic evaluation of cor-rosion protection properties of polyurethane/polyvinyl chloride blend coating on steel
13. Stojanović, I., Logar, M., Fatović, I., Alar, V., and Rakela-Ristevski, D. (2023). Experimental Study of Atmospherically and Infrared-Dried Industrial Topcoats. Coatings, 13.10.3390/coatings13081343 ↗
14. Chen, J., Liu, J., Wang, H., Li, B., Hu, Q., Shao, T., Yang, R., Wang, B., Wan, Q., and Li, Z. (2023). Experimental Study on Neutral Salt Spray Accelerated Corrosion of Metal Protective Coatings for Power-Transmission and Transformation Equipment. Coatings, 13.10.3390/coatings13030480 ↗
15. Tsai, P.-Y., Chen, T.-E., and Lee, Y.-L. (2018). Development and Characterization of Anticorrosion and Antifriction Properties for High Performance Polyurethane/Graphene Composite Coatings. Coatings, 8.10.3390/coatings8070250 ↗
16. (2020). Paints and Varnishes—Cross-Cut Test (Standard No. ISO 2409).
17. Research into the possibility of using the new generation paint systems for the anticorrosion protection of steel structures
18. (2017). Paints and Varnishes—Determination of Resistance to Humidity—Part 1: Condensation (Single-Sided Exposure) (Standard No. ISO 6270).
19. (2016). Paints and Varnishes—Evaluation of Degradation of Coatings—Designation of Quantity and Size of Defects, and of Intensity of Uniform Changes in Appearance—Part 1: General Introduction and Designation System (Standard No. ISO 4628).
20. Polymeric and ceramic silicon-based coatings—A review10.1039/C8TA09054H ↗
21. Indumathy, B., Sathiyanathan, P., Prasad, G., Reza, M.S., Prabu, A.A., and Kim, H. (2023). A Comprehensive Review on Processing, Development and Applications of Organofunctional Silanes and Silane-Based Hyperbranched Polymers. Polymers, 15.10.3390/polym15112517 ↗
22. Hoang, N., Khoa, T.A., Nhung, L.T., Phuong, P.M., Binh, T.D., Hang, T.T.X., Chi, N.V., and Nguyen, T.-D. (2022). Flake ZnAl Alloy as an Effective Pigment in Silicate Coatings for the Corrosion Protection of Steel. Coatings, 12.10.3390/coatings12081046 ↗
23. (2019). Paints and Varnishes—Determination of Film Thickness (Standard No. ISO 2808).
24. (2022). Corrosion Tests in Artificial Atmospheres—Salt Spray Tests (Standard No. ISO 9227).
25. (2018). Paints and Varnishes—Corrosion Protection of Steel Structures by Protective Coating Systems—Part 6: Laboratory Performance Test Methods (Standard No. ISO 12944-6).
26. (2007). Preparation of Steel Substrates before Application of Paints and Related Products—Visual Assessment of Surface Cleanliness—Part 1: Rust Grades and Preparation Grades of Uncoated Steel Substrates and of Steel Substrates after Overall Removal of Previous Coatings (Standard No. ISO 8501-1).
27. Adhesion and anticorrosive properties of DTM coating as related to primer coating
28. Pintaude, G., Cousseau, T., and Rudawska, A. (2022). Tribology of Machine Elements, IntechOpen.
29. Advances in corrosion protection by organic coatings: What we know and what we would like to know10.1016/j.porgcoat.2016.04.030 ↗
30. Ambat, R., and Piotrowska, K. (2022). Humidity and Electronics, Woodhead Publishing.
31. Stojanović, I., Cindrić, I., Turkalj, L., Kurtela, M., and Rakela-Ristevski, D. (2022). Durability and Corrosion Properties of Waterborne Coating Systems on Mild Steel Dried under Atmospheric Conditions and by Infrared Radiation. Materials, 15.10.3390/ma15228001 ↗
32. Gel-Electrolyte EIS setup used for probing of IR Dried/Cured industrial coatings10.1016/j.porgcoat.2019.105331 ↗
33. Preparation and Characterization Of Weather Resistant Silicone/Acrylic Resin Coatings10.1007/BF02697923 ↗