Low-Cost Deposition of Antibacterial Ion-Substituted Hydroxyapatite Coatings onto 316L Stainless Steel for Biomedical and Dental Applications

Substitutions of ions into an apatitic lattice may result in antibacterial properties. In this study, magnesium (Mg)-, zinc (Zn)-, and silicon (Si)-substituted hydroxyapatite (HA) were synthesized using a microwave irradiation technique. Polyvinyl alcohol (PVA) was added during the synthesis of the substituted HA as a binding agent. The synthesized Mg-, Zn-, and Si-substituted HAs were then coated onto a 316L-grade stainless-steel substrate using low-cost electrophoretic deposition (EPD), thereby avoiding exposure to high temperatures. The deposited layer thickness was measured and the structural, phase and morphological analysis were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The bacterial adhesion of Staphylococcus aureus was characterized at 30 min, 2 h and 6 h. The results showed homogeneous, uniform thickness (50–70 µm) of the substrate. FTIR and XRD showed the characteristic spectral peaks of HA, where the presence of Mg, Zn and Si changed the spectral peak intensities. The Mg–HA coating showed the least bacterial adhesion at 30 min and 2 h. In contrast, the Si–HA coating showed the least adhesion at 6 h. EPD showed an effective way to get a uniform coating on bio-grade metal implants, where ionic-substituted HA appeared as alternative coating material compared to conventional HA and showed the least bacterial adhesion.