Preparation of Melamine-Formaldehyde Resin/Rice Husk Powder Coated Epoxy Resin Microcapsules and Effects of Different Microcapsule Contents on the Properties of Waterborne Coatings on Tilia europaea Surface
Source abstract
Abstract
With the development of economy and science and technology, people put forward higher standards for the performance of the surface coating of wood products, which requires us to carry out innovative research on the coating. In this work, a kind of microcapsule was prepared with melamine-formaldehyde resin/rice husk powder as wall material and epoxy resin as core material. The microcapsules were added to the waterborne acrylic resin coating according to the contents of 0%, 1.0%, 4.0%, 7.0%, 10.0%, 13.0%, 16.0% and 20.0% respectively, and were coated on the surface of the Tilia europaea boards in the form of topcoat. The effects of different contents of microcapsules on the optical properties, mechanical properties and aging resistance of the coating were explored, and the optimal content that can effectively improve the properties of the coating was analyzed. Test results indicated that when the microcapsule content is 7.0%, the comprehensive properties of the coating is optimal. At this time, the color difference of the coating is 6.96, the gloss at 60° is 13.4%, the hardness is 2H, the adhesion grade is 1, and the impact resistance is 12.0 kg·cm. After the aging test, the gloss loss rate decreases, the color difference is 5.69, and the gloss at 60° is 11.6%. The results of aging test show that the coating with epoxy microcapsules has a certain self-healing function. In this study, the microcapsules which can optimize the mechanical properties waterborne coating and prolong the service life of wood were prepared. This can meet the diverse needs of consumers, supply a theoretical reference for the preparation of functional microcapsules, and provide reference value for the functional research of the coating on wood furniture surface.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Lignin and Wood Chemistry · Wood Treatment and Properties · Dyeing and Modifying Textile Fibers
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Co-Innovation Center of Efficient Processing and Utilization of Forest Resources, Nanjing Forestry University, Nanjing 210037, China
College of Furnishings and Industrial Design, Nanjing Forestry University, Nanjing 210037, China
Funding
Postgraduate Research & Practice Innovation Program of Jiangsu Province · Natural Science Foundation of Jiangsu Province
References (45)
Show source-provided references
1. Kanbayashi, T., Ishikawa, A., Matsunaga, M., Kobayashi, M., and Kataoka, Y. (2019). Application of Confocal Raman Microscopy for the Analysis of the Distribution of Wood Preservative Coatings. Coatings, 9.10.3390/coatings9100621 ↗
2. A brief overview on the development of wood research10.1515/hf-2021-0155 ↗
3. Rowell, R., and Bongers, F. (2018). Role of Moisture in the Failure of Coatings on Wood. Coatings, 7.10.3390/coatings7120219 ↗
4. Effects of three kinds of fungi on color, chemical composition and route of infection of Picea sitchensis
5. Optimal design of a furniture frame by reducing the volume of wood10.12841/wood.1644-3985.275.12 ↗
6. Effect of Coating Thickness on Sound Absorption Property of Four Wood Species Commonly Used for Piano Soundboards10.22382/wfs-2020-004 ↗
7. Evaluation and Modeling of Processability of Laser Removal Technique for Bamboo Outer Layer10.1007/s11837-021-04755-2 ↗
8. Liu, Y., and Hu, J. (2021). Investigation of Polystyrene-Based Microspheres from Different Copolymers and Their Structural Color Coatings on Wood Surface. Coatings, 11.10.3390/coatings11010014 ↗
9. Surface retention of polyurethane and acrylic coatings on impregnated spruce wood (Picea abies Karst) and comparison with some wood preservatives10.46490/BF223 ↗
10. Hu, W., and Zhang, J. (2020). Bolt-Bearing Yield Strength of Three-Layered Cross-Laminated Timber Treated with Phenol Formaldehyde Resin. Forests, 11.10.3390/f11050551 ↗
11. Analyses on chemical composition of ancient wood structural component by using near infrared spectroscopy
12. Liu, Y., Hu, J., and Wu, Z. (2020). Fabrication of Coatings with Structural Color on a Wood Surface. Coatings, 10.10.3390/coatings10010032 ↗
13. The influence of mechanical, physical and chemical pre-treatment processes of wood surface on the relationships of wood with a waterborne opaque coating
