Dissolution Behavior of Different Alumina Phases within Plasma Electrolytic Oxidation Coatings

The influence of chemical redissolution in the PEO layer-growth equilibrium on aluminum is evaluated differently in literature. In order to estimate whether and to what extent various alumina modifications could be affected by redissolution processes during PEO, immersion experiments were carried out on PEO coatings in model electrolytes of different alkalinity and silicate concentration. Their composition was determined spectroscopically before and after the experiments. The layers were characterized by XRD before and after the tests and examined at affected and unaffected zones using SEM, EDX, and EBSD. The results show that chemical oxide dissolution can only be observed at the layer/substrate interface and that primarily amorphous alumina is affected. This process is intensified by higher alkalinity and inhibited by silicate additives. The crystalline Al2O3 modifications show no significant attack by the electrolytes used. Transferring these observations to plasma electrolytic oxidation, they allow the conclusion that the electrochemically active zone in the pore ground of discharge channels interacts with the electrolytic and electrical process parameters throughout the entire PEO procedure. Influences of bath alkalinity and silicate content on layer growth rates are to be understood as impact on the passivation processes at the layer/substrate interface rather than chemical redissolution.