Effect of Coating Process on Performance of Reversible Thermochromic Waterborne Coatings for Chinese Fir
Source abstract
Abstract
The effect of the coating process on the properties of reversible thermochromic waterborne coating on the surface of Chinese fir was examined. The results demonstrated that the most critical process parameter affecting the color difference and gloss of the coating was the way of adding thermochromic ink. The coating process had little influence on the adhesion, impact resistance adding, liquid resistance, and original properties of the coating. There was no obvious gloss variation in the coating under different coating processes. For the (3+3) layered coatings, when the thermochromic ink was added to the topcoats, the discoloration performance was the most obvious and the comprehensive performance of coating was better. Meanwhile, the gloss was 55.6%, the adhesion grade was grade 0, the impact resistance was 5.0 kg·cm, the liquid resistance grade of the coating to sodium chloride, ethanol and detergent was grade 1, and the liquid resistance grade to red ink was grade 3. The discoloration performance of the coating was stable under the conditions of aging and time change. This study provides new insight into preparing thermochromic intelligent waterborne wood coatings with potential practical applications on Chinese fir wood surfaces, and also lays a foundation for its application in furniture engineering.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Polymer composites and self-healing
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Furnishings and Industrial Design, Nanjing Forestry University, Nanjing 210037, China
References (33)
Show source-provided references
1. Preparation and properties of multifunctional thermochromic energy-storage wood materials10.1007/s10853-015-9585-9 ↗
2. Thermochromic VO2-SiO2 nanocomposite smart window coatings with narrow phase transition hysteresis and transition gradient width10.1016/j.solmat.2019.109944 ↗
3. W-doped VO2/PVP coatings with enhanced thermochromic performance10.1016/j.solmat.2019.04.022 ↗
4. Dispersion of microcapsules for the improved thermochromic performance of smart coatings10.1039/C9RA04740A ↗
5. An edge-heating device for optical measurement of thermochromic glazing materials and recommended test procedure10.1520/JTE20120341 ↗
6. Simple and general platform for highly adjustable thermochromic fluorescent materials and multi-feasible applications10.1039/C9MH00253G ↗
7. Facile flexible reversible thermochromic membranes based on micro/nanoencapsulated phase change materials for wearable temperature sensor10.1016/j.apenergy.2019.04.077 ↗
8. 3,6-Disubtituted fluorans containing 4(3H)-quinazolinon-3-yl, diethyl amino groups and their application in reversible thermochromic materials10.1016/j.dyepig.2004.08.004 ↗
9. Composite phase change materials with good reversible thermochromic ability in delignified wood substrate for thermal energy storage10.1016/j.apenergy.2017.12.006 ↗
10. Solvent-free microwave-assisted synthesis and characterization of polybenzoxazine as a thermochromic material for smart coatings10.1007/s00396-019-04491-9 ↗
11. An exploration of the combined effects of NIR and VIS spectrally selective thermochromic materials on building performance10.1016/j.enbuild.2019.05.061 ↗
12. Novel stretchable thermochromic transparent heaters designed for smart window defroster applications by spray coating silver nanowire10.1039/C9RA06508C ↗
13. Preparation and testing of thermochromic coatings for buildings10.1016/j.solener.2019.09.042 ↗
14. Imitation-mussel-based high-performance conductive coating on hydrophobic fabric for thermochromic application10.1002/app.47751 ↗
15. The durability study of thermochromic vanadium dioxide films with the addition of barrier coatings10.1016/j.vacuum.2017.08.028 ↗
16. Reversibly thermochromic bismuth-organic materials with tunable optical gaps10.1039/C7TC03277C ↗
17. safety evaluation of deinked pulp containing offset thermochromic inks
18. Effect of coating thickness on sound absorption property of four wood species commonly used for piano soundboards10.22382/wfs-2020-004 ↗
19. Moisture-dependent orthotropic viscoelastic properties of Chinese fir wood during quenching in the temperature range of 20 to −120 °C10.1515/hf-2018-0281 ↗
20. Effects of the manufacturing conditions on the VOCs emissions of particleboard10.15376/biores.15.1.1074-1084 ↗
21. Special coating technology and film performance of rice straw particleboard
22. Liu, Y., Hu, J., and Wu, Z.H. (2020). Fabrication of coatings with structural color on a wood surface. Coatings, 10.10.3390/coatings10010032 ↗
23. Sun, S.J., Zhang, M., Umemura, K., and Zhao, Z.Y. (2019). Investigation and characterization of synthesis conditions on sucrose-ammonium dihydrogen phosphate (SADP) adhesive: Bond performance and chemical transformation. Materials, 12.10.3390/ma12244078 ↗
24. Preparation and application of high performance corn starch glue in straw decorative panel10.22382/wfs-2018-009 ↗
25. Thermochromic perovskite inks for reversible smart window applications10.1021/acs.chemmater.6b05112 ↗
26. Colorimetric properties of reversible thermochromic printing inks10.1016/j.dyepig.2010.01.014 ↗
27. Yan, X.X., Chang, Y.J., and Qian, X.Y. (2019). Effect of the concentration of pigment slurry on the film performances of waterborne wood coatings. Coatings, 9.10.3390/coatings9100635 ↗
28. (1995). GB/T 3181-1995 Colour Standard for Paint Film, Standardization Administration of the People’s Republic of China. (In Chinese).
29. (2007). GB/T 9754-2007 Paints and Varnishes—Determination of Specular Gloss of Non-Metallic Paint Films at 20°, 60° and 85°, Standardization Administration of the People’s Republic of China. (In Chinese).
30. (1993). GB/T 1732-93 Determination of Impact Resistance of Film, Standardization Administration of the People’s Republic of China. (In Chinese).
31. (1979). GB/T 1720-89 Determination of Adhesion of Film, Standardization Administration of the People’s Republic of China. (In Chinese).
32. (1993). GB/T 1733-93 Determination of Resistance to Water of Films, Standardization Administration of the People’s Republic of China. (In Chinese).
33. Investigation of waterborne thermochromic topcoat film with colorchanging microcapsules on Chinese fir surface10.1016/j.porgcoat.2019.105262 ↗