14. Davis, K., Leavengood, S., and Morrell, J. (2021). Performance of Exterior Wood Coatings in Temperate Climates. Coatings, 11.10.3390/coatings11030325 ↗
15. Development and finishing technology of waterborne UV lacquer-coated wooden flooring10.15376/biores.16.1.1101-1114 ↗
16. Synthesis and properties of eco-friendly coatings using waterborne polyaspartic and blocked isocyanate10.1080/15421406.2019.1651061 ↗
17. Liu, Q., Gao, D., and Xu, W. (2021). Effect of Paint Process on the Performance of Modified Poplar Wood Antique. Coatings, 11.10.3390/coatings11101174 ↗
18. Liu, Q., Gao, D., and Xu, W. (2021). Influence of the Bottom Color Modification and Material Color Modification Process on the Performance of Modified Poplar. Coatings, 11.10.3390/coatings11060660 ↗
19. Construction of bionic structural color coating on wood surface based on polystyrene microspheres
20. Wu, Y., Sun, Y., Yang, F., Zhang, H., and Wang, Y. (2019). The Implication of Benzene–Ethanol Extractive on Mechanical Properties of Waterborne Coating and Wood Cell Wall by Nanoindentation. Coatings, 9.10.3390/coatings9070449 ↗
21. Research on wettability of wood surface with waterborne-resin priming paint
22. Yan, X., Zhao, W., and Wang, L. (2022). Mechanism of Thermochromic and Self-Repairing of Waterborne Wood Coatings by Synergistic Action of Waterborne Acrylic Microcapsules and Fluorane Microcapsules. Polymers, 14.10.3390/polym14010056 ↗
23. Yan, X., Wang, L., and Qian, X. (2020). Effect of Microcapsules with Different Core–wall Ratios on Properties of Waterborne Primer Coating for European Linden. Coatings, 10.10.3390/coatings10090826 ↗
24. Yan, X., Zhao, W., and Qian, X. (2021). Effect of Water-Based Emulsion Core Microcapsules on Aging Resistance and Self-Repairing Properties of Water-Based Coatings on Linden. Appl. Sci., 11.10.3390/app11104662 ↗
25. The formation mechanism of “skin-tactile” coating and its application and trends in furniture
26. Potential use of microcapsules in manufacture of fibrous products: A review10.1002/app.47066 ↗
27. Production of briquettes as a tool to optimize the use of waste from rice cultivation and industrial processing10.1016/j.renene.2017.03.084 ↗
28. Modification of rice husk to improve the interface in isotactic polypropylene composites
29. Structure and properties of natural rubber filled with epoxidised natural rubber modified rice husk ash10.1179/1432891713Z.000000000225 ↗
30. Yan, X., Li, W., Han, Y., and Yin, T. (2022). Preparation of Melamine/Rice Husk Powder Coated Shellac Microcapsules and Effect of Different Rice Husk Powder Content in Wall Material on Properties of Wood Waterborne Primer. Polymers, 14.10.3390/polym14010072 ↗
31. The Effects of Adding Melamine at Different Resin Synthesis Points of Low Mole Ratio Urea-Melamine-Formaldehyde (UMF) Resins
32. Modification with Melamine Formaldehyde and Melamine-Urea Formaldehyde Resin to Improve the Physical and Mechanical Properties of Wood
33. Water resistance evaluation of a MFU resins with different molar ratio catalyzed with citric acid10.1016/j.ijadhadh.2021.103020 ↗
34. Synthesis of Phenolic Resin-Based Epoxy Resins Containing Acetal Linkages and Degradability of Their Cured Epoxy Resins10.1295/koron.2015-0063 ↗
35. Synthesis characterization and application of hexafunctional epoxy resin and comparison against commercial epoxy resin
36. Zhao, Y., Xu, R., Xiao, Y., Wang, H., Zhang, W., and Zhang, G. (2022). Mechanical Performances of Phenolic Modified Epoxy Resins at Room and High Temperatures. Coatings, 12.10.3390/coatings12050643 ↗
37. A study of the surface properties of a solid wood coating system with self-healing microcapsules
38. (1990). Methods for Measuring the Colour of Paint Films. Part III: Calculation of Colour Differences. (Standard No. GB/T 11186.3-1989).
39. (2013). Test of Surface Coatings of Furniture (Standard No. GB/T 4893.4-2013).10.1016/S1364-5439(13)70163-1 ↗
40. (1998). Paint and Varnishes-Determination of Film Hardness by Pencil Test (Standard No. GB/T 6739-2006).
41. (1998). Paint and Varnishes-Cross Cut Test for Films (Standard No. GB/T 9286-1998).
42. (1993). Determination of Impact Resistance of Film (Standard No. GB/T 1732-1993).
43. (2007). Determination of Resistance to Heat and Humidity of Paint Films (Standard No. GB/T 1740-2007).
44. Color Changes of Wood during Natural Aging and Heat Treatment10.2488/jwrs.62.266 ↗
45. Effects of aging on wood: A literature review10.1007/s00226-015-0766-0 ↗