Microstructure and Properties of Hydroxyapatite Coatings Made by Aerosol Cold Spraying–Sintering Technology

Hydroxyapatite is a widely used material used for the bioactivation of an implant’s surface. A promising hydroxyapatite coating approach is the kinetic deposition of powder particles. The possibility of solid-state deposition improvement through the merging of Aerosol Deposition and Low Pressure Cold Spraying techniques is a promising prospect for improving the deposition efficiency and the quality of coatings. The objective of the paper is to study the possibilities of hydroxyapatite coating structure modification through changes in the coating process and post-heat treatment. The novel Aerosol Cold Spraying system joining Low Pressure Cold Spraying and Aerosol Deposition was used for the deposition of coatings. The coating’s post-processing was conducted using two techniques: Spark Plasma Sintering and Pressureless Sintering. The coating’s structure was examined using scanning, transmission, and light microscopy, and X-ray diffraction. Substrate–coating bond strength was assessed using a tensile test. Homogenous buildup using Aerosol Cold Spraying of hydroxyapatite was achieved. Various pores and microcracks were visible in the sprayed coatings. The deposition process and the thermal post-processing did not lead to significant degradation of the hydroxyapatite phase. As a result of the Spark Plasma Sintering and Pressureless Sintering at 800 °C, an increase in tensile adhesion bond strength and crystal size was obtained